The research and development of new materials such as particle-reinforced aluminum matrix composites (AMCs) will only result in a successful innovation if these materials show significant advantages not only from a technological, but also from an economic point of view. Against this background, in the Collaborative Research Center SFB 692, the concept of an integrated technology, user, and market analysis and forecast has been developed as a means for assessing the technological and commercial potential of new materials in early life cycle stages. After briefly describing this concept, it is applied to AMCs and the potential field of manufacturing aircraft components. Results show not only technological advances, but also considerable economic potential—the latter one primarily resulting from the possible weight reduction being enabled by the increased yield strength of the new material.

The reinforcement of aluminum alloys with particles leads to the enhancement of their mechanical properties at room temperature. However, the creep behavior at elevated temperatures is often negatively influenced. This raises the question of how it is possible to influence the creep behavior of this type of material. Within this paper, selected creep and tensile tests demonstrate the beneficial effects of boron on the properties of precipitation-hardenable aluminum matrix composites (AMCs). The focus is on the underlying microstructure behind this effect. For this purpose, boron was added to AMCs by means of mechanical alloying. Comparatively higher boron contents than in steel are investigated in order to be able to record their influence on the microstructure including the formation of potential new phases as well as possible. While the newly formed phase Al₃BC can be reliably detected by X-ray diffraction (XRD), it is difficult to obtain information about the phase distribution by means of scanning electron microscopy (SEM) and scanning transmission electron microscopy (STEM) investigations. An important contribution to this is finally provided by the investigation using Raman microscopy. Thus, the homogeneous distribution of finely scaled Al₃BC particles is detectable, which allows conclusions about the microstructure/property relationship.