Cu-doped TiO₂ films were synthesized directly on FTO glass with a spin coating method. With a variation in copper amount, samples were prepared with 0%, 1%, 2%, 4% and 8% of dopant concentrations. Morphological and structural characterization of undoped and Cu-doped TiO₂ samples were investigated and the obtained results showed the small, spherical shapes of the nanoparticles forming a thin film on top of FTO glass and their preferred orientation of TiO₂ anatase (101), which is the same for each sample. However, this peak exhibited a slight shift for the 2% sample, related to the inflation of the microstrain compared to the other samples. For the optical properties, the 4% sample displayed the highest transmittance whereas the 2% sample exhibited the lowest band gap energy of 2.96 eV. Moreover, the PL intensity seems to be at its highest for the 2% sample due to the present peaking defects in the structure, whereas the 8% sample shows a whole new signal that is related to copper oxide. These properties make this material a potential candidate to perform as an electron transport layer (ETL) in solar cells and enhance their power conversion efficiency.

This study presents a comparative analysis of anodization and hydrothermal techniques for synthesizing TiO₂ nanotubes directly on titanium foil. It emphasizes its advantages as a substrate due to its superior conductivity and efficient charge transfer. Optimized synthesis conditions enable a thorough evaluation of the resulting nanotubes’ morphology, structure, and optical properties, ultimately assessing their photoelectrochemical and photocatalytic performances. Scanning electron microscopy (SEM) reveals differences in tube diameter and organization. An X-ray diffraction (XRD) analysis shows a dominant anatase (101) crystal phase in both methods, with the hydrothermally synthesized nanotubes exhibiting a biphase structure after annealing at 500 °C. UV–Vis and photoluminescence analyses indicate slight variations in band gaps (around 0.02 eV) and recombination rates. The anodized TiO₂ nanotubes, exhibiting superior hydrophilicity and order, demonstrate significantly enhanced photocatalytic degradation of a model pollutant, amido black (80 vs. 78%), and achieve a 0.1% higher photoconversion efficiency compared to the hydrothermally synthesized tubes. This study underscores the potential advantages of the anodization method for photocatalytic applications, particularly by demonstrating the efficacy of direct TiO₂ nanotube growth on titanium foil for efficient photocatalysis.

This work focused on the photocatalytic performance enhancement of titanium dioxide (TiO₂) nanotubes decorated by gold nanoparticles. The surface of the nanotubes synthesized using the anodization technique was modified with subsequent deposition of gold nanoparticles (Au-NPs) via electrophoretic deposition. The impact of electrophoretically deposited gold nanoparticles (Au-NPs) on TiO₂ nanotubes, with varying deposition times (5 min, 8 min and 12 min), was investigated in the degradation of amido black (AB) dye. The morphological analysis using scanning electron microscopy (SEM, TESCAN VEGA3, TESCAN Orsay Holding, Brno, Czech Republic) and transmission electron microscopy (TEM, JEM—100CX2, JEOL Japan). revealed a well-organized nanotubular structure of TiO₂, with a wall thickness of 25 nm and an internal diameter of 75 nm. Optical study, including photoluminescence and diffuse reflectance spectroscopy, provided evidence of charge transfer between the Au-NPs and the TiO₂-NTs. Furthermore, the photocatalytic measurements showed that the enhanced photocatalytic activity of the TiO₂-NTs resulted from successful Au deposition onto their surface, surpassing that of the pure sample. This improvement is attributed to the higher work function of gold nanoparticles, which effectively promoted the separation of photogenerated electron–hole pairs. The sample Au-NPs/TiO₂-NTs with a deposition time of 5 min exhibited the best photocatalytic efficiency, achieving an 85% degradation rate after 270 min under UV irradiation. Moreover, the enhancement obtained was also attributed to the plasmonic effect induced by Au-NPs. Kinetic investigations revealed that the photocatalytic reaction followed apparent first-order kinetics, highlighting the efficiency of Au-NPs/TiO₂-NTs as a photocatalyst for dye degradation.

To enhance the photocatalytic performance of TiO₂ nanotubes (NTs) for the degradation of Amido Black as an organic pollutant, electrodeposition of bismuth vanadate (BiVO₄) nanostructures was successfully applied. The effect of electrodeposited BiVO₄ (25 s, 50 s, 150 s, 250 s), followed by a thermal treatment on TiO₂-NTs, was studied. The structures of the as-prepared samples were characterized by X-ray diffraction (XRD). Morphological behavior was investigated using Scanning Electron Microscopy (SEM) and Transmission Electron Microscopy (TEM), both coupled with EDX. Optical characterizations were performed using photoluminescence and diffuse reflectance spectroscopy. The BiVO₄/TiO₂ NTs sample with 50 s deposition time gave the highest photocatalytic performance for Amido Black degradation, 99.4% after 150 min under UV light. This result has been achieved due to the structure and the optical properties of the sample. The heterojunction of both catalysts showed the synergetic effect on the photocatalytic performance where they remained stable after five cycling runs. Furthermore, quenching tests were conducted and proved that superoxide radicals (O₂^•) are the main active species during photodegradation process.

Titanium dioxide nanotubes (TiO₂ NTs) decorated with lead sulfide nanoparticles (PbS NPs) were synthesized using the Successive Ionic Layer Adsorption and Reaction (SILAR) method at different number (n) of cycles (where n = 3, 5, and 8) and evaluated for tetracycline (TC) photodegradation under UV light. PbS NPs/TiO₂ NTs heterojunctions prepared with 5 SILAR cycles showed optimal photocatalytic activity. Also, under optimized conditions, pure TiO₂ NTs achieved complete TC photodegradation (99%) within 5 h under UV irradiation, with a proposed degradation mechanism based on holes (h⁺) and hydroxyl radicals (•OH) as dominant reactive species.

Successive ionic layer adsorption reaction (SILAR) was used to deposit Cu₂O nanosheets on anodized TiO₂ nanotubes at different deposition cycles (4, 8, 15, and 20). Compared to the bare TiO₂ nanotubes, these coatings were investigated for their tribological behavior (friction, wear and energy loss), scanning and transmission electron microscopy (SEM, TEM), X-ray Diffraction (XRD) was used to characterize Cu₂O/TiO₂ coatings to study the effect of number of cycles on the morphological and structural properties of the samples; these characteristics engage in determining the wear mechanisms. The assessment of the coating’s adhesion was determined by the obtained critical loads from the scratch test; the 15 cycles Cu₂O/TiO₂ exhibited higher critical loads, which corresponds to improved adhesion. This sample also showed a low wear volume of 7.5 × 10⁶ µm³ compared to other samples but higher energy loss due to the low shear strength of copper oxide. The friction coefficient, however, decreased from 0.7 for bare TiO₂ nanotubes to 0.48 for 20 cycles Cu₂O/TiO₂ coatings at higher loads, which proves the wear resistance enhancement. Since these coatings will be manufactured for orthopedic and dental implant applications, the corrosion resistance was tested, and the 15 cycles Cu₂O-NPs/TiO₂-NTs where these coatings exhibited the most favorable combination of a low corrosion current density (1.9 × 10⁻⁴ A/cm²) and a noble corrosion potential (−0.3 V/SCE); furthermore, there was a polarization resistance of 2.4 × 10⁴ Ω·cm² and a protection efficiency of 96.7%, indicating significantly enhanced corrosion resistance as opposed to the other samples.