Biodegradable zinc (Zn) has attracted increasing interest as a material for temporary implants, primarily due to its moderate degradation kinetics. In recent years, additive manufacturing of Zn alloys using the laser powder bed fusion method (L-PBF) has shown promising results. Compared to as-cast Zn alloys, it offers preferable customized solutions for patient-specific temporary biomedical implants. Due to the novelty of these printed degradable biomaterials and due to reported cytotoxic effects of Zn alloys, this study investigates additively manufactured ZnAgCu, ZnAgCuMn, and ZnAgCuTi alloys, both in as-printed and post-processed conditions, with a focus on L929 and SAOS-2 biocompatibility. In this work, we demonstrate that the increased porosity and therefore larger surface areas compared to polished Zn-alloy samples affect their biocompatibility. Minimal to no cell proliferation was observed on and near the Zn-alloy test plates after 24 h. Undiluted extracts from as-cast Zn and L-PBF-manufactured plates were initially cytotoxic to SAOS-2 cells. However, as passivation proceeded, cytocompatibility was significantly increased from day 3 onward. Zn²⁺ ion release peaked at 24 h and declined significantly from day 2 to day 10. Compared to the other Zn alloys, ZnAgCuMn exhibited the lowest cytocompatibility. Most intriguingly, 3-month surfaces exhibited reduced cytocompatibility to osteoblasts compared to freshly polished samples. The observed in vitro cytotoxicity motivates further investigation of as-printed and post-processed L-PBF-manufactured Zn alloys, aiming to develop novel surface modification strategies to mitigate the initial ion burst responsible for reduced cytocompatibility and to adjust and tailor the overall degradation kinetics to physiologically tolerable levels tailored to the intended clinical application.

Biodegradable implants as bone fixations may present a safe alternative to traditional permanent implants, reducing the risk of infections, promoting bone healing, and eliminating the need for removal surgeries. Structural integrity is an important consideration when choosing an implant material. As a biodegradable implant is being resorbed, until the natural bone has regrown, the implant material needs to provide mechanical stability. However, the corrosive environment of the human body may affect the fatigue life of the material. Conversely, mechanical stress can have an effect on electrochemical corrosion processes. This is known as corrosion fatigue. In the presented work, an experimental setup and methodology was established to analyze the corrosion fatigue of experimental bioresorbable materials while simultaneously monitoring the electrochemical processes. A double-walled measurement cell was constructed for a three-point bending test in Dulbecco‘s Phosphate-Buffered Saline (DPBS^{− −}), which was used as simulated body fluid (SBF), at 37 ± 1 °C. The setup was combined with a three-electrode setup for corrosion measurements. Rod-shaped zinc samples were used to validate the setup’s functionality. Preliminary static and dynamic bending tests were carried out as per the outlined methodology to determine the test parameters. Open-circuit as well as potentiostatic polarization measurements were performed with and without mechanical loading. For the control, fatigue tests were performed in an air environment. The tested zinc samples were inspected via scanning electron microscopy (SEM). Based on the measured mechanical and electrochemical values as well as the SEM images, the effects of the different environments were investigated, and the setup’s functionality was verified. An analysis of the data showed that a comprehensive investigation of corrosion fatigue characteristics is feasible with the outlined approach. Therefore, this novel methodology shows great potential for furthering our understanding of the effects of corrosion on the fatigue of biodegradable implant materials.