A through-mask electrochemical micromachining process with a foamed cathode (foamed-cathode through-mask electrochemical micromachining (TMEMM)) has recently been proposed involving micro-scale surface microstructures with a high geometric consistency that are fabricated on the curved-surface workpiece. In this paper, to make the foamed-cathode TMEMM process more cost-efficient in the applications, significant modifications are made to this process and an upgraded version of the foamed-cathode TMEMM process is developed. In this modified process, the sandwich-like unit (including the foamed cathode, mask, and workpiece) is closely assembled by the magnetic field force instead of the conventionally-used mechanical force and is kept moving up-and-down inside the electrolyte, avoiding the use of the traditional pump-driven circulation for the electrode process. Experiments are carried out to evaluate the machining effect of this modified TMEMM for fabricating micro-dimples. The research results verify that this modified TMEMM process can produce highly uniform micro-dimples whose minimum CV (coefficient of variation) values in depth and in diameter are 5.4% and 1.9%, respectively, with smooth surfaces of the minimum Ra being 0.21–0.35 µm. These values are smaller than those previously reported. This results in the positive effects on the mass transfer driven by magnetohydrodynamic convection induced by the magnetic field within the interelectrode and the foamed electrode.

A flake is a crack that is induced by trapped hydrogen within steel. To study its formation mechanism, previous studies mostly focused on the formation process and magnitude of hydrogen pressure in hydrogen traps such as cavities and cracks. However, according to recent studies, the hydrogen leads to the decline of the mechanical properties of steel, which is known as hydrogen embrittlement, is another reason for flake formation. In addition, the phenomenon of stress induced hydrogen uphill diffusion should not be neglected. All of the three behaviors are at work simultaneously. In order to further explore the formation mechanism of flakes in steel, the process of flake initiation and growth were studied with the following three coupling factors: trap hydrogen pressure, hydrogen embrittlement, and stress induced hydrogen re-distribution. The analysis model was established using the finite element method, and a crack whose radius is 0.5 mm was set in its center. The cohesive method and Bilinear Traction Separate Law (BTSL) were used to address the coupling effect. The results show that trap hydrogen pressure is the main driving force for flake formation. After the high hydrogen pressure was generated around the trap, a stress field formed. In addition, the trap is the center of stress concentration. Then, hydrogen is concentrated in a distribution around this trap, and most of the steel mechanical properties are reduced. The trap size is a key factor for defining the critical hydrogen content for flake formation and propagation. However, when the trap size exceeds the specified value, the critical hydrogen content does not change any more. As for the crack whose radius is 0.5 mm, the critical hydrogen content of Cr5VMo steel is 2.2 ppm, which is much closer to the maximum safe hydrogen concentration of 2.0 ppm used in China. The work presented in this article increases our understanding of flake formation and propagation mechanisms in steel.

A seamless thin-walled hollow metallic cylinder with array of micro-perforations is one of the key components for some products. Normally, these micro-perforations are formed by removing material from the given metallic hollow cylinder (pipe or tube) one by one or row by row. To efficiently and flexibly manufacture such a highly perforated hollow cylinder, this paper proposed a hybrid technique combining extrusion moulding process and electroforming process. In the hybrid technique, the extrusion moulding process was used to create polymer extrusion patterns on the outside surface of the given stainless steel (SS) pipe, and then the electroforming process was carried out using the SS pipe as the mandrel. The formation of the polymer extrusion patterns was simulated and extruding molding experiments were carried out to examine the feasibility of the various mandrels. Electroforming experiments were implemented to verify the achievement of the seamless perforated thin-walled hollow cylinder. It was found that five different types of polymer extrusion pattern were able to be obtained on the same extruding pipe just by adjusting some extruding conditions and parameters, and correspondingly four types of perforated hollow cylinder with different tapered orifices are produced after the electroforming process. The obtainable perforations are: perforation with double conic-orifices, perforation with hemispheric orifice and conic orifice, unidirectionally tapered perforation, and straight-walled perforation. The geometric profile of the extrusion patterns is highly dependent on the processing conditions and parameters. The proposed hybrid process represents a promising alternative process to fabricate seamless thin-walled perforated hollow metallic cylinder efficiently, flexibly, and with low cost.

GH4169 alloy/Inconel 718 is extensively utilized in aerospace manufacturing due to its excellent high temperature mechanical properties. Micro-structuring on the workpiece surface can enhance its properties further. Through-mask electrochemical micromachining (TMEMM) is a promising and potential processing method for nickel-based superalloys. It can effectively solve the problem that traditional processing methods are difficult to achieve large-scale, high-precision and efficiency processing of surface micro-structure. This study explores the feasibility of electrochemical machining (ECM) for GH4169 using roll-print mask electrochemical machining with a linear cathode. Electrochemical dissolution characteristics of GH4169 alloy were analyzed in various electrolyte solutions and concentrations. Key parameters including cathode sizes, applied voltage and corrosion time were studied in the roll-print mask electrochemical machining. A qualitative model for micro-pit formation on GH4169 was established. Optimal parameters were determined through experiments: 300 μm mask hole and cathode size, 10 wt% NaNO₃ electrolyte, 12 V voltage, 6 s corrosion time. The results demonstrate that the micro-pits with a diameter of 402.3 μm, depth of 92.8 μm and etch factor (EF) of 1.81 show an excellent profile and localization.

In order to improve the thickness uniformity of the electroformed metal layer and components, a new electroforming technique is proposed—wire-anode scanning electroforming (WAS-EF). WAS-EF uses an ultrafine inert anode so that the interelectrode voltage/current is superimposed upon a very narrow ribbon-shaped area at the cathode, thus ensuring better localization of the electric field. The anode of WAS-EF is in constant motion, which reduces the effect of the current edge effect. The stirring paddle of WAS-EF can affect the fluid flow in the microstructure, and improve the mass transfer effect inside the structure. The simulation results show that, when the depth-to-width ratio decreases from 1 to 0.23, the depth of fluid flow in the microstructure can increase from 30% to 100%. Experimental results show that. Compared with the traditional electroforming method, the single metal feature and arrayed metal components prepared by WAS-EF are respectively improved by 15.5% and 11.4%.

High aspect ratio (HAR) ultrafine tapered holes (diameter ≤5 μm; AR ≥5) are the most important elements for some high-tech perforated metallic products, but they are very difficult to manufacture. Therefore, this paper proposes a nontraditional over-growth electroforming process. The formation mechanism of the HAR ultrafine tapered holes is investigated, and the factors controlling the geometric shape evolution are analyzed numerically. It was found that the geometric shape and dimensions of the holes are highly dependent on the diameter and thickness of the photoresist film patterns, but are hardly affected by the spacing between two neighboring patterns; the achievable diameter for a given hole depth becomes small with the increasing pattern diameter, but it becomes big with the increasing pattern thickness. These correlations can be well interpreted by the established two empirical equations that characterize the relationship between the minimum orifice of the tapered hole and the structural parameters of the photoresist film patterns previously formed on the substrate. Application of the fabricated 1500 tapered holes with 3-μm diameter and 17-AR as the nozzles of the medical precision nebulizer is also examined. The studies show that the over-growth electroforming process is highly applicable in fabricating the perforated metallic plate with HAR ultrafine tapered holes.