High-density polyethylene polymer (HDPE) and carbon black (CB) were utilized to create HDPE/CB composites with different filler concentrations (0.0, 2.0, 4.0, 6.0, 8.0, 10.0, 16.0, 20.0, and 24.0 wt.%). The composites were extruded into filaments, which were then utilized to fabricate 3D-printed specimens with the material extrusion (MEX) method, suitable for a variety of standard mechanical tests. The electrical conductivity was investigated. Furthermore, thermogravimetric analysis and differential scanning calorimetry were carried out for all the HDPE/CB composites and pure HDPE. Scanning electron microscopy in different magnifications was performed on the specimens’ fracture and side surfaces to investigate the morphological characteristics. Rheological tests and Raman spectroscopy were also performed. Eleven different tests in total were performed to fully characterize the composites and reveal connections between their various properties. HDPE/CB 20.0 wt.% showed the greatest reinforcement results in relation to pure HDPE. Such composites are novel in the MEX 3D printing method. The addition of the CB filler greatly enhanced the performance of the popular HDPE polymer, expanding its applications.

In this study, poly (ethylene terephthalate) (PETG) was combined with Antimony-doped Tin Oxide (ATO) to create five different composites (2.0–10.0 wt.% ATO). The PETG/ATO filaments were extruded and supplied to a material extrusion (MEX) 3D printer to fabricate the specimens following international standards. Various tests were conducted on thermal, rheological, mechanical, and morphological properties. The mechanical performance of the prepared nanocomposites was evaluated using flexural, tensile, microhardness, and Charpy impact tests. The dielectric and electrical properties of the prepared composites were evaluated over a broad frequency range. The dimensional accuracy and porosity of the 3D printed structure were assessed using micro-computed tomography. Other investigations include scanning electron microscopy and energy-dispersive X-ray spectroscopy, which were performed to investigate the structures and morphologies of the samples. The PETG/6.0 wt.% ATO composite presented the highest mechanical performance (21% increase over the pure polymer in tensile strength). The results show the potential of such nanocomposites when enhanced mechanical performance is required in MEX 3D printing applications, in which PETG is the most commonly used polymer.