The response characteristics of carbyne-enriched surface-acoustic-wave (SAW)-based gas sensors utilizing meander and rectangular microheater topologies were investigated to assess their desorption and recovery properties. Comparative analysis of contact resistance and interface capacitance before and after heating revealed minimal deviation in contact resistance, signifying strong thermal stability in the carbyne-enriched layer. However, the interface capacitance varied with the microheater size. Our analysis reveals that a small meander microheater configuration (line width: 300 µm) facilitates efficient sensor recovery at ethanol concentration measurements in the range of 180–680 ppm, maintaining a low deviation in time delay across different concentrations (~2.3%), resulting in a narrow hysteresis and linear sensor response. Conversely, the large meander microheater (line width: 450 µm) and rectangular dense microheater induce irreversible changes in the sensing structure, leading to a widened hysteresis at higher concentrations and increased power consumption. Recovery patterns display substantial deviations from initial values at different concentration levels. Higher concentrations exhibit broader hysteresis, while lower concentrations show narrower hysteresis loops, compared to the small meander microheater. The study offers insights into desorption rates, power consumption variations, and recovery behaviors related to different microheater configurations. It demonstrates the importance of microheater topology selection in tailoring recovery properties and response characteristics, contributing to the advancement of carbyne-based sensor technology.

This study presents the development and characterization of electrospun nanofibers composed of polyvinyl alcohol (PVA) and natural beeswax (BW). A stable emulsion containing 9 wt% PVA and 5 wt% BW was successfully formulated and electrospun. The effects of beeswax incorporation on solution properties-viscosity, conductivity, and surface tension—were systematically evaluated. Electrospinning was performed at 30 kV and a working distance of 14.5 cm, yielding nanofibers with diameters between 125 and 425 nm. Scanning electron microscopy (SEM) revealed increased surface roughness and diameter variability in PVA/BW fibers compared to the PVA. Fourier transform infrared spectroscopy (FTIR) confirmed physical incorporation of BW without evidence of chemical bonding. Thermogravimetric and differential scanning calorimetry analyses (TGA/DSC) demonstrated altered behavior and an expanded profile of temperature transitions due to the waxy components. The solubility test of the nanofiber mat in saline indicated that BW slows dissolution and improves the structural integrity of the fibers. This study demonstrates, for the first time, the incorporation of beeswax into electrospun PVA nanofibers with improved structural and thermal properties, indicating potential for further exploration in biomedical material design.

This study developed a novel 3D-printable poly(vinylidene fluoride) (PVDF)-based nanocomposite incorporating 6 wt% graphene nanoplatelets (GNPs) with programmable characteristics for resistive heating applications. The results highlighted the significant effect of a controlled printing direction (longitudinal, diagonal, and transverse) on the electrical, thermal, Joule heating, and thermo-resistive properties of the printed structures. The 6 wt% GNP/PVDF nanocomposite exhibited a high electrical conductivity of 112 S·m⁻¹ when printed in a longitudinal direction, which decreased significantly in other directions. The Joule heating tests confirmed the material’s efficiency in resistive heating, with the maximum temperature reaching up to 65 °C under an applied low voltage of 2 V at a raster angle of printing of 0°, while the heating T_max decreased stepwise with 10 °C at the 45° and the 90° printing directions. The repeatability of the Joule heating performance was verified through multiple heating and cooling cycles, demonstrating consistent maximum temperatures across several tests. The effect of sample thickness, controlled by the number of printed layers, was investigated, and the results underscore the advantages of programmable 3D printing orientation in thin layers for enhanced thermal stability, tailored electrical conductivity, and efficient Joule heating capabilities of 6 wt% GNP/PVDF composites, positioning them as promising candidates for next-generation 3D-printed electronic devices and self-heating applications.

A self-sustainable power supply function with flexibility, mechanical stability, and lightweight quality is among the required properties for pressure sensors and other low-power-consuming electronics and wearable devices. In this work, a poly(vinylidene fluoride-trifluoroethylene)/multi-walled carbon nanotube (P(VDF–TrFE)/MWCNT) composite was prepared to increase the electrical conductivity of the piezoelectric polymer and, thus, improve its electrical power generation capabilities. It was soaked by injection molding through an anodic aluminum oxide membrane to align vertically with the dipoles and exclude the possibility of dipole moment quenching. The composite membrane-type element exhibited an excellent piezoelectric coefficient d₃₃ of 42 pC/N at a frequency of 50 Hz and an applied force intensity of 10 N, while the sensitivity was ~375 µV/g, which is favorable for self-powered pressure sensor application. The resulting composite element was utilized to generate the piezoelectric signal and to investigate the dependence of the electromechanical behavior on the surface roughness, morphology, and contact interface resistance.

Nanowires of ferroelectric potassium niobate were grown by filling nanoporous templates of both side opened anodic aluminum oxide (AAO) through radiofrequency vacuum sputtering for multisensor fabrication. The precise geometrical ordering of the AAO matrix led to well defined single axis oriented wire-shaped material inside the pores. The sensing abilities of the samples were studied and analyzed in terms of piezoelectric and pyroelectric response and the results were compared for different length of the nanopores (nanotubes)—1.3 µm, 6.3 µm and 10 µm. Based on scanning electronic microscopy, elemental and microstructural analyses, as well as electrical measurements at bending and heating, the overall sensing performance of the devices was estimated. It was found that the produced membrane type elements, consisting potassium niobate grown in AAO template exhibited excellent piezoelectric response due to the increased specific area as compared to non-structured films, and could be further enhanced with the nanowires length. The piezoelectric voltage increased linearly with 16 mV per micrometer of nanowire’s length. At the same time the pyroelectric voltage was found to be less sensitive to the nanowires length, changing its value at 400 nV/µm. This paper provides a simple and low-cost approach for nanostructuring ferroelectric oxides with multisensing application, and serves as a base for further optimization of template based nanostructured devices.

Two layer system from sputtered indium tin oxide (ITO) and gallium doped zinc oxide (Ga:ZnO, GZO) were studied for transparency in the visible electromagnetic range, reflectivity in the near infrared range, conductivity and valent band for a solar cells with quantum dots. The bi-layer coatings produced at optimized oxygen partial pressure, films thickness and surface roughness exhibit improved optical properties without worsening the electrical parameters, even if additional oxygen introduction during the reactive sputtering of the GZO. With an average optical transmittance of 91.3% in the visible range, average reflection and resistivity lower than 0.4 × 10⁻² Ω.cm, these coatings are suitable for top electrode in the solar cells. The obtained results reveal that multilayered stacks of transparent ITO/Ga-doped ZnO coatings possess relatively low surface roughness (7–9 nm) and appropriate refractive index. The additional oxidation of GZO films induces modification of the film thickness and respectively of their optical performances.