Large quantities of tobacco stalks residues are generated and discarded as crop waste or combusted directly every year. Thus, we need to find an appropriate way to dispose of this type of waste and recycle it. The conversion of biomass waste into electrode materials for supercapacitors is entirely in line with the concept of sustainability and green. In this paper, tobacco-stalk-based, porous activated carbon (TC) was successfully synthesized by high-temperature and high-pressure hydrothermal pre-carbonization and KOH activation. The synthesized TC had a high pore volume and a large surface area of 1875.5 m² g⁻¹, in which there were many mesopores and interconnected micro-/macropores. The electrochemical test demonstrated that TC-1 could reach a high specific capacitance of up to 356.4 F g⁻¹ at a current density of 0.5 A g⁻¹, which was carried in 6M KOH. Additionally, a symmetrical supercapacitor device was fabricated by using TC-1 as the electrode, which delivered a high energy density up to 10.4 Wh kg⁻¹ at a power density of 300 W kg⁻¹, and excellent long-term cycling stability (92.8% of the initial capacitance retention rate after 5000 cycles). Therefore, TC-1 is considered to be a promising candidate for high-performance supercapacitor electrode materials and is a good choice for converting tobacco biomass waste into a resource.

Ag nanoparticles were successfully prepared using a liquid reduction method with a suitable mixture reductant of polyethylene glycol (PEG) and ethylene glycol (EG). OP-10 as a dispersing agent, was used to prepare the conductive Ag ink. Ag nanoparticles with an average particle size of 40 nm were prepared while the ratio of PEG to EG was 1:2. Meanwhile, the Ag particles had a narrow size distribution and great dispersion performance. The effects of paper substrates, sintering temperature, and sintering time on the conductivity of the printed Ag ink pattern were also studied. It was found that Lucky porous high glossy photo paper was a good candidate as the printing substrate. The resistivity of the printed pattern could reach 5.1 × 10⁻³ Ω·cm after heated at 100 °C for 2 h. Hence, the printed pattern showed good conductivity which led to the LED light being on. Furthermore, the Ag nanoparticle ink could be printed to form any pattern as required that still showed good electrical conductivity after being sintered under low-temperature. This could provide new possibilities for the preparation of flexible electrodes.

Silver nanowires are receiving increasing attention as a kind of prospective transparent and conductive material. Here, we successfully synthesized high-performance silver nanowires with a significantly decreased reaction time by a modified polyol method. The synthesis process involved the addition of halides, including NaCl and NaBr, to control the release rate of Ag⁺ ions, as Cl⁻ and Br⁻ ions react with Ag⁺ ions to form AgCl and AgBr with different solubilities. As a result, Ag⁺ ions could be slowly released by graded dissolution, and the formation of silver nanowires was promoted. The results showed that the concentration of the added halides played an important role in the morphology of the final product. High-quality silver nanowires with an average diameter of 70 nm and average length of 21 μm were obtained by optimizing the reaction parameters. Afterwards, a simple silver nanowire coating was applied in order to fabricate the transparent conductive films. The film that was based on the silver nanowires provided a transmittance of 91.2% at the 550 nm light wavelength and a sheet resistance of about 78.5 Ω·sq⁻¹, which is promising for applications in flexible and transparent optoelectronic devices.

For the development of light, flexible, and wearable electronic devices, it is crucial to develop energy storage components combining high capacity and flexibility. Herein, an all-solid-state supercapacitor is prepared through an in situ growth method. The electrode contains polyaniline deposited on a carbon nanotube and a poly (ethylene-co-vinyl acetate) film. The hybrid electrode exhibits excellent mechanical and electrochemical performance. The optimized few-layer polyaniline wrapping layer provides a conductive network that effectively enhances the cycling stability, as 66.4% of the starting capacitance is maintained after 3000 charge/discharge cycles. Furthermore, the polyaniline (PANI)-50 displays the highest areal energy density of 83.6 mWh·cm⁻², with an areal power density of 1000 mW·cm⁻², and a high areal capacity of 620 mF cm⁻². The assembled device delivers a high areal capacity (192.3 mF·cm⁻²) at the current density of 0.1 mA·cm⁻², a high areal energy (26.7 mWh·cm⁻²) at the power density of 100 mW·cm⁻², and shows no significant decrease in the performance with a bending angle of 180°. This unique flexible supercapacitor thus exhibits great potential for wearable electronics.

In this work, we present a cellulose acetate membrane flexible supercapacitor prepared through a direct writing method. A carbon nanotube (CNT) and silver (Ag) nanoparticle were prepared into ink for direct writing. The composite electrode displayed excellent electrochemical and mechanical electrochemical performance. Furthermore, the CNT-Ag displayed the highest areal capacity of 72.8 F/cm³. The assembled device delivered a high areal capacity (17.68 F/cm³) at a current density of 0.5 mA/cm², a high areal energy (9.08–5.87 mWh/cm³) at a power density of 1.18–0.22 W/cm³, and showed no significant decrease in performance with a bending angle of 180°. The as-fabricated CNT/Ag electrodes exhibited good long-term cycling stability after 1000 time cycles with 75.92% capacitance retention. The direct writing was a simple, cost-effective, fast, and non-contact deposition method. This method has been used in current printed electronic devices and has potential applications in energy storage.

The poor tribological performances of titanium have significantly limited its applications in the field of artificial joints. In order to solve problems regarding the wear and corrosion of artificial joints in the body, we fabricated the composite materials utilizing the combination of laser surface texturing and nitrogen ion implantation technology, and investigated the effect of laser surface texturing, nitrogen ion implantation, and different dimple area densities on tribological performance. The results show that the textured surface could reduce the friction coefficient and improve the wear resistance, and the optimum dimple density was found to be 25%. After N ion implantation, the wear resistance of the textured sample was further improved, due to the formation of the nitride layer. Moreover, as shown by the electrochemical test results, the corrosion resistance was enhanced significantly. The friction coefficient decreased the most, and the wear resistance increased by 405% with the lowest wear rate of 0.37 × 10⁻³ mm³/N·m. However, the specimen with a dimple density of 60% had the worst wear resistance. The results of the study provide a basis for the development and application of artificial joint materials.