CoCrFeMnNi high entropy alloys (HEAs) were additively manufactured (AM) by laser powder bed fusion and their corrosion resistance in 3.5 wt% NaCl solution was studied by potentiodynamic polarization and electrochemical impedance spectroscopy tests. A systematic study of AM CoCrFeMnNi HEAs’ porosity under a wide range of laser processing parameters was conducted and a processing map was constructed to identify the optimal laser processing window for CoCrFeMnNi HEAs. The near fully dense AM CoCrFeMnNi HEAs exhibit a unique non-equilibrium microstructure consisting of tortuous grain boundaries, sub-grain cellular structures, columnar dendrites, associated with some processing defects such as micro-pores. Compared with conventional as-cast counterpart, the AM CoCrFeMnNi HEAs showed higher pitting resistance (ΔE) and greater polarization resistance (R_p). The superior corrosion resistance of AM CoCrFeMnNi HEAs may be attributed to the homogeneous elemental distribution and lower density of micro-pores. Our study widens the toolbox to manufacture HEAs with exceptional corrosion resistance by additive manufacturing.

Ni40Co20Fe10Cr10Al18W2 additively manufactured using laser powder bed fusion (LPBF) is among the toughest as-built alloys reported and is a promising candidate for use in extreme environments. However, its behavior under multi-megabar pressure regimes remains unexplored. We used femtosecond in situ X-ray diffraction to investigate the shock response of LPBF Ni40Co20Fe10Cr10Al18W2 under laser-driven shock compression and release. Our results reveal that the initial dual-phase face-centered + body-centered structure transforms to a single face-centered phase over a wide pressure range of 84 +/- 10 to 277 +/- 55 GPa, followed by a transition to a single body-centered phase at 431 +/- 48 GPa. We establish the Hugoniot equation-of-state of LPBF Ni40Co20Fe10Cr10Al18W2 and compare it to the benchmark alloy AlCoCrFeNi2.1, demonstrating the effects of W-doping and increased Al content. High stacking fault probabilities, close to those measured in Au and Ag, are observed upon compression. A portion of the stacking faults are annihilated upon release to ambient pressure.