The properties of a polymer synthesized by the Gluconacetobacter hansenii strain GH-1/2008 were investigated. The studied bacterial cellulose polymer films are characterized by a mesh nanostructure composed of micro- and macrofibrils, a high water absorption capacity 556 ± 16.8%, and high strength and elasticity. Analysis of the spectrum recorded by ¹³С CP/MAS NMR spectroscopy showed that the bacterial cellulose synthesized by G. hansenii GH-1/2008 is a pure compound composed of Iα (65–70%) and Iβ (30–35%) allomorphs without any other impurities. It was found that the bacterial cellulose films with adsorbed antibiotics such as amoxiclav and fluconazole can be used as antibacterial and antifungal wound healing materials.

New functional medical materials with antibacterial activity based on biocompatible bacterial cellulose (BC) and Ag nanoparticles (Ag NPs) were obtained. Bacterial cellulose films were prepared by stationary liquid-phase cultivation of the Gluconacetobacter hansenii strain GH-1/2008 in Hestrin–Schramm medium with glucose as a carbon source. To functionalize the surface and immobilize Ag NPs deposited by magnetron sputtering, BC films were treated with low-pressure oxygen–nitrogen plasma. The composition and structure of the nanomaterials were studied using transmission (TEM) and scanning (SEM) electron microscopy and X-ray photoelectron spectroscopy (XPS). Using electron microscopy, it was shown that on the surface of the fibrils that make up the network of bacterial cellulose, Ag particles are stabilized in the form of aggregates 5–35 nm in size. The XPS C 1s spectra show that after the deposition of Ag NPs, the relative intensities of the C-OH and O-C-O bonds are significantly reduced. This may indicate the destruction of BC oxypyran rings and the oxidation of alcohol groups. In the Ag 3d_5/2 spectrum, two states at 368.4 and 369.7 eV with relative intensities of 0.86 and 0.14 are distinguished, which are assigned to Ag⁰ state and Ag acetate, respectively. Nanocomposites based on plasma-treated BC and Ag nanoparticles deposited by magnetron sputtering (BCP-Ag) exhibited antimicrobial activity against Aspergillus niger, S. aureus and Bacillus subtilis.

Composite fibers and films based on cellulose and betulin were spun for the first time from solutions in N-methylmorpholine-N-oxide using the dry–wet jet method. The rheological properties of the composite solutions did not reveal any fundamental difference from those of the cellulose solutions. Introduction of betulin into the cellulose matrix (up to 10%) led to a decrease in the mechanical properties of the obtained fibers. The structure of the composite fibers was analyzed using SEM and X-ray diffraction methods. It was shown that the introduction of an additive into the cellulose matrix led to a decrease in the structural ordering of the cellulose. Comparative studies of the antibacterial activity of the composite films on Escherichia coli (E. coli) were carried out. The antifungal activity of the composite films was estimated using the strain of the O-97 Trichoderma viride Pers ex Fr (Gause Institute of New Antibiotics, Moscow, Russia).

In the present study, one of the possible methods of the bacterial cellulose processing is proposed via its dissolution in N-methylmorpholine-N-oxide using the stage of mechano-chemical activation of the solid polymer–solvent system. Preliminary solid-phase activation is apparently a decisive factor affecting the dissolution rate of bacterial cellulose in N-methylmorpholine-N-oxide. The effects of bacterial cellulose concentration, solvent nature, degree of polymerization and temperature on dissolution time were studied. The rheological behavior of the solutions does not change at 120 °C for at least half an hour that allowed us to process such solutions for films preparation. The films from these solutions by means of dry-wet jet spinning in aqueous coagulant were formed. The structure of the nascent cellulose and formed films was tested by the X-ray diffraction method and SEM. The thermal behavior of the films revealed an increase in the carbon yield for the formed films compared to the nascent bacterial cellulose. The process of film pyrolysis is accompanied by exothermic effects, which are not typical for wood cellulose. Some reasons of such thermal behavior are considered.

Bacterial cellulose (BC) is a natural polymer that has a number of unique properties that determine the need to synthesize large amounts of it and to search the ways to increase the productivity of strains and to optimize the nutritive media. It is known that the choice of the producer for BC synthesis has an impact on its final properties and on the productivity of this polymer production. Under static liquid phase cultivation conditions, all cellulose-producing bacteria form a uniform film on the medium surface that serves as a scaffold for cells immobilization, thus providing them with the access to the air/liquid interface, where the access to oxygen is not limited. Meanwhile, when cultivation goes under agitating conditions, most of Gluconacetobacter xylinus strains produce less cellulose in form of globules of various sizes, despite the better oxygen access. Several authors explain the lower cellulose outcome when cultivated under agitated conditions by the appearance of spontaneous mutants that do not produce cellulose in the population. It was revealed that when grown on agarized media, cellulosenon- producing mutants form colonies of a specific mucoid type, while non-mucoid phenotype cells form smooth colonies of non-mucoid type. To our knowledge, there is no published research on the impact of cultivation conditions and nutritive medium composition on the appearance of spontaneous phenotype mutations in the population of Gluconacetobacter hansenii representatives. The aim of the present research is to elucidate the impact of the carbon source on the productivity of G. hansenii strain and the appearance of cellulose-negative mutants under static cultivation conditions. We studied the strain G. hansenii GH 1/2008 (VKPM В-10547) as a BC source. Liquid phase static cultivation of G. hansenii GH 1/2008 was carried out using the modified Hestrin-Schramm (HS) medium, containing 4% of monosaccharides (glucose, fructose and galactose) or disaccharides (sucrose, maltose, lactose) as carbon sources. The occurrence of mutants was calculated considering phenotypes of colonies obtained by seeding the samples of cultural liquid and wash-offs of cells from films produced by the cultivation of the producer on modified agarized HS media. The polymer outcome was expressed as the film absolute dry weight (a.d.w.) per cultivation medium volume unit. We studied the morphology of the producer’s wild type and mutant cells by means of atomic force microscopy (AFM) (See Fig. 8). The structural organization of the produced films and gel was revealed by means of scanning electron microscopy (SEM) performed after freeze-drying. The composition of the fibers was checked acquiring FTIR Spectroscopy. We established that G. hansenii GH 1/2008 produces a dense film on media containing fructose, glucose and sucrose, while the polymer has gel consistence when grown on maltose, galactose and lactose (See Fig. 1). The maximal quantity (a.d.w.) of polymer was produced on fructose- and sucrose-containing media. The overall number of immobilized producer cells was considerably higher when grown on media with glucose, fructose and sucrose than on gels grown on those containing maltose, galactose and lactose (See Table 1). SEM imaging revealed considerable difference in the microscale organization of films and gels produced by G. hansenii GH 1/2008 on various carbon sources (See Fig. 2). Fructose-containing medium yields the densest structure with dense layers separated by 2μm thick areas filled with non-ordered BC fibrils. The microscale organization of sucrose- and glucose-based films were very similar and had a cell-like structure. In cases where the synthesized polymer had squeezable gel consistence, its microstructure was not layered but close to isotropic. The studies of gels by means of FTIR spectroscopy showed that the gels are also formed of BC molecules; the spectra were almost identical (See Fig. 4). The only difference, i.e. the intensity of the 1638 см-1 peak, can be explained by the presence of a higher amount of bound water in the latter. It is known that some strains of this species may produce glucuronic acid oligomers under unfavorable conditions, but peaks corresponding to carboxyl or carbonyl groups were not revealed in the spectra. This is the evidence that no detectable amounts of glucuronic acid were produced under conditions studied. The analysis of colonies of G. hansenii GH 1/2008 cultivated under static conditions on media containing various carbon sources revealed colonies with two dominating phenotypes: non-mucoid smooth convex colonies and mucoid flat ones (See Fig. 5). The number of cells forming smooth non-mucoid colonies on agarized media was maximal in the inoculations of cultural liquids after the cultivation on media containing fructose and sucrose, i.e. those carbon sources that demonstrated high productivity per 1L of cultural liquid (See Fig. 6). In the inoculations of the cultural liquid and wash-offs of cells immobilized on gels obtained by the cultivation on media containing galactose and lactose, the number of mucoid colonies was considerably higher (See Table 2). The clones forming mucoid type colonies did not produce BC films when reinoculated in liquid media, while those forming colonies of mucoid (smooth) type produce films on the 3rd day of cultivation (See Fig. 7). The analysis of cells shape and sizes by means of AFM did not reveal any statistically valid difference between the mutants and the wild type. The present research shows that the source of carbon is a selective factor in the formation of the inner composition of the population of clones of the bacterial cellulose producer Gluconacetobacter hansenii GH 1/2008. The proliferation of cellulosenegative cells arouses competition for the substrate with cellulose-positive cells of G. hansenii GH 1/2008 that reduces the number of the latter and the production of the exopolymer.