In recent years, the exploitation of natural resources and industrial development have led to the production of harmful pollutants. Much of these contaminants end up in water resources, reducing the availability of drinking water. Therefore, it is necessary to find remedies to this situation. Solutions could be the adsorption or the degradation through photocatalysis of these compounds. A good candidate for this task is titanium dioxide (TiO₂), due to its non-toxicity, stability and low cost. In this work, we propose a novel synthesis of TiO₂ nanoparticles (NPs), with high adsorption capacity, produced at low temperature in alkaline environment. Adsorption tests were conducted using methylene blue and diclofenac as model pollutants. Moreover, the obtained NPs have been characterized through Raman spectroscopy, Scanning and Transmission electron microscopies and with thermogravimetric analysis. The results showed a porous structure with a high surface area, able to efficiently adsorb large amounts of dye from the aqueous solution. These properties make the obtained TiO₂ powders suitable for applications devoted to the adsorption and recovery of harmful compounds. Graphic

Nanodiamond (ND) layers on silicon substrate are deposited by the pulsed spray technique starting from nanoparticles of about 250 nm dispersed in 1,2-dichloroethane solvent. The aim of this letter is to investigate the quantum efficiency (QE) of photocathodes based on ND particles in the vacuum ultraviolet spectral range. Various ND layers are examined employing as-received and hydrogenated nanoparticles. As expected, the hydrogen plasma treatment improves strongly the photoemission of the layer giving a QE of 22% at 146 nm. Indeed, this efficiency value is achieved only if the particles are treated in H2 microwave plasma before the growth of the sprayed layer rather than to hydrogenate the already formed one. These QE values are higher than those of photocathodes based on plasma chemical vapor deposition diamond films, but with the advantage of being much stable, too. The highest QE values are explained to be due to the intrinsic chemical and structural features of utilized ND particles.

Development and characterization of TGF-β1 MIP electrochemical sensor as a tool for POC diagnostics.