Conventionally used brass alloy CuZn30 shows problems with corrosion resistance in the form of dezincification when used in brass instruments. Therefore, within the scope of this investigation, a new brass alloy CuZn30 is developed in the microalloy range with corrosion-free or corrosion-inhibiting properties. First, the influence of microalloying elements on the phase composition is investigated by simulation using Thermo-Calc. On the basis of this, suitable alloying elements and contents are selected and a modified CuZn30X alloy with 0.1% phosphorus, tin, and nickel in mass fractions, respectively, is produced. The modified alloy is then investigated with regard to its mechanical and microstructural composition and its corrosion properties. The corrosion properties were examined using stress corrosion cracking tests, dezincification tests, and the recording of polarization curves. The modified alloy exhibited good cold and hot rolling properties as well as good corrosion resistance. The dezincification test confirmed the improved corrosion resistance of the modified CuZn30X alloy, which is attributed to the formation of a protective top layer due to the alloying elements.

This study focuses on the effect of pre-deformation on hydrogen diffusion and hydrogen embrittlement of the high alloy austenitic TRIP steel X3CrMnNiMo17-8-4. Different cold-rolled steel sheets with thicknesses of ≤400 µm were electrochemically charged on both sides in 0.1 M sodium hydroxide with hydrogen for two weeks. Comparative measurements on uncharged and immersed samples prove that hydrogen causes embrittlement in this steel for all investigated states. The embrittlement increases with increasing pre-deformation and is accompanied by deformation-induced martensite formation. The corresponding fractured surfaces were examined using electron microscopy and compared to modelled hydrogen distributions with previously determined diffusion coefficients. For this purpose, various diffusion coefficients are determined using the Devanathan–Stachurski permeation test and hot extraction in order to describe the diffusion process. The hydrogen concentration profiles and the fractographic analyses show a good agreement, so this study provides a basis for estimating the embrittlement behaviour for later application.