This study underscores the potential of utilizing natural volcanic tuffs (NVTs) as supplementary cementitious materials (SCMs) in alignment with global sustainability efforts aimed at mitigating the cement industry’s negative impacts on both the economy and the environment. Experimental investigations were conducted on concrete mixtures containing 10%, 20%, 30%, 40%, and 50% NVT as partial cement replacements to assess their influence on concrete’s mechanical and microstructural properties. Based on the findings, concrete samples with 10% NVT replacements exhibited increased flexural and compressive strengths of 35.6% and 5.6%, respectively, compared with ordinary concrete after 28 days. The depth of water penetration in the concrete samples was significantly reduced by the inclusion of NVT, with a maximum reduction of 56.5%. Microstructural analysis using scanning electron microscopy (SEM) revealed enhanced densification of the concrete microstructures, attributed to the high pozzolanic activity of NVT use in cement-based composites. Analysis of variance (ANOVA) revealed statistically significant relationships between NVT content and both the compressive and flexural strengths of the concrete samples. In conclusion, substituting 10% cement with NVT not only enhances the mechanical properties of concrete but also decreases the energy demand for cement production and reduces carbon dioxide (CO₂) emissions, thus contributing to more sustainable construction practices.

This study investigates the influence of basalt fiber on the rheological, mechanical, and microstructural properties of sustainable self-compacting concrete (SCC) incorporating fly ash and microsilica as supplementary cementitious materials (SCMs). Various SCC mixes were prepared, incorporating five different volume fractions of basalt fiber (0.05%, 0.1%, 0.5%, 1%, and 1.5%), along with a control mix. The rheological properties of fresh SCC were evaluated using slump flow and V-funnel flow tests. Subsequently, the mechanical properties, including compressive strength, splitting tensile strength, and flexural strength, were measured after 28 days of curing. Additionally, microstructural analysis was conducted using scanning electron microscopy (SEM) on fractured specimen surfaces. The results indicated that the inclusion of basalt fiber adversely affected the flowability of fresh SCC mixes, with increased fiber volume. However, the hardened concrete exhibited significant improvements in mechanical properties with the addition of basalt fibers. The optimal performance was observed in the SCC70-85/0.10 mix specimens, which demonstrated a 69.90% improvement in flexural strength and a 23.47% increase in splitting tensile strength compared with the control specimen. SEM analysis further revealed enhanced microstructural density in the concrete matrix containing basalt fiber. A two-factor analysis of variance (ANOVA) with repetitions was conducted to evaluate the effects of varying basalt fiber concentrations on the compressive, flexural, and tensile strengths of SCC mixes. The ANOVA results indicated significant effects for both SCC grade and basalt fiber concentration, demonstrating that each factor independently affected the compressive, tensile, and flexural strengths of SCC. These findings suggest that the incorporation of basalt fibers holds promise for extending building lifespans and enhancing concrete quality, representing a valuable advancement in structural engineering applications.

This experimental study evaluated the performance of modified asphalt mixtures prepared by incorporating 2%, 4%, and 6% linear low-density polyethylene (LLDPE) by weight of asphalt binder through a series of tests. The microstructural analyses using scanning electron microscopy (SEM) were conducted on asphalt samples to assess the engineering properties of the asphalt mixes. Finally, ANOVA statistical analysis has been employed to determine the statistical significance of the differences in all tests’ means. Based on laboratory findings, the Marshall stability test result showed that the modified asphalt mixes up to 4% LLDPE had enhanced performance by 12.7% compared to the control mix. A significant decrease (up to 31.3%) in binder penetration was demonstrated due to the incorporation of LLDPE into the asphalt mix. The softening point of the LLDPE–asphalt mixes was increased by up to 17.6%. It was also demonstrated that the incorporation of such LLDPE dosages maintains the flow limits within the specified range; however, the flow of the asphalt mix with 4% LLDPE was 3.17 mm which is the nearest to the average value of the upper and lower acceptable limits. The air voids of mixes with LLDPE content more than 4% by was decreased to less than 4% which is not recommended in high-temperature climates to control mixture bleeding. Microscopic analysis revealed an improvement in the densification of asphalt microstructures, attributed to the LLDPE particles significantly changing the rheology and viscosity of the base mixture and making the hot asphalt mixture more homogeneous. Based on the physical and rheological properties investigated in this study, it could be concluded that 4% LLDPE produces the best performance in asphalt mixtures. Overall, the ANOVA analysis demonstrated that the incorporation of LLDPE into asphalt mixes has a significant impact on all of their properties.

This study evaluates the mechanical performance and failure characteristics of concrete reinforced with corn fibers as a sustainable natural additive. Corn fibers were incorporated at 0.25%, 0.5%, and 1.5% by weight of cement, with a control mix used for comparison. All mixtures were prepared at a constant water–cement ratio and adjusted for workability using a high-range water-reducing admixture. Results indicate that fiber dosage significantly influences strength and fracture behavior. The 0.5% fiber content yielded the best performance, improving compressive and flexural strength by approximately 36% and 24%, respectively, and promoting enhanced crack control and ductile response. In contrast, excessive fiber addition reduced performance due to fiber clustering and higher pore content. This study confirms that properly proportioned corn fibers can enhance concrete properties while encouraging sustainable construction through the reuse of agricultural waste. SEM further indicated a denser and more refined microstructure in the fiber-modified matrix. An ANOVA analysis and Tukey’s HSD post hoc test were performed to assess the influence of corn fiber content on the compressive, flexural, and tensile strengths of concrete mixtures, revealing statistically significant effects. Overall, the results highlight the potential of corn fiber reinforcement to improve the short-term mechanical performance of concrete mixes.