Waste tire rubber powder-modified asphalt (RMA) has been widely used in road construction, which was traditionally limited by the poor compatibility of RMA, affecting pavement performance. By synthesizing epoxy soybean oil with amide groups (ESO/TETA) and grafting it onto desulfurized rubber powder (DCR) through microwave irradiation, a surface-functionalized rubber powder (MDCR) was produced successfully. The effects of the physical properties, storage stability, thermal stability, and rheological behavior of the modified asphalt were studied. The results show that the MDCR with a polar surface improved the compatibility and adhesive interactions between the modified crumb rubber and the asphalt. The MDCR content could reach 50%, and the phase separation could meet the requirements of 2.2 °C, which has application conditions in engineering for stable storage. Additionally, the inclusion of MDCR in the asphalt formulations significantly mitigated the temperature sensitivity of the modified asphalt. Importantly, when the MDCR constituted from 20% to 50% of the asphalt, there was a noted reduction in the phase angle at temperatures above 70 °C, indicating a significant improvement in the elastic efficiency. The MDCR also led to substantial enhancements in the resistance of the asphalt to high-temperature and high-stress rutting, addressing the crucial limitations in the consumption ability of waste tire rubber powder and improving the overall performance of RMA in pavement applications.

To improve heat dissipation capability and enhance mechanical properties, a series of silica aerogel (SA) and modified glass fiber (GF)-filled SBR composites were prepared. It was found that the addition of SA successfully reduced the thermal conductivity of SBR by 35%, owing to the heat shield of the nanoscale porous structure of SA. Moreover, the addition of modified glass fiber (MGF) yielded a significant increase in the tensile and tear strength of SBR/SA composite rubber of 37% and 15%, respectively. This enhancement was more pronounced than the improvement observed with unmodified GF, and was attributed to the improved dispersion of fillers and crosslinking density of the SBR matrix. Rheological analysis revealed that the addition of SA and MGF weakened the ω dependence. This was due to the partial relaxation of immobilized rubber chains and limited relaxation of rubber chains adsorbed on the MGF. Furthermore, the strain amplification effect of MGF was stronger than that of GF, leading to a more pronounced reinforcing effect.