European beech wood has low natural resistance to microbial attacks especially when it is exposed outdoors. We looked at ways of improving this by applying three hydrophilic extracts from other species known for their ability to inhibit fungal growth. We prepared oak heartwood and black locust bark extracts by accelerated-solvent extraction with aqueous methanol and freeze-drying, and obtained black wattle bark hot-water extract commercially. The molecular size of the phenolic components and associated saccharides in the extracts were determined by size-exclusion chromatography (SEC). We found that two extracts improved beech wood durability even at low concentrations (5 wt.% solution); the most effective extract was black wattle extract. The worst performance, by black locust bark extract, was attributed to the presence of small-molecule phenolics. The total phenolic content was up to 9× lower than that reported for fresh extracts. Even though the extracts were not stored specifically to preserve the original phenolic content, we found that two were still effective as fungal inhibitors.

Wood modification (by thermal or chemical treatment) helps to improve the dimensional stability of wood and enhance its resistance to biological agents. Beech wood is non-durable and exposure in exterior settings dramatically shortens its service life. To determine the full potential of beech wood for advanced applications, a better understanding of the chemical changes induced by modification is needed. Two chemical treatments (acetylation and melamine formaldehyde resin impregnation) and three thermal treatments (heating to 180, 200 and 220 °C) were performed on beech wood. The modification effect was examined based on (i) molecular changes in functional groups by Fourier-transform infrared spectroscopy (ATR-FTIR); (ii) extractive content; and (iii) pH changes. Moreover, the explanation of these changes was supported by the FTIR-analysis of isolated main wood components (cellulose, holocellulose and lignin) from the modified wood. The high temperatures applied to samples during thermal modification promoted the deacetylation and degradation of hemicelluloses. Hemicelluloses were targeted also by acetic anhydride and melamine resin, the bonding of which was confirmed by FTIR analysis. The formation of fewer methylene bridges affected the properties of the melamine network. This observation suggests the need to determine optimal curing conditions in future research, to reduce melamine-wood hydrophilicity.

The wood-water interactions of modified beech wood (Fagus sylvatica L.) were studied. Specimens were thermally modified at 180 (TM₁), 200 (TM₂) and 220 °C (TM₃), acetylated (Acet), and melamine formaldehyde (MF) resin (Mel) modified. Afterwards, the water vapour characteristics, i.e. water vapour sorption isotherms, equilibrium moisture content (EMC), dimensional stability of specimens conditioned at 30, 65 and 90% RH and liquid water characteristics, i.e. water absorption, maximum moisture content (MC), leachability and swelling kinetics, were determined and the results compared with reference (Ref) specimens. From the results, it is evident that the scale of wood-water interactions was highly dependent on the thermal modification temperature and type of chemical modification. The water vapour isotherms of thermally modified wood decreased, whereas more severe treatment exhibited more distinct reduction. The EMC values of the Mel and TM₁ specimens decreased only at high RH, whereas the most significant decrease, within the whole range of observation, was found in the Acet group. The maximum MC reduction was achieved by acetylation. As a consequence of swelling reduction, dimensional stability expressed as anti-swelling efficiency (ASE) was considerably improved. A relatively high initial linear-phase swelling rate was found for the Ref specimens, whereas modified wood exhibited comparatively slow and gradual swelling.

The aim of this paper was to analyze selected properties of beech wood (Fagus sylvatica L.) treated by one-sided surface charring. Specimens were one-side charred with a hot plate using several time-temperature combinations (from 200 to 400 °C). Characteristics such as colour, discoloration, surface roughness, fire resistance, total carbohydrate content at several wood layers and decay resistance were evaluated. Surface charring was applied to the radial and tangential surfaces. Colour measurements showed that the surface of the wood turned grey due to charring. In addition to colour measurements, other experiments showed significant differences between radial and tangential specimens due to their different structures. The higher the temperature used in treating them, the lower the roughness values for radial specimens, while the trend for tangential specimens was the opposite. A smoother surface is more fire resistant, so radial specimens are generally better in this regard. Tangential specimens are more susceptible during preparation to forming cracks that impair flame resistance because a continuous protective densified layer is not formed. The determination of total carbohydrates revealed significant changes at various wood depths after surface charring. These changes were more predictable in radial specimens due to the annual ring orientation, because each layer consisted of a similar earlywood/latewood ratio. Finally, when decay resistance was assessed, weight loss was found to be lower in all specimens than in the references. The results suggest that charring at a particular combination of temperature and time improved the investigated properties of the surface-modified beech.

Tannins and their toxic effects against various decay organisms have been interrelated for centuries. As natural products have gained more interest, waste from several production fields abundant in tannins has yielded promising components for wood preservation. In this work, the main approach was to split condensed tannins into smaller fractions by chemical hydrolysis and evaluate their suitability for beech wood impregnation. Commercial extract from black wattle was treated with mineral acid of low concentration. The volatile hydrochloric acid was completely removed after reaction by evaporation in the course of freeze-drying. The modified extract was then applied as aqueous solution into beech wood. The water resistance of the modified beech wood was not increased significantly, and scanning electron microscopy (SEM) showed no evidence of tannin successful bonding within wood cells. Nevertheless, after strong leaching cycles, part of the extract accumulated in fibers. Moreover, lyophilization was found to be a suitable technique to eliminate volatile acids from temperature-sensitive extracts, such as tannins. These findings could help in the development of water-borne tannin formulations for wood protection, while using phlobaphene formation as a potential natural pathway of tannin autocondensation.