One of the biggest challenges in the construction industry in recent times is the mitigation of the environmental impact of this sector, the reduction in dependence on primary raw materials, and the reduction in CO₂ production while maintaining functional properties. Alkaline activation of a number of waste products represents a promising way to achieve the above-mentioned goals, but the availability of a number of waste products changes over time, especially in Europe. While freshwater sediments were in the past widely utilized as an agricultural fertilizer, recent precautions have significantly decreased such application, and thus new destinations must be delivered. To explore the potential of freshwater sediments, select samples from various locations were subjected to detailed characterization to verify the applicability of the material for alkali activation. As recognized, the selected sediments contain a substantial volume of desired mineralogical compounds that can serve, after 900 °C curing, as suitable precursors. Such samples have consequently activated the mixture of alkaline activators to obtain dense structures and were subjected to detailed investigation aimed at understanding the mechanical parameters. The obtained mechanical results ranging between 14.9 MPa and 36.8 MPa reveal the engineering potential of sediments for valorization through alkali activation and outline new research challenges in this area.

Alkali-activated materials (AAMs) offer a promising low-carbon alternative to Portland cement, but their development has been dominated by fly ash and slag, whose availability is increasingly limited. This research explores waste brick powder (WBP) and metakaolin residue (RN), two abundant yet underutilized by-products, as blended precursors for sustainable binder design. The novelty lies in demonstrating how complementary chemistry between crystalline-rich WBP and amorphous RN can overcome the drawbacks of single-precursor systems while valorizing construction and industrial residues. Pastes were prepared with varying WBP/RN ratios, activated with alkaline solutions, and characterized by Vicat setting tests, isothermal calorimetry, XRD with Rietveld refinement, MIP, SEM, and mechanical testing. Carbon footprint analysis was performed to evaluate environmental performance. Results show that WBP reacts very rapidly, causing flash setting and limited long-term strength, whereas the incorporation of 30–50% RN extends setting times, sustains dissolution, and increases amorphous gel formation. These changes refine the formed reaction products, leading to compressive strengths up to 39 MPa and flexural strengths of 8 MPa at 90 days. The carbon footprint of all blends remained 392–408 kg CO₂e/m³, thus providing about a 60% improvement compared to conventional Portland cement paste. The study establishes clear design rules for waste-derived blended precursors and highlights their potential as circular, low-carbon binders.