This study aimed to develop gelatin methacryloyl (GelMA)-injectable hydrogels incorporated with 58S bioactive glass/BG-doped with strontium for vital pulp therapy applications. GelMA hydrogels containing 0% (control), 5%, 10%, and 20% BG (w/v) were prepared. Their morphological and chemical properties were evaluated by scanning electron microscopy/SEM, energy dispersive spectroscopy/EDS, and Fourier transform infrared spectroscopy/FTIR (n = 3). Their swelling capacity and degradation ratio were also measured (n = 4). Cell viability (n = 8), mineralized matrix formation, cell adhesion, and spreading (n = 6) on DPSCs were evaluated. Data were analyzed using ANOVA/post hoc tests (α = 5%). SEM and EDS characterization confirmed the incorporation of BG particles into the hydrogel matrix, showing GelMA’s (C, O) and BG’s (Si, Cl, Na, Sr) chemical elements. FTIR revealed the main chemical groups of GelMA and BG, as ~1000 cm⁻¹ corresponds to Si-O and ~1440 cm⁻¹ to C-H. All the formulations were degraded by day 12, with a lower degradation ratio observed for GelMA+BG20%. Increasing the concentration of BG resulted in a lower mass swelling ratio. Biologically, all the groups were compatible with cells (p > 0.6196), and cell adhesion increased over time, irrespective of BG concentration, indicating great biocompatibility. GelMA+BG5% demonstrated a higher deposition of mineral nodules over 21 days (p < 0.0001), evidencing the osteogenic potential of hydrogels. GelMA hydrogels incorporated with BG present great cytocompatibility, support cell adhesion, and have a clinically relevant degradation profile and suitable mineralization potential, supporting their therapeutic potential as promising biomaterials for pulp capping.

This study investigated gelatin methacryloyl (GelMA) and polycaprolactone (PCL) blend scaffolds incorporating cerium oxide (CeO) nanoparticles at concentrations of 0%, 5%, and 10% w/w via electrospinning for periodontal tissue engineering. The impact of photocrosslinking on these scaffolds was evaluated by comparing crosslinked (C) and non-crosslinked (NC) versions. Methods included Fourier transform infrared spectroscopy (FTIR) for chemical analysis, scanning electron microscopy (SEM) for fiber morphology/diameters, and assessments of swelling capacity, degradation profile, and biomechanical properties. Biological evaluations with alveolar bone-derived mesenchymal stem cells (aBMSCs) and human gingival fibroblasts (HGFs) encompassed tests for cell viability, mineralized nodule deposition (MND), and collagen production (CP). Statistical analysis was performed using Kruskal–Wallis or ANOVA/post-hoc tests (α = 5%). Results indicate that C scaffolds had larger fiber diameters (~250 nm) compared with NC scaffolds (~150 nm). NC scaffolds exhibited higher swelling capacities than C scaffolds, while both types demonstrated significant mass loss (~50%) after 60 days (p < 0.05). C scaffolds containing CeO showed increased Young’s modulus and tensile strength than NC scaffolds. Cells cultured on C scaffolds with 10% CeO exhibited significantly higher metabolic activity (>400%, p < 0.05) after 7 days among all groups. Furthermore, CeO-containing scaffolds promoted enhanced MND by aBMSCs (>120%, p < 0.05) and increased CP in 5% CeO scaffolds for both variants (>180%, p < 0.05). These findings underscore the promising biomechanical properties, biodegradability, cytocompatibility, and enhanced tissue regenerative potential of CeO-loaded GelMA/PCL scaffolds for periodontal applications.

This study develops and characterizes GelMA–dopamine conjugates as novel tissue adhesives, offering an alternative to sutures. GelMA was synthesized at 5%, 10%, and 15% (w/v) with medium and high dopamine (DOPA) conjugation. Adhesives were evaluated for swelling, degradation, mechanical strength, and cytocompatibility using AlamarBlue assays and F-actin staining to assess cell viability and adhesion. Our findings indicate that DOPA conjugation significantly reduced the swelling ratio while increasing the biodegradation rate, resulting in enhanced release of free methacrylate groups over time. The mechanical properties and adhesion capabilities showed a complex relationship with DOPA substitution. Notably, the formulation containing 10% GelMA with high dopamine conjugation (HD) exhibited superior adhesion and mechanical strength. All formulations demonstrated shear-thinning behavior and recovery, making them suitable for injection and bioprinting applications. Although increased DOPA levels negatively affected crosslinking, the optimal formulation achieved a balance between adhesion and gel concentration. Rapid crosslinking was achieved within five minutes, enhancing the material’s suitability for clinical applications. In vitro cell-based assays confirmed the non-cytotoxic nature of the optimal adhesives, with metabolic activity showing significant increases over a 7-day period. These advancements support the development of improved tissue adhesives, potentially reducing reliance on sutures and enhancing wound healing outcomes.