The aim of this study is to analyze the properties of a series of polysaccharide composite films, such as apparent density, color, the presence of functional groups, morphology, and thermal stability, as well as the correlation between them and their antimicrobial and optical properties. Natural antioxidants such as anthocyanins (from cranberry; blueberry and pomegranate); betalains (from beetroot and pitaya); resveratrol (from grape); and thymol and carvacrol (from oregano) were added to the films. Few changes in the position and intensity of the FTIR spectra bands were observed despite the low content of extract added to the films. Due to this fact, the antioxidants were extracted and identified by spectroscopic analysis; and they were also quantified using the Folin-Denis method and a gallic acid calibration curve, which confirmed the presence of natural antioxidants in the films. According to the SEM analysis, the presence of natural antioxidants has no influence on the film morphology because the stretch marks and white points that were observed were related to starch presence. On the other hand, the TGA analysis showed that the type of extract influences the total weight loss. The overall interpretation of the results suggests that the use of natural antioxidants as additives for chitosan-starch film preparation has a prominent impact on most of the critical properties that are decisive in making them suitable for food-packing applications.

The use of Closite 15A and a triblock copolymer branch type (BP) as asphalt modifiers was studied. Modified asphalt binder was prepared by adding nanocomposites (NCs) of styrene–butadiene–styrene copolymer (BP) and Cloisite 15 A (NCMM). The NCs were obtained by means of a melt mixing technique. The morphology of the modified asphalt blends was observed via fluorescence microscopy, which revealed a good dispersion pattern of NCMM into the asphalt binder, and explains to a considerable extent, their final rheological behaviour. The modified asphalts exhibited a relatively high complex modulus compared to the unmodified asphalt and, as a consequence displayed enhanced viscoelastic properties. NCMM increased slightly both the softening point and the viscosity of the modified asphalts at elevated temperatures, and had a compatibilising effect on them, which was shown as an improvement of their storage stability.

The effect of sargassum particle size on the final properties of sargassum-modified asphalt is investigated in this article. Seaweed sargassum particles were first obtained and characterized through elemental analysis, thermogravimetric analysis (TGA), X-ray diffraction, and FTIR spectroscopy. Additionally, pure and sargassum-modified asphalt blends were evaluated through physical and rheological tests such as penetration, softening point, thermal stability, dynamic viscosity, failure temperature, and epifluorescence microscopy. Modified asphalt blends were prepared by the hot mixing technique using different proportions of sargassum particles of two maximum sizes: 500 μm and 850 μm. Incorporating 3.0 wt.% of sargassum particles under 500 μm into the asphalt increased the viscosity of the original binder by a factor of 2.5 and its complex modulus by a factor of 1.9. At the same time, its failure temperature was 11 °C higher than the reference asphalt, which implies an improved viscoelastic behavior and rutting resistance at high temperatures. The study results suggest that the particles under 500 μm were responsible for the most significant effect on the final properties of the asphalt. Moreover, the storage stability test revealed that the modified asphalt blends are stable when the sargassum particle content was kept below 3.0 wt.%. The statistical analysis of the effect of sargassum particle size and concentration on the modified asphalt properties revealed that the rheological behavior is more affected by the modifier particle size; in contrast, the conventional physical properties were more determined by its concentration. Therefore, using low proportions of fine sargassum particles is efficient for improving the physical and rheological properties of the original asphalt, which is not only positive from the asphalt modification technology point of view but also from a sustainable perspective, since seaweed sargassum has become a useless plague in many coastal regions.

An organogel shows a gel-to-gel transition corresponding to the transformation of nanotubular aggregates into plain fibers, either by heating or aging. The domains of the existence of both gels are mapped in the c – T phase diagram.