Brown-rot fungi are large fungi that can decompose the cell walls of wood; they are notable for their secretion of diverse and complex enzymes that synergistically hydrolyze natural wood cellulose molecules. Fomitopsis pinicola (F. pinicola) is a brown-rot fungus of interest for its ability to break down the cellulose in wood efficiently. In this study, through a combination of rDNA-ITS analysis and morphological observation, the wood decay pathogen infecting Korean pine (Pinus koraiensis Siebold and Zucc.) was identified. Endoglucanase (CMCase) and β-glucosidase were quantified using the DNS (3,5-Dinitrosalicylic acid) method, and the cellulase activity was optimized using a single-factor method and orthogonal test. The results revealed that the wood-decaying fungus NE1 identified was Fomitopsis pinicola with the ITS accession number OQ880566.1. The highest cellulase activity of the strain reached 116.94 U/mL under the condition of an initial pH of 6.0, lactose 15 g·L⁻¹, KH₂PO₄ 0.5 g·L⁻¹, NH₄NO₃ 15 g·L⁻¹, MgSO₄ 0.5 g·L⁻¹, VB₁ 0.4 g·L⁻¹, inoculated two 5 mm fungal cakes in 80 mL medium volume cultured 28 °C for 5 days. This laid a foundation for improving the degradation rate of cellulose and biotransformation research, as well as exploring the degradation of cellulose by brown rot fungi.

As one of the decay-resistant woods, Korean pine is widely used in the construction industry. However, even the most corrosion-resistant wood is still susceptible to decay under the right humidity and temperature conditions. In this study, Bacillus amyloliquefaciens (B. amyloliquefaciens) bacterial liquid and filter bacterial solution were prepared for the anti-corrosion treatment of Korean pine wood, aiming to improve its decay-resistant property. Through the plate confrontation test, it was discovered that B. amyloliquefaciens AW3 could significantly inhibit the growth of Fomitopsis pinicola (F. Pinicola). The results of mass loss rate, mechanical properties test, XRD, FTIR and SEM analysis showed that the preserved Korean pine wood had significant improvement in various properties compared with the decayed wood, which was manifested in the significant reduction of mass loss, improvement of mechanical properties, and increased wood cellulose diffraction peak intensity. There is no mycelium infection of F. pinicola in Korean pine wood, and the antiseptic liquid can penetrate into the wood evenly, which plays an effective antiseptic role. The B. amyloliquefaciens bacterial liquid exhibited superior preservative performance compared to the B. amyloliquefaciens filter bacterial solution. In conclusion, B. amyloliquefaciens, as an efficient and environmentally friendly biological preservative, holds broad application prospects in improving the anti-corrosion performance of Korean pine wood.