The development of hydroxyapatite (HAp) and polyether ether ketone (PEEK) biocomposites has been extensively studied for bone repair applications due to the synergistic properties of the involved materials. In this study, we aimed to develop HAp/PEEK biocomposites using high-energy ball milling, with HAp concentrations (20%, 40%, and 60% w/v) in PEEK, to evaluate their physicochemical, mechanical, cytotoxicity, and antimicrobial properties for potential applications in Tissue Engineering (TE). The biocomposites were characterized by structure, morphology, apparent porosity, diametral compression strength, cytotoxicity, and antimicrobial activity. The study results demonstrated that the HAp/PEEK biocomposites were successfully synthesized. The C2 biocomposite, containing 40% HAp, stood out due to the optimal distribution of HAp particles in the PEEK matrix, resulting in higher compression strength (246 MPa) and a homogeneous microstructure. It exhibited antimicrobial activity against Staphylococcus aureus, Pseudomonas aeruginosa, and Escherichia coli, with no cytotoxicity observed. These properties make the C2 biocomposite promising for regenerative medicine applications, combining mechanical strength, bioactivity, and biocompatibility.

Background/Objectives : This study investigates the development of 3D chitosan-x-cobalt ferrite scaffolds (x = 5, 7.5, and 10 wt%) with interconnected porosity for potential biomedical applications. The objective was to evaluate the effects of magnetic particle incorporation on the scaffolds’ structural, mechanical, magnetic, and biological properties, specifically focusing on their biocompatibility and antimicrobial performance. Methods: Scaffolds were synthesized using freeze-drying, while cobalt ferrite nanoparticles were produced via a pilot-scale combustion reaction. The scaffolds were characterized for their physical and chemical properties, including porosity, swelling, and mechanical strength. Hydrophilicity was assessed through contact angle measurements. Antimicrobial efficacy was evaluated using time kill kinetics and agar diffusion assays, and biocompatibility was confirmed through cytotoxicity tests. Results: The incorporation of cobalt ferrite increased magnetic responsiveness, altered porosity profiles, and influenced swelling, biodegradation, and compressive strength, with a maximum value of 87 kPa at 7.5 wt% ferrite content. The scaffolds maintained non-toxicity and demonstrated bactericidal activity. The optimal concentration for achieving a balance between structural integrity and biological performance was found at 7.5 wt% cobalt ferrite. Conclusions: These findings suggest that magnetic chitosan-cobalt ferrite scaffolds possess significant potential for use in biomedical applications, including tissue regeneration and advanced healing therapies. The incorporation of magnetic properties enhances both the structural and biological functionalities, presenting promising opportunities for innovative therapeutic approaches in reconstructive procedures.

The study aimed to utilize MoO₃ catalysts, produced on a pilot scale via combustion reaction, to produce biodiesel from residual oil. Optimization of the process was conducted using a 2³ experimental design. Structural characterization of the catalysts was performed through X-ray diffraction, fluorescence, Raman spectroscopy, and particle size distribution analyses. At the same time, thermal properties were examined via thermogravimetry and differential thermal analysis. Catalytic performance was assessed following process optimization. α-MoO₃ exhibited a monophasic structure with orthorhombic phase, whereas α/h-MoO₃ showed a biphasic structure. α-MoO₃ had a larger crystallite size and higher crystallinity, with thermal stability observed up to certain temperatures. X-ray fluorescence confirmed molybdenum oxide predominance in the catalysts, with traces of iron oxide. Particle size distribution analyses revealed polymodal distributions attributed to structural differences. Both catalysts demonstrated activity under all conditions tested, with ester conversions ranging from 93% to 99%. The single-phase catalyst had a long life cycle and was reusable for six biodiesel production cycles. The experimental design proved to be predictive and significant, with the type of catalyst being the most influential variable. Optimal conditions included α-MoO₃ catalyst, oil/alcohol ratio of 1/15, and a reaction time of 60 min, resulting in high biodiesel conversion rates and showcasing the viability of MoO₃ catalysts in residual oil biodiesel production.