Injection molding technology is widely utilized across various industries for its ability to fabricate complex-shaped components with exceptional dimensional accuracy. However, challenges related to injection quality often arise, necessitating innovative approaches for improvement. This study investigates the influence of surface roughness on the efficiency of conformal cooling channels produced using additive manufacturing technologies, specifically Direct Metal Laser Sintering (DMLS) and Atomic Diffusion Additive Manufacturing (ADAM). Through a combination of experimental measurements, including surface roughness analysis, scanning electron microscopy, and cooling system flow analysis, this study elucidates the impact of surface roughness on coolant flow dynamics and pressure distribution within the cooling channels. The results reveal significant differences in surface roughness between DMLS and ADAM technologies, with corresponding effects on coolant flow behavior. Following that fact, this study shows that when cooling channels’ surface roughness is lowered up to 90%, the reduction in coolant media pressure is lowered by 0.033 MPa. Regression models are developed to quantitatively describe the relationship between surface roughness and key parameters, such as coolant pressure, Reynolds number, and flow velocity. Practical implications for the optimization of injection molding cooling systems are discussed, highlighting the importance of informed decision making in technology selection and post-processing techniques. Overall, this research contributes to a deeper understanding of the role of surface roughness in injection molding processes and provides valuable insights for enhancing cooling system efficiency and product quality.

This study investigates the challenges and potential of conventional injection molding for producing thick-walled optical components. The research primarily focuses on optimizing process parameters and mold design to enhance product quality. The methods include software simulations and experimental validation using polycarbonate test samples (optical lenses). Significant parameters such as melt temperature, mold temperature, injection pressure, and packing pressure were varied to assess their impact on geometric accuracy and visual properties. The results show that lower melt temperatures and higher mold temperatures significantly reduce the occurrence of dimensional defects. Additionally, the design of the gate system was found to be crucial in minimizing defects and ensuring uniform material flow. Effective packing pressure was essential in reducing volumetric shrinkage and sink marks. Furthermore, we monitored the deviation between the predicted and actual defects relative to the thickness of the sample wall. After optimization, the occurrence of obvious defects was eliminated across all sample thicknesses (lenses), and the impact of the critical defect, the sink mark on the planar side of the lens, was minimized. These findings demonstrate the substantial potential of conventional injection molding to produce high-quality thick-walled parts when these parameters are precisely controlled. This study provides valuable insights for the efficient design and manufacturing of optical components, addressing the growing demand for high-performance thick-walled plastic products.

This publication deals with the study of the mechanical properties of injection-molded polypropylene parts depending on the process parameters and the distance from the gate location in which the mechanical properties were investigated. Due to the fact that the mechanical properties of injection-molded parts are not the same at all locations, this research was designed to investigate the inhomogeneity of the properties of injection-molded parts along the length of the product. The inhomogeneity is affected by various influences, including distance from the sprue mouth, melt and mold temperature, injection pressure, crystal structure, and others. It was demonstrated that mechanical properties are not uniform over the entire injected product. Contrary to popular belief, mechanical properties can vary along the flow length due to uneven cooling and process parameters. Injection pressure and mold temperature significantly affect the mechanical properties of the injection-molded parts. The limiting injection pressure is 40 MPa and the mold temperature is 40 °C. The difference in individual spots in an injected article was up to 37%. Changes in mechanical properties are closely related to changes in morphology (crystallinity measured by DSC) caused by different injection molding process parameters. As is evident from the aforementioned results, the possible benefits of this work for injection molding of polymer products are apparent. Suitably chosen gate location, surface of the cavity, and process parameters can ensure targeted improvement of mechanical properties in stressed parts of a product.

This study describes the effect of electron radiation on the nano-mechanical properties of surface layers of selected polyamide (PA) types. Electron radiation initiates the cross-linking of macromolecules in the polyamide structure, leading to the creation of a 3D network which fundamentally changes the properties of the tested polymers. Selected types of polyamide (PA 6, PA 66 and PA 9T) were exposed to various intensities of electron radiation (33 kGy, 66 kGy, 99 kGy, 132 kGy, 165 kGy and 198 kGy). The cross-linked polyamides’ surface properties were measured by means of the modern nano-indentation technique (Depth Sensing Indentation; DSI), which operates on the principle of the immediate detection of indenter penetration depth in dependence on the applied load. The evaluation was preformed using the Oliver–Pharr method. The effect of electron radiation on the tested polyamides manifested itself in the creation of a 3D network, which led to an increase of surface layer properties, such as indentation hardness, elastic modulus, creep and temperature resistance, by up to 93%. The increase of temperature and mechanical properties substantially broadens the field of application of these materials in technical practice, especially when higher temperature resistance is required. The positive changes to the nano-mechanical properties as well as mechanical and temperature capabilities instigated by the cross-linking process were confirmed by the gel volume test. These measurements lay the foundation for a detailed study of this topic, as well as for a more effective means of modifying chosen properties of technical polyamide products by radiation.

This study focuses on the problematic of polyamide 6 containing various concentrations of cross-linking agent that was exposed to electron radiation. It is important to improve the material properties of polymers as much as possible. This endeavor can be realized by numerous methods, one of which is radiation exposure. This study investigates the effect of electron beam radiation in doses ranging from 66 to 132 kGy on the micro-mechanical properties of polymers, specifically polyamide 6 filled with 1, 3 and 5 wt.% of cross-linking agent triallyl isocyanurate (TAIC). The changes in the material brought by the radiation exposure were quantified by measurements of indentation hardness and modulus, which were the main measured micro-mechanical properties. Furthermore, thermo-mechanical analysis (TMA) was chosen to confirm the results of the material cross-linking, while the effect of degradation was investigated by Fourier-transform infrared spectroscopy (FTIR). In pursuit of complete evaluation, the topography of the test subject’s surface was explored by atomic force microscopy (AFM). The optimal concentration/radiation ratio was found in polyamide 6 enriched by 5 wt.% concentration of TAIC, which was irradiated by 132 kGy. Material treated in such a way had its indentation hardness by 33% and indentation modulus improved by 26% in comparison with the untreated material. These results were subsequently confirmed by the TMA and FTIR methods.

Fused Filament Fabrication (FFF) printers are usually designed to create a product with one single material. Some of them allow fabricating items in multiple colours but creating a single product consisting of two different materials remains an advantage of industrial 3D printers only. The aim of this research was to develop a design of a device with two printheads which enables to print products with two different materials, compatible with a cheap and commonly available FFF device Prusa i3MK2S, and the subsequent production of a prototype. A key aspect of the design was the hardware compatibility of the device with the given printer while maintaining the maximum possible printing area.