This study focuses on improving the performance of asphalt mixture at low- and high- temperature and analyzing the effect of diatomite and basalt fiber on the performance of the asphalt mixture. Based on the L₁₆(4⁵) orthogonal experimental design (OED), the content of diatomite (D) and basalt fiber (B) and the asphalt-aggregate (A) ratio were selected as contributing factors, and each contributing factor corresponded to four levels. Bulk volume density (γ_f), volume of air voids (VV), voids filled with asphalt (VFA), Marshall stability (MS) and splitting strength at −10 °C (S_b) were taken as the evaluation indexes. According to the results of the orthogonal experiment, the range analysis and variance analysis were used to study the effect of the diatomite content, basalt fiber content and asphalt-aggregate ratio on the performance of the asphalt mixture, and the grey correlation grade analysis (GCGA) was used to obtain the optimal mixing scheme. Furthermore, the performance tests were conducted to evaluate the performance improvement of asphalt mixtures with diatomite and basalt fibers, and the scanning electron microscopy (SEM) tests were carried out to analyze the mechanism of diatomite and basalt fibers in asphalt mixtures. The results revealed that the addition of diatomite and basalt fiber can significantly increase the VV of asphalt mixture, and reduce γ_f and VFA; the optimal performance of the asphalt mixture at high- and low-temperature are achieved with 14% diatomite, 0.32% basalt fibers and 5.45% asphalt-aggregate ratio. Moreover, the porous structure of diatomite and the overlapping network of basalt fibers are the main reasons for improving the performance of asphalt mixture.

To obtain the viscoelastic parameters of asphalt mixtures and analyze the effect of temperatures and modifiers on viscoelastic properties of asphalt mixtures, the creep compliances of the neat asphalt mixture (AM), compound diatomite and basalt fibers reinforced asphalt mixture (DBFAM), and styrene-butadiene-styrene modified asphalt mixture (SBSAM) were tested and calculated by the static creep tests. And the creep compliances of the three asphalt mixtures at −20 °C, −10 °C, and 0 °C are deducted by the time–temperature equivalence principle (TTEP) and Arrhenius equation. Further, the relaxation modulus of the three asphalt mixtures from −20 °C to 50 °C at 10 °C increments are calculated by the convolution integral and Simpson method. Subsequently, the Burgers model, the generalized Kelvin model, and the generalized Maxwell model are applied to analyze the viscoelastic properties of the three asphalt mixtures at different temperatures. The results show that the generalized Kelvin model and the generalized Maxwell model are superior to the Burgers model in describing the variation of viscoelastic properties of asphalt mixtures with loading time. At low temperatures, asphalt mixtures have excellent properties in resisting permanent deformation and releasing internal stress. Besides, the addition of SBS modifier and compound diatomite and basalt fibers modifier can significantly raise the viscosity η₁ and the elastic modulus E₁ of the asphalt mixture, respectively.

This paper studies the mechanical properties of porous asphalt concrete with styrene-butadiene-styrene (SBS) polymer modified bitumen as the binder, steel slag as the aggregate and crumb rubber and basalt fiber as modifiers. First, the appearance, mechanics, chemical composition and high-temperature stability of steel slag were studied by some equipment. Then, three kinds of porous asphalt concrete with SBS polymer modified bitumen as binder were produced, Namely, crumb rubber modified porous asphalt concrete (CR-PAC), basalt fiber modified porous asphalt concrete (BF-PAC), and basalt fiber and crumb rubber composite modified asphalt concrete (CM-PAC). Finally, the properties of the three kinds of modified PACs were studied through the Marshall test, freeze-thaw splitting test, low-temperature splitting test, permeability test, and creep test. The results showed that the crush value and abrasion value of steel slag are 15.1% and 13.5%, respectively; it has excellent strength and abrasion. In addition, the steel slag shows a porous structure and it provides an interface basis for a better bond with bitumen. For the three PACs, the results showed that the Marshall stability, water stability, and low-temperature crack resistance of CM-PAC are all the best Furthermore, CM-PAC has better rutting resistance than two single modified PACs, based on creep test results. The CM-PAC in this study can be used as a new type of pavement material.