Steel mill dust (SMD), produced by electric arc furnaces, is a highly polluting industrial waste due to its high content of metals (Zn, Fe, and Pb) and fine particle size (ca. 5.4 µm). This residue can be valorized to recover Zn using pyro and hydrometallurgical methods, with hydrometallurgy offering greater selectivity and lower energy costs. However, composition of SMD presents a challenge in identifying an optimal leaching agent. This study investigates the preferential extraction of Zn using two leaching agents, namely 150 g L⁻¹ (1.5 M) phosphoric acid (H₃PO₄) and 240 g L⁻¹ (6 M) sodium hydroxide (NaOH), in a two-stage leaching process (80 °C). Metallic Zn from the alkaline pregnant solution was recovered by electrodeposition (750 A/m², graphite anode, stainless-steel cathode) and smelting (450 °C). The samples of SMD contained 26.3% Zn, 20.1% Fe, and 0.9% Pb, in compounds such as magnetite (Fe₃O₄), zincite (ZnO), and franklinite (ZnFe₂O₄). Each leaching agent successfully attained a 99% Zn recovery, demonstrating the proposed procedure’s high efficacy. However, H₃PO₄ leached also Fe and corroded the cathode during electrodeposition, thereby restricting the final recovery of metallic Zn. NaOH demonstrated greater selectivity for Zn over Fe and Pb, producing high-purity Zn deposits on the cathode by electrodeposition and 99% metallic zinc by smelting.

Anodic sludges generated in the production of aluminum profiles pose both an environmental and economic problem due to their accumulation in municipal landfills. This study investigates their valorization as a raw material for industry through leaching and calcination processes. The solid residue was characterized both physically and chemically. In the leaching process, concentrations of NaOH (1–2.5 M) and solid percentages (10–30%) were evaluated, achieving a 93.7% recovery of aluminum as sodium aluminate with 2 M NaOH and 10% solids. In the calcination process, the sludges were treated at temperatures ranging from 200 to 1600 °C, and different particle sizes (−3 + 1 mm, −1000 + 400 μm, −400 + 200 μm). The best result from calcination was obtained at 1600 °C, producing a refractory material composed of corundum (α-Al₂O₃) and diaoyudaoite (NaAl₁₁O₁₇).