The technology of high-density electropulsing has been applied to increase the performance of metallic materials since the 1990s and has shown significant advantages over traditional heat treatment in many aspects. However, the microstructure changes in electropulsing treatment (EPT) metals and alloys have not been fully explored, and the effects vary significantly on different material. When high-density electrical pulses are applied to metals and alloys, the input of electric energy and thermal energy generally leads to structural rearrangements, such as dynamic recrystallization, dislocation movements and grain refinement. The enhanced mechanical properties of the metals and alloys after high-density electropulsing treatment are reflected by the significant improvement of elongation. As a result, this technology holds great promise in improving the deformation limit and repairing cracks and defects in the plastic processing of metals. This review summarizes the effect of high-density electropulsing treatment on microstructural properties and, thus, the enhancement in mechanical strength, hardness and corrosion performance of metallic materials. It is noteworthy that the change of some properties can be related to the structure state before EPT (quenched, annealed, deformed or others). The mechanisms for the microstructural evolution, grain refinement and formation of oriented microstructures of different metals and alloys are presented. Future research trends of high-density electrical pulse technology for specific metals and alloys are highlighted.

Magnesium (Mg)-based materials are promising candidates for hydrogen storage due to the low cost, high hydrogen storage capacity and abundant resources of magnesium for the realization of a hydrogen society. However, the sluggish kinetics and strong stability of the metal-hydrogen bonding of Mg-based materials hinder their application, especially for onboard storage. Many researchers are devoted to overcoming these challenges by numerous methods. Here, this review summarizes some advances in the development of Mg-based hydrogen storage materials related to downsizing and catalysis. In particular, the focus is on how downsizing and catalysts affect the hydrogen storage capacity, kinetics and thermodynamics of Mg-based hydrogen storage materials. Finally, the future development and applications of Mg-based hydrogen storage materials is discussed.

Natural serpentine powders are applicable as additives for various lubricating oils. However, no uniform theories explain their tribological performance, lubrication, and wear mechanism, especially their self-repairing mechanism. Herein, the influence of different nano serpentine powders (NSPs) contents in liquid paraffin on the friction and wear characteristics of steel balls and the self-repairing process of NSPs on the worn surface were studied. Results show that the optimal amount of NSPs was 0.5 wt %. Relative to those of the base oil, the friction coefficients and wear spot diameters were reduced by 22.8% and 34.2%, respectively. Moreover, the long-term tribological test shows that the wear scar diameter decreased slightly after 3 h, reaching the state of dynamic balance between wear and repair. The outstanding tribological performance should be attributed to the formed bilayer tribofilm, the first layer of which contains nanoparticles surrounded by lubricants and the second layer of which contains nanoparticles compacted onto the surface of the steel ball.

Silver nanowires are receiving increasing attention as a kind of prospective transparent and conductive material. Here, we successfully synthesized high-performance silver nanowires with a significantly decreased reaction time by a modified polyol method. The synthesis process involved the addition of halides, including NaCl and NaBr, to control the release rate of Ag⁺ ions, as Cl⁻ and Br⁻ ions react with Ag⁺ ions to form AgCl and AgBr with different solubilities. As a result, Ag⁺ ions could be slowly released by graded dissolution, and the formation of silver nanowires was promoted. The results showed that the concentration of the added halides played an important role in the morphology of the final product. High-quality silver nanowires with an average diameter of 70 nm and average length of 21 μm were obtained by optimizing the reaction parameters. Afterwards, a simple silver nanowire coating was applied in order to fabricate the transparent conductive films. The film that was based on the silver nanowires provided a transmittance of 91.2% at the 550 nm light wavelength and a sheet resistance of about 78.5 Ω·sq⁻¹, which is promising for applications in flexible and transparent optoelectronic devices.

In this work, we present a cellulose acetate membrane flexible supercapacitor prepared through a direct writing method. A carbon nanotube (CNT) and silver (Ag) nanoparticle were prepared into ink for direct writing. The composite electrode displayed excellent electrochemical and mechanical electrochemical performance. Furthermore, the CNT-Ag displayed the highest areal capacity of 72.8 F/cm³. The assembled device delivered a high areal capacity (17.68 F/cm³) at a current density of 0.5 mA/cm², a high areal energy (9.08–5.87 mWh/cm³) at a power density of 1.18–0.22 W/cm³, and showed no significant decrease in performance with a bending angle of 180°. The as-fabricated CNT/Ag electrodes exhibited good long-term cycling stability after 1000 time cycles with 75.92% capacitance retention. The direct writing was a simple, cost-effective, fast, and non-contact deposition method. This method has been used in current printed electronic devices and has potential applications in energy storage.