The aim of this study was to develop new materials with adsorbent properties that can be used for the adsorption recovery of Au(III) from aqueous solutions. To achieve this result, it is necessary to obtain inexpensive adsorbent materials in a granular form. Concomitantly, these materials must have a high adsorption capacity and selectivity. Other desired properties of these materials include a higher physical resistance, insolubility in water, and materials that can be regenerated or reused. Among the methods applied for the separation, purification, and preconcentration of platinum-group metal ions, adsorption is recognised as one of the most promising methods because of its simplicity, high efficiency, and wide availability. The studies were carried out using three supports: cellulose (CE), chitosan (Chi), and diatomea earth (Diat). These supports were functionalised by impregnation with extractants, using the ultrasound method. The extractants are environmentally friendly and relatively cheap amino acids, which contain in their structure pendant groups with nitrogen and sulphur heteroatoms (aspartic acid—Asp, l-glutamic acid—Glu, valine—Val, DL-cysteine—Cys, or serine—Ser). After preliminary testing from 75 synthesised materials, CE-Cys was chosen for the further recovery of Au(III) ions from aqueous solutions. To highlight the morphology and the functionalisation of the material, we physicochemically characterised the obtained material. Therefore, the analysis of the specific surface and porosity showed that the CE-Cys material has a specific surface of 4.6 m²/g, with a porosity of about 3 nm. The FT-IR analysis showed the presence, at a wavelength of 3340 cm⁻¹, of the specific NH bond vibration for cysteine. At the same time, pHpZc was determined to be 2.8. The kinetic, thermodynamic, and equilibrium studies showed that the pseudo-second-order kinetic model best describes the adsorption process of Au(III) ions on the CE-Cys material. A maximum adsorption capacity of 12.18 mg per gram of the adsorbent material was achieved. It was established that the CE-Cys material can be reused five times with a good recovery degree.

In this study, chitosan (Chi) functionalized with the amino acid serine (Ser) was synthesized for the adsorption-based recovery of Pt(IV) from aqueous solutions. To identify the active functional groups of the amino acid and the support material, the synthesized adsorbent was characterized using SEM, FT-IR, and EDX analyses, and its point of zero charge (pH_PZC) was determined. Static and dynamic adsorption studies were conducted to optimize process parameters. Under static conditions, equilibrium studies established the maximum Pt(IV) concentration that could be adsorbed onto Chi–Ser, as well as its maximum adsorption capacity. At pH > 4, with an S-L ratio of 0.1 g:25 mL Pt(IV) solution, a contact time of 90 min, and a temperature of 298 K, the maximum adsorption capacity reached 7.23 mg/g. The adsorption process was best described by the Sips isotherm. The Taguchi method was employed to optimize static adsorption conditions. The Clark equation most accurately modeled the adsorption process under dynamic conditions. Additionally, multiple adsorption–desorption cycles evaluated the adsorbent’s reusability.