The main research objective of this study was to investigate the effect of the impregnation of Twaron® fabric with various shear thickening fluids (STFs) on the stab resistance at quasi-static conditions—being the main parameter characterizing the future application of the impregnated textiles in the scope of the new functionality of the elaborated protection of the multi-layer system. It was found that the STF/Twaron® fabric composites required significantly higher loading than the untreated fabric to achieve spike penetration. In the composite fabric tests, the spike did not fully puncture the material.

In response to the demand for new implant materials characterized by high biocompatibility and bioresorption, two prototypes of fibrous nanocomposite implants for osseous tissue regeneration made of a newly developed blend of poly(l-lactide-co-glycolide) (PLGA) and syntheticpoly([R,S]-3-hydroxybutyrate), PLGA/PHB, have been developed and fabricated. Afibre-forming copolymer of glycolide and l-lactide (PLGA) was obtained by a unique method of synthesis carried out in blocksusing Zr(AcAc)₄ as an initiator. The prototypes of the implants are composed of three layers of PLGA or PLGA/PHB, nonwoven fabrics with a pore structure designed to provide the best conditions for the cell proliferation. The bioactivity of the proposed implants has been imparted by introducing a hydroxyapatite material and IGF1, a growth factor. The developed prototypes of implants have been subjected to a set of in vitro and in vivobiocompatibility tests: in vitro cytotoxic effect, in vitro genotoxicity and systemic toxicity. Rabbitsshowed no signs of negative reactionafter implantation of the experimental implant prototypes.