3D printing, also known as additive manufacturing, is becoming increasingly popular for prototype processing in industrial practice. Laser sintering, which is a laser powder bed fusion technique, is a versatile and common 3D printing technology, which enables compact and high-quality products. Polyamide 12, a popular 3D printing material, provides reliable mechanical and thermal properties. Weaknesses in applying this technology for polyamide 12 include incomplete information regarding the application of various types of additives and different printing orientations with respect to the properties. This study aimed to investigate the influence of various additives (including carbon fiber, glass fiber, flame retardant, and aluminum powder) combined with polyamide 12, using processing of predefined powder refreshing mixture on the properties of a finished product. The thermal, surface, and mechanical properties of samples printed with five different polyamides 12-based powders at three different print orientations were investigated. It was found that the inclusion of additives decreases the tensile strength and increases the surface roughness of printed components—however, the toughness increases. The results can assist designers in selecting an appropriate material that will produce a finished part with the required properties for a given application.

The aim of this paper was to analyze selected properties of beech wood (Fagus sylvatica L.) treated by one-sided surface charring. Specimens were one-side charred with a hot plate using several time-temperature combinations (from 200 to 400 °C). Characteristics such as colour, discoloration, surface roughness, fire resistance, total carbohydrate content at several wood layers and decay resistance were evaluated. Surface charring was applied to the radial and tangential surfaces. Colour measurements showed that the surface of the wood turned grey due to charring. In addition to colour measurements, other experiments showed significant differences between radial and tangential specimens due to their different structures. The higher the temperature used in treating them, the lower the roughness values for radial specimens, while the trend for tangential specimens was the opposite. A smoother surface is more fire resistant, so radial specimens are generally better in this regard. Tangential specimens are more susceptible during preparation to forming cracks that impair flame resistance because a continuous protective densified layer is not formed. The determination of total carbohydrates revealed significant changes at various wood depths after surface charring. These changes were more predictable in radial specimens due to the annual ring orientation, because each layer consisted of a similar earlywood/latewood ratio. Finally, when decay resistance was assessed, weight loss was found to be lower in all specimens than in the references. The results suggest that charring at a particular combination of temperature and time improved the investigated properties of the surface-modified beech.