This research evaluates four sustainable cementitious composites with sustainable plant fibers and bio-aggregates: (1) cementitious matrix composite with lechuguilla fibers (LFC) and (2) with flax fibers (FFC); and (3) cementitious matrix composite with wood shavings (WSC) and (4) with hemp shavings (HSC). The fibers are for reinforcement and the shavings act as bio-aggregates as a total replacement for limestone aggregates. The lechuguilla (LF) and flax (FF) fibers were treated; wood (WS) and hemp (HS) bio-aggregates were also processed. Nineteen mixtures were manufactured, and five were used as controls, and the hygrothermal, mechanical, and durability properties were evaluated. The results for LFC and FFC showed that fiber treatment negatively affected flexural–compressive strength; untreated LFC with accelerated deterioration had better mechanical behavior, higher density, and lower porosity than FFC. Strength and density decreased, but porosity increased with increasing fiber volume (Vf). Regarding WSC and HSC, the microstructure of WS and HS had a significant effect on the physical and mechanical properties. The high porosity influenced the results obtained, since it decreased compressive strength and bulk density; however, thermal conductivity, hygroscopicity, and vapor resistance showed better behavior in most cases than the control specimens, i.e., without bio-aggregates.

Depending on the morphology of the natural fibers, they can be used as reinforcement to improve flexural strength in cement-based composites or as aggregates to improve thermal conductivity properties. In this last aspect, hemp, coconut, flax, sunflower, and corn fibers have been used extensively, and further study is expected into different bioaggregates that allow diversifying of the raw materials. The objective of the research was to develop plant-based concretes with a matrix based on Portland cement and an aggregate of Agave salmiana (AS) leaves, obtained from the residues of the tequila industry that have no current purpose, as a total replacement for the calcareous aggregates commonly used in the manufacturing of mortars and whose extraction is associated with high levels of pollution, to improve their thermal properties and reduce the energy demand for air conditioning in homes. Characterization tests were carried out on the raw materials and the vegetal aggregate was processed to improve its compatibility with the cement paste through four different treatments: (a) freezing (T/C), (b) hornification (T/H), (c) sodium hydroxide (T/NaOH), and (d) solid paraffin (T/P). The effect of the treatments on the physical properties of the resulting composite was evaluated by studying the vegetal concrete under thermal conductivity, bulk density, and compressive strength tests with a volumetric ratio between the vegetal aggregate and the cement paste of 0.36 and a water/cement ratio of 0.35. The hornification treatment showed a 15.2% decrease in the water absorption capacity of the aggregate, resulting in a composite with a thermal conductivity of 0.49 W/mK and a compressive strength of 8.66 MPa, which allows its utilization as a construction material to produce prefabricated blocks.

Concrete barely possesses tensile strength, and it is susceptible to cracking, which leads to a reduction of its service life. Consequently, it is significant to find a complementary material that helps alleviate these drawbacks. The aim of this research was to determine analytically and experimentally the effect of the addition of the steel fibers on the performance of the post-cracking stage on fiber-reinforced concrete, by studying four notch-to-depth ratios of 0, 0.08, 0.16, and 0.33. This was evaluated through 72 bending tests, using plain concrete (control) and fiber-reinforced concrete with volume fibers of 0.25% and 0.50%. Results showed that the specimens with a notch-to-depth ratio up to 0.33 are capable of attaining a hardening behavior. The study concludes that the increase in the dosage leads to an improvement in the residual performance, even though an increase in the notch-to-depth ratio has also occurred.

In post-tensioned systems, grouts act as a last line of defense to prevent the penetration of harmful compounds such as chlorides, moisture and other substances that cause corrosion in the prestressing steel. For this reason, improving grouts results in the enhancement of the overall durability of the structure. In this study, the physical properties of grouts with basalt microfiber additions in the amounts of 0.03, 0.07 and 0.10% with respect to the mix volume were evaluated. The fresh properties included flowability and unit mass. Specimens were fabricated to evaluate drying shrinkage, compressive strength, air permeability and rapid permeability to chloride ions. The incorporation of basalt microfibers showed a beneficial effect on the physical properties of the grout by increasing the drying shrinkage resistance and decreasing the permeability compared to the reference mix and two commercial dry prepackaged grouts. The optimal grout mix was the one with a percentage of basalt microfibers of 0.10%, which decreased drying shrinkage by 15.98% at 14 days compared to the reference mix, and permeability to chloride ions decreased by 10.82% compared to the control mix.

This article presents an experimental study to analyze the mechanical properties of a soil stabilized with ordinary Portland cement (OPC) under a sustainable approach consisting of a significant substitution of OPC for sugarcane bagasse ash (SCBA) to reduce the quantity of cement used in the stabilization, reaching the necessary mechanical requirements for its use as a subgrade layer. Soil specimens were elaborated with 3%, 5%, and 7% OPC as a stabilizing agent by weight of the soil. These mixtures were then partially substituted with 25%, 50%, and 75% SCBA, with these percentages being by weight of the stabilizer (OPC). Compaction, compressive strength, and California bearing ratio (CBR) tests were performed to evaluate the mechanical properties of the specimens. The results indicate that a 25% substitution of OPC by SCBA shows a similar performance to the mixture with only Portland cement, so a reduction in OPC use can be made. Further, with a substitution of 100% OPC by SCBA, the CBR of natural soil without stabilizers is improved.

The original concept of “Total Prestress” consists of creating compressions in concrete without generating tension stresses for service load, while in "Partially Prestressed” elements, tensions are allowed in the service stage, which would produce some cracking depending on applied loads that will be taken with non-prestressed reinforcement. Using criteria and design recommendations can guarantee maximum flexural capacity and admissible serviceability requirements of partially prestressed elements; however, there is insufficient research for estimating more accurately the required parameters for the design and review of these types of elements. Because of this, the present investigation consisted in the realization of experimental studies in continuous partially prestressed beams with unbonded tendons for the evaluation of the flexural behavior for different stages of load determining the actual stresses and the strains taking into account the structural stiffness decrease and its effect on deflections. The dimensions of the specimens were selected based on common dimensions presented on slabs. The tested specimens considered variables such as the relationship between the length of the continuous spans, the cross-section, and the partial prestressing ratio. Afterward, equations were proposed to predict the decrease in the structural stiffness, depending on the degree of cracking, the type of cross-section, the partial prestressing ratio, and the magnitude of the applied load and the tension and compression stresses to estimate the probable deflections for a particular loading stage. The crack width equation presented a difference of −16% to +18% with respect to the experimental data, while the flexural stiffness equation showed a highly accurate correlation to the experimental data.