In this paper, we report the results of our investigation on the possibility of producing foam concrete by using a geopolymer system. Class C fly ash was mixed with an alkaline activator solution (a mixture of sodium silicate and NaOH), and foam was added to the geopolymeric mixture to produce lightweight concrete. The NaOH solution was prepared by dilute NaOH pellets with distilled water. The reactives were mixed to produce a homogeneous mixture, which was placed into a 50 mm mold and cured at two different curing temperatures (60 °C and room temperature), for 24 hours. After the curing process, the strengths of the samples were tested on days 1, 7, and 28. The water absorption, porosity, chemical composition, microstructure, XRD and FTIR analyses were studied. The results showed that the sample which was cured at 60 °C (LW2) produced the maximum compressive strength for all tests, (11.03 MPa, 17.59 MPa, and 18.19 MPa) for days 1, 7, and 28, respectively. Also, the water absorption and porosity of LW2 were reduced by 6.78% and 1.22% after 28 days, respectively. The SEM showed that the LW2 sample had a denser matrix than LW1. This was because LW2 was heat cured, which caused the geopolymerization rate to increase, producing a denser matrix. However for LW1, microcracks were present on the surface, which reduced the compressive strength and increased water absorption and porosity.

Fly ash–based geopolymers required heat to increase the geopolymerization process in order to obtain higher compressive strength. As such, geopolymer samples were prepared using different curing temperatures (room temperature, 50°C, 60°C, 70°C, 80°C), in which sodium silicate and NaOH were used as alkaline activators. The samples were cured for 24hours in the oven and tested on the seventh day. The result revealed that the maximum compressive strength (67.04MPa) was obtained at a temperature of 60°C. However when the geopolymers sample cured at temperature more than 60°C, the compressive strength decreased. From the FTIR spectra, the higher content of Si on sample cured at 60°C also contributed to higher compressive strength. Moreover, SEM analysis showed a denser matrix as well as less unreacted fly ash of the sample cured at 60°C compared to other temperatures

This paper investigates the effect of the solids-to-liquids (S/L) and Na₂SiO₃/NaOH ratios on the production of palm oil boiler ash (POBA) based geopolymer. Sodium silicate and sodium hydroxide (NaOH) solution were used as alkaline activator with a NaOH concentration of 14 M. The geopolymer samples were prepared with different S/L ratios (0.5, 1.0, 1.25, 1.5, and 1.75) and Na₂SiO₃/NaOH ratios (0.5, 1.0, 1.5, 2.0, 2.5, and 3.0). The main evaluation techniques in this study were compressive strength, X-Ray Diffraction (XRD), Fourier Transform Infrared Spectroscopy (FTIR), and Scanning Electron Microscope (SEM). The results showed that the maximum compressive strength (11.9 MPa) was obtained at a S/L ratio and Na₂SiO₃/NaOH ratio of 1.5 and 2.5 at seven days of testing. v

Geopolymer, produced by the reaction of fly ash with an alkaline activator (mixture of Na₂SiO₃ and NaOH solutions), is an alternative to the use of ordinary Portland cement (OPC) in the construction industry. However, there are salient parameters that affecting the compressive strength of geopolymer. In this research, the effects of various NaOH molarities, Na₂SiO₃/NaOH ratios, fly ash/alkaline activator, and curing temperature to the strength of geopolymer paste fly ash were studied. Tests were carried out on 50 x 50 x 50 mm cube geopolymer specimens. Compression tests were conducted on the seventh day of testing for all samples. The test results revealed that a 12 M NaOH solution produced the highest compressive strength for the geopolymer. The combination mass ratios of fly ash/alkaline activator and Na₂SiO₃/NaOH of 2.0 and 2.5, respectively, produced the highest compressive strength after seven days. Geopolymer samples cured at 60 °C produced compressive strength as high as 70 MPa.

There is nothing more fundamental than clean potable water for living beings next to air. On the other hand, wastewater management is cropping up as a challenging task day-by-day due to lots of new additions of novel pollutants as well as the development of infrastructures and regulations that could not maintain its pace with the burgeoning escalation of populace and urbanizations. Therefore, momentous approaches must be sought-after to reclaim fresh water from wastewaters in order to address this great societal challenge. One of the routes is to clean wastewater through treatment processes using diverse adsorbents. However, most of them are unsustainable and quite costly e.g. activated carbon adsorbents, etc. Quite recently, innovative, sustainable, durable, affordable, user and eco-benevolent Geopolymer composites have been brought into play to serve the purpose as a pretty novel subject matter since they can be manufactured by a simple process of Geopolymerization at low temperature, lower energy with mitigated carbon footprints and marvellously, exhibit outstanding properties of physical and chemical stability, ion-exchange, dielectric characteristics, etc., with a porous structure and of course lucrative too because of the incorporation of wastes with them, which is in harmony with the goal to transit from linear to circular economy, i.e., “one’s waste is the treasure for another”. For these reasons, nowadays, this ground-breaking inorganic class of amorphous alumina-silicate materials are drawing the attention of the world researchers for designing them as adsorbents for water and wastewater treatment where the chemical nature and structure of the materials have a great impact on their adsorption competence. The aim of the current most recent state-of-the-art and scientometric review is to comprehend and assess thoroughly the advancements in geo-synthesis, properties and applications of geopolymer composites designed for the elimination of hazardous contaminants viz., heavy metal ions, dyes, etc. The adsorption mechanisms and effects of various environmental conditions on adsorption efficiency are also taken into account for review of the importance of Geopolymers as most recent adsorbents to get rid of the death-defying and toxic pollutants from wastewater with a view to obtaining reclaimed potable and sparkling water for reuse offering to trim down the massive crisis of scarcity of water promoting sustainable water and wastewater treatment for greener environments. The appraisal is made on the performance estimation of Geopolymers for water and wastewater treatment along with the three-dimensional printed components are characterized for mechanical, physical and chemical attributes, permeability and Ammonium (NH₄⁺) ion removal competence of Geopolymer composites as alternative adsorbents for sequestration of an assortment of contaminants during wastewater treatment.