Considering the rising demand for rare earth elements (REEs), researchers are looking for new sources for their extraction, thereby fostering economic and environmentally justified processing solutions. Among potential industrial sources, coal fly ash emerges as one of the most promising. The recovery of REEs from coal fly and bottom ashes derived from different thermal power plants was the main focus of this study. A dual-step methodology was conducted on ash samples, which involved an ultrasonic roasting process to disintegrate the silica matrix, followed by a microwave-assisted acid leaching step to extract REEs. The roasting procedure was studied using the Plackett–Burman design, and the Box–Behnken design was subsequently implemented to optimize the leaching procedure. The optimized ultrasonic roasting procedure was set up at 95 °C for 10 min with an ash-to-roasting agent (3M NaOH) ratio of 0.5:1 (m/V). For acid leaching, the optimal conditions were obtained at 174 °C for 30 min with an HCl ÷ HNO₃ mixture (1:1 V/V). The standard reference material (NIST 1633c) was used in the conclusive experiments to estimate the average recovery (80%) of REEs. The green aspects of this methodology were evaluated using several metrics (atom economy, E-factor, and energy consumption). The proposed process outperforms high-temperature roasting procedures in terms of greenness; however, the REE recovery rate is lower.

This study investigated the occurrence and distribution of rare earth elements (REEs), including 14 lanthanoids, scandium (Sc), and yttrium (Y), in groundwater around a large coal-fired thermal power plant (TPP). The ICP-MS technique was used to analyze 16 REEs in groundwater samples collected from monitoring wells. REE concentrations ranged from 59.9 to 758 ng/L, with an average of 290 ng/L. The most abundant was Sc, followed by La, accounting for 54.2% and 21.4% of the total REE concentration, respectively. Geospatial analysis revealed the REE enrichment at several hotspots near the TPP. The highest REE concentrations were observed near the TPP and ash landfill, decreasing with the distance from the plant and the landfill. REE fractionation ratios and anomalies suggested the Light REE dominance, comprising over 78% of the total REEs. Correlation and principal component analyses indicated similar behavior and sources for most REEs. Health risk assessment found hazard indices (HI) of 1.36 × 10⁻³ and 1.98 × 10⁻³ for adults and children, respectively, which are far below the permissible limit (HI = 1). Likewise, incremental lifetime cancer risks (ILCR) were all below 1 × 10⁻⁶. Nevertheless, ongoing ash disposal and potential accumulation in the environment could elevate the REE exposure over time.

The occurrence and distribution of yttrium and rare earth elements (REYs), along with major elements and heavy metal(loid)s (HMs) in coal fly ash (CFA) from five coal-fired power plants (CFPPs), were analyzed, and the REY-associated ecological and health risks were assessed. The individual REYs in CFA were abundant in the following order: Ce > La > Nd > Y > Pr > Gd > Sm > Dy > Er > Yb > Eu > Ho > Tb > Tm > Lu. The total REY content ranged from 135 to 362 mg/kg, averaging 302 mg/kg. The mean light-to-heavy REY ratio was 4.1, indicating prevalent light REY enrichment in CFA. Significantly positive correlations between the REYs suggested that they coexist and share similar origins in CFA. REYs were estimated to pose low to moderate ecological risks, with risk index (RI) values ranging from 66 to 245. The hazard index (HI) and target cancer risk (TCR) of REYs from CFA, estimated to be higher for children (HIc = 0.15, TCRc = 8.4 × 10⁻¹⁶) than for adults (HIa = 0.017, TCRa = 3.6 × 10⁻¹⁶), were well below the safety limits (HI = 1, TCR = 1.0 × 10⁻⁶). However, the danger to human health posed by HMs in the same CFA samples (HIc = 5.74, TCRc = 2.6 × 10⁻⁴, TCRa = 1.1 × 10⁻⁴) exceeded the safe thresholds (excl. HIa = 0.63). The mean RI and HI attributed to REYs in CFA were 14% and 2.6%, respectively, of the total risks that include HMs.

In this work, different methods for fly ash modification were applied to obtain an adsorbent for the efficient removal of selected pharmaceuticals from a multiclass aqueous solution. Morphological and surface properties of the modified fly ash samples were analyzed by scanning electron microscopy, X-ray fluorescence, X-ray diffraction, Fourier transform infrared spectroscopy, and point of zero charge, and the influence of the applied modifications was determined by comparison with the results obtained for unmodified fly ash. Experimental parameters of the adsorption of the pharmaceutical onto the modified fly ash were optimized, and special attention was paid to the influence of different parameters on the adsorption capacities. Multivariate methods of analysis, such as artificial neural networks, applied to the obtained results showed that the contact time, the initial concentration of the pharmaceutical solution, and the pH value had the strongest influence on the adsorption process. Fly ash modified with chitosan and magnetic iron oxide showed the best adsorption properties (removal efficiency above 80% for the majority of the selected pharmaceuticals), and artificial neural networks confirmed its susceptibility to the modeling process.

Due to industrial growth and its impact on the environment, the increasing amount of industrial waste requires a comprehensive approach aligned with the principles of sustainable development. The main goals are not only to preserve natural resources but also to encourage innovation in the reuse of waste materials. In an attempt to reduce the problems regarding waste disposal and wastewater treatment in the textile industry, fibrous textile waste was used as a starting material to obtain carbon adsorbents for the removal of pollutants from wastewater. Waste cotton and mixed yarns, mainly consisting of polysaccharide cellulose, were hydrothermally carbonized and activated with KOH to convert them into efficient carbon adsorbents for heavy metal removal from water. Characterization of carbonized material showed that after activation, an increase in specific surface area (up to 872 m²/g) and content of surface oxygen groups (6.04 mmol/g) leads to a higher affinity towards heavy metal ions, especially lead ions, and high adsorption capacity of 19.98 mg/g obtained for activated cotton yarns. The results of this research represent a contribution to the reduction of waste materials by modifying them into adsorbents, while the regeneration of adsorbents is an example of the practical application of polysaccharide-based materials in the purification of wastewater containing various heavy metal ions.

Hybrid adsorbent, based on the cross-linked copolymer impregnated with hydrous iron oxide, was applied for the first time for Se(VI) adsorption from water. The influence of the initial solution pH, selenate concentration and contact time to adsorption capacity was investigated. Adsorbent regeneration was explored using a full factorial experimental design in order to optimize the volume, initial pH value and concentration of the applied NaCl solution as a reagent. Equilibrium state was described using the Langmuir model, while kinetics fitted the pseudo-first order. The maximum adsorption capacity was found to be 28.8 mg/g. Desorption efficiency increased up to 70%, and became statistically significant with the reagent concentration and pH increase, while the applied solution volume was found to be insignificant in the investigated range. Based on the results obtained, pH influence to the adsorption capacity, desorption efficiency, Fourier transform infrared (FTIR) and X-ray diffraction (XRD) analysis of loaded adsorbent, it was concluded that the outer- and inner-sphere complexation are mechanisms responsible for Se(VI) separation from water. In addition to the experiments with synthetic solutions, the adsorbent performances in drinking water samples were explored, showing the purification efficiency up to 25%, depending on the initial Se(VI) concentration and water pH. Determined sorption capacity of the cross-linked copolymer impregnated with hydrous iron oxide and its ability for regeneration, candidate this material for further research, as a promising anionic species sorbent.