Zinc (Zn) and Zn-based alloys have been proposed as a new generation of absorbable metals mainly owing to the moderate degradation behavior of zinc between magnesium and iron. Nonetheless, mechanical strength of pure Zn is relatively poor, making it insufficient for the majority of clinical applications. In this study, a novel Zn–2Ag–1.8Au–0.2V (wt.%) alloy (Zn–Ag–Au–V) was fabricated and investigated for use as a potential absorbable biocompatible material. Microstructural characterization indicated an effective grain-refining effect on the Zn alloy after a thermomechanical treatment. Compared to pure Zn, the Zn–Ag–Au–V alloy showed significantly enhanced mechanical properties, with a yield strength of 168 MPa, an ultimate tensile strength of 233 MPa, and an elongation of 17%. Immersion test indicated that the degradation rate of the Zn–Ag–Au–V alloy in Dulbecco’s phosphate buffered saline was approximately 7.34 ± 0.64 μm/year, thus being slightly lower than that of pure Zn. Biocompatibility tests with L929 and Saos-2 cells showed a moderate cytotoxicity, alloy extracts at 16.7%, and 10% concentration did not affect metabolic activity and cell proliferation. Plaque formation in vitro was reduced, the Zn–Ag–Au–V surface inhibited adhesion and biofilm formation by the early oral colonizer Streptococcus gordonii, indicating antibacterial properties of the alloy.

The micro- and nanostructures, chemical composition, and wettability of titanium surfaces are essential for dental implants’ osseointegration. Combining hydrophilicity and nanostructure has been shown to improve the cell response and to shorten the healing time. This study aimed to investigate the biological response to different wettability levels and nanotopographical modifications in aged and non-aged titanium surfaces. By plasma etching titanium surfaces with the fluorine gas 2,3,3,3-tetrafluoropropene (R1234yF), additional nanostructures were created on the sample surfaces. Furthermore, this treatment resulted in sustained superhydrophilicity and fluoride accumulation. We examined the effect of various nanostructuring processes and aging using scanning electron microscopy, roughness analyses, and wettability measurement. In addition, all the surface modifications were tested for their effects on fibroblast adhesion, proliferation, and viability as well as osteoblast differentiation. Our study indicates that the plasma etching, with 2,3,3,3-tetrafluoropropene, of the machined and SLA surface neither favored nor had an adverse effect on the biological response of the SAOS-2 osteoblast cell line. Although the fluorine-plasma-etched surfaces demonstrated improved fibroblast cell viability, they did not lead to improved early osseointegration. It is still unclear which surface properties mainly influence fibroblast and osteoblast adhesion. Further physiochemical aspects, such as electrostatic interaction and surface tension, are crucial to be analyzed along with wettability and roughness.

Various surface modification strategies are being developed to endow dental titanium implant surfaces with micro- and nano-structures to improve their biocompatibility, and first of all their osseointegration. These modifications have the potential to address clinical concerns by stimulating different biological processes. This study aims to evaluate the biological responses of ananatase-modified blasted/etched titanium (SLA-anatase) surfaces compared to blasted/acid etched (SLA) and machined titanium surfaces. Using unipolar pulsed direct current (DC) sputtering, a nanocrystalline anatase layer was fabricated. In vitro experiments have shown that SLA-anatase discs can effectively promote osteoblast adhesion and proliferation, which are regarded as important features of a successful dental implant with bone contact. Furthermore, anatase surface modification has been shown to partially enhance osteoblast mineralization in vitro, while not significantly affecting bacterial colonization. Consequently, the recently created anatase coating holds significant potential as a promising candidate for future advancements in dental implant surface modification for improving the initial stages of osseointegration.

Foreign body reaction (FBR), an immune-mediated complex healing process, plays a crucial role in integrating implants into the body. Macrophages, as the first line of immune system interaction with implant surfaces, play a bidirectional role in modulating the inflammation-regeneration balance. For a deep understanding and the evaluation of the reactions between implant materials and immune responses, reliable in vitro methods and protocols are pivotal. Among different in vitro models, primary monocyte-derived macrophages (MDMs) present an excellent model for investigating macrophage-implant interactions. We have implemented an experimental protocol to evaluate the polarization of MDMs into M1 (classically activated) and M2 (alternatively activated) macrophages on implant surfaces. We isolated blood monocytes from healthy donors and differentiated them into macrophages using macrophage colony-stimulating factor (M-CSF). Differentiated macrophages were cultured on implant surfaces and polarized into M1 and M2 subtypes. M1 polarization was achieved in the presence of interferon (IFN)-γ and lipopolysaccharide (LPS), while M2 polarization was performed in a medium containing interleukin (IL)-4 and IL-13. We evaluated macrophage phenotypes by Enzyme-linked Immunosorbent Assay (ELISA), confocal laser scanning microscopy (CLSM), and quantitative real-time PCR (qRT-PCR) based on panels of secreted cytokines, cell surface markers, and expressed genes. The extracted RNA was transformed into complementary DNA (cDNA), and qRT-PCR was used to quantify mRNA related to M1 and M2 macrophages. Accordingly, M1 macrophages have been characterized by higher expression of proinflammatory Tumor necrosis factor (TNF-α) cytokine and CCR7 surface marker compared to M2 macrophages, which exhibited higher levels of CD209 and CCL13. Consequently, CCR7 and CD209 were identified as specific and reliable markers of M1 and M2 macrophage subtypes by immunostaining and visualizing by CLSM. Further confirmation was achieved by ELISA detecting elevated TNF-ɑ level in M1 and increased CCL13 in M2 cells. The proposed markers and experimental setup can be used effectively to assess the immunomodulatory potential of implants.

Physicochemical modification of titanium implants aims to enhance early osseointegration by improving bioactivity. This study deposited and evaluated an anatase TiO₂ film on clinically relevant sandblasted, acid-etched titanium (Ti-SLA) to enhance in vitro bioactivity and osteogenic responses. An ~8 µm TiO₂-anatase coating was deposited on Ti-SLA by reactive pulsed DC magnetron sputtering. Surface characterization included FE-SEM, helium ion microscopy, and XRD. Wettability and surface free energy (SFE) were evaluated by contact angle analysis. In vitro bioactivity was assessed by hydroxyapatite (HA) formation in twofold-concentrated simulated body fluid (2× SBF). Osteoblast responses were evaluated through cell adhesion, viability, alkaline phosphatase activity, gene expression, and mineralization. The coating produced hierarchical multi-globular microstructures decorated with faceted anatase nanocrystals. Ti-SLA’s initial hydrophobicity converted to a superhydrophilic, high-energy surface with increased polar SFE. Homogeneous HA crystallites deposited exclusively on SLA-anatase in 2× SBF. SAOS-2 cells showed enhanced metabolic activity, ALP activity, osteogenic gene upregulation, and improved mineralized matrix, while primary human osteoblasts exhibited increased metabolic activity and calcium deposition. The anatase coating produced a superhydrophilic, high-energy micro-nano surface that accelerates HA formation and enhances osteoblast function in vitro, warranting in vivo validation for early osseointegration.

Biodegradable zinc (Zn) has attracted increasing interest as a material for temporary implants, primarily due to its moderate degradation kinetics. In recent years, additive manufacturing of Zn alloys using the laser powder bed fusion method (L-PBF) has shown promising results. Compared to as-cast Zn alloys, it offers preferable customized solutions for patient-specific temporary biomedical implants. Due to the novelty of these printed degradable biomaterials and due to reported cytotoxic effects of Zn alloys, this study investigates additively manufactured ZnAgCu, ZnAgCuMn, and ZnAgCuTi alloys, both in as-printed and post-processed conditions, with a focus on L929 and SAOS-2 biocompatibility. In this work, we demonstrate that the increased porosity and therefore larger surface areas compared to polished Zn-alloy samples affect their biocompatibility. Minimal to no cell proliferation was observed on and near the Zn-alloy test plates after 24 h. Undiluted extracts from as-cast Zn and L-PBF-manufactured plates were initially cytotoxic to SAOS-2 cells. However, as passivation proceeded, cytocompatibility was significantly increased from day 3 onward. Zn²⁺ ion release peaked at 24 h and declined significantly from day 2 to day 10. Compared to the other Zn alloys, ZnAgCuMn exhibited the lowest cytocompatibility. Most intriguingly, 3-month surfaces exhibited reduced cytocompatibility to osteoblasts compared to freshly polished samples. The observed in vitro cytotoxicity motivates further investigation of as-printed and post-processed L-PBF-manufactured Zn alloys, aiming to develop novel surface modification strategies to mitigate the initial ion burst responsible for reduced cytocompatibility and to adjust and tailor the overall degradation kinetics to physiologically tolerable levels tailored to the intended clinical application.