A through-mask electrochemical micromachining process with a foamed cathode (foamed-cathode through-mask electrochemical micromachining (TMEMM)) has recently been proposed involving micro-scale surface microstructures with a high geometric consistency that are fabricated on the curved-surface workpiece. In this paper, to make the foamed-cathode TMEMM process more cost-efficient in the applications, significant modifications are made to this process and an upgraded version of the foamed-cathode TMEMM process is developed. In this modified process, the sandwich-like unit (including the foamed cathode, mask, and workpiece) is closely assembled by the magnetic field force instead of the conventionally-used mechanical force and is kept moving up-and-down inside the electrolyte, avoiding the use of the traditional pump-driven circulation for the electrode process. Experiments are carried out to evaluate the machining effect of this modified TMEMM for fabricating micro-dimples. The research results verify that this modified TMEMM process can produce highly uniform micro-dimples whose minimum CV (coefficient of variation) values in depth and in diameter are 5.4% and 1.9%, respectively, with smooth surfaces of the minimum Ra being 0.21–0.35 µm. These values are smaller than those previously reported. This results in the positive effects on the mass transfer driven by magnetohydrodynamic convection induced by the magnetic field within the interelectrode and the foamed electrode.

Titanium alloys have many excellent characteristics, and they are widely used in aerospace, biomedicine, and precision engineering. Meanwhile, titanium alloys are difficult to machine and passivate readily. Electrochemical grinding (ECG) is an ideal technology for the efficient–precise machining of titanium alloys. In the ECG process of titanium alloys, the common approach of applying high voltage and active electrolytes to achieve high efficiency of material removal will lead to serious stray corrosion, and the time utilized for the subsequent finishing will be extended greatly. Therefore, the application of ECG in the field of high efficiency and precision machining of titanium alloys is limited. In order to address the aforementioned issues, the present study proposed an efficient–precise continuous ECG (E-P-C-ECG) process for Ti–6Al–4V applying high-pulsed voltage with an optimized duty cycle and low DC voltage in the efficient ECG stage and precise ECG stage, respectively, without changing the grinding wheel. According to the result of the passivation properties tests, the ideal electrolyte was selected. Optimization of the process parameters was implemented experimentally to improve the processing efficiency and precision of ECG of Ti–6Al–4V. Utilizing the process advantages of the proposed process, a thin-walled structure of Ti–6Al–4V was obtained with high efficiency and precision. Compared to the conventional mechanical grinding process, the compressive residual stress of the machined surface and the processing time were reduced by 90.5% and 63.3% respectively, and both the surface roughness and tool wear were obviously improved.

Titanium alloys are widely used in aerospace and biomedicine because of their excellent mechanical characteristics, but these properties also make such alloys difficult to cut. Jet electrochemical micromilling (JEMM) is based on the principle of electrochemical anodic dissolution; it has some inherent advantages for the machining of titanium alloy microstructures. However, titanium oxidizes readily, forming an oxide film that impedes a uniform dissolution during electrochemical machining. Therefore, a high voltage and an aqueous NaCl electrolyte are usually used to break the oxide film, which can lead to severe stray corrosion. To overcome this problem, the present study investigated the JEMM of Ti-6Al-4V using a NaCl–ethylene glycol (NaCl-EG) electrolyte. Electrochemical testing showed that Ti-6Al-4V exhibits a better corrosion resistance in the NaCl-EG electrolyte compared to the aqueous NaCl electrolyte, thereby reducing stray corrosion. The localization and surface quality of the grooves were enhanced significantly when using JEMM with a NaCl-EG electrolyte. A multiple-pass strategy was adopted during JEMM to improve the aspect ratio, and the effects of the feed depth and number of passes on the multiple-pass machining performance were investigated. Ultimately, a square annular microstructure with a high geometric dimensional consistency and a smooth surface was obtained via JEMM with multiple passes using the optimal parameters.

Jet electrochemical micromilling (JEMM) exhibits significant potential for high-efficiency and high-quality machining of titanium alloy microstructures. However, during the JEMM process, the machined surface of the workpiece inevitably experiences stray current attacks at low current levels. Due to the formation of a dense passive film on the surface of the titanium alloy under electrochemical action, stray corrosion occurs on the machined surface. Hence, the electrochemical dissolution behavior of titanium alloys at low current densities directly impacts both machining efficiency and quality. This study first analyzed the effects of electrolyte composition and current density on the transpassive potential, breakdown of the passive film, current efficiency, and the dissolved surface on Ti-6Al-4V. The transpassive potential and electrochemical impedance of Ti-6Al-4V were found to be lower in NaCl solution than in NaNO₃ solution. In addition, lower current densities enabled higher current efficiency and resulted in a more uniform and flat dissolution surface. Subsequent experiments used these two solutions for JEMM of complex-shaped microstructures on Ti-6Al-4V. The findings demonstrated that, compared to the NaNO₃ solution, the use of NaCl solution increases the material removal rate by approximately 30%, enhances the aspect ratio by about 26%, and reduces surface roughness by roughly 58%. This indicates that employing NaCl solution can lead to superior machining efficiency and quality.

Difficult-to-cut titanium matrix composites (TiB+TiC)/Ti6Al4V have extensive application prospects in the fields of biomedical and aerospace metal microcomponents due to their excellent mechanical properties. Jet electrochemical micromilling (JEMM) technology is an ideal method for machining microstructures that leverages the principle of electrochemical anodic dissolution. However, the matrix Ti6Al4V is susceptible to passivation during electrochemical milling, and the inclusion of high-strength TiB whiskers and TiC particles as reinforcing phases further increases the machining difficulty of (TiB+TiC)/Ti6Al4V. In this study, a novel approach using NaCl+NaNO3 mixed electrolyte for the JEMM of (TiB+TiC)/Ti6Al4V was adopted. Electrochemical behaviors were measured in NaCl and NaCl+NaNO3 electrolytes. In the mixed electrolyte, a higher transpassive potential was required to break down the passive film, which led to better corrosion resistance of (TiB+TiC)/Ti6Al4V, and the exposed reinforcing phases on the dissolved surface were significantly reduced. The results of the JEMM machining indicate that, compared to NaCl electrolyte, using mixed electrolyte effectively mitigates stray corrosion at the edges of micro-grooves and markedly improves the uniformity of both groove depth and width dimensions. Additionally, the surface quality was noticeably improved, with a reduction in Ra from 2.84 μm to 1.03 μm and in Rq from 3.41 μm to 1.40 μm.

A seamless thin-walled hollow metallic cylinder with array of micro-perforations is one of the key components for some products. Normally, these micro-perforations are formed by removing material from the given metallic hollow cylinder (pipe or tube) one by one or row by row. To efficiently and flexibly manufacture such a highly perforated hollow cylinder, this paper proposed a hybrid technique combining extrusion moulding process and electroforming process. In the hybrid technique, the extrusion moulding process was used to create polymer extrusion patterns on the outside surface of the given stainless steel (SS) pipe, and then the electroforming process was carried out using the SS pipe as the mandrel. The formation of the polymer extrusion patterns was simulated and extruding molding experiments were carried out to examine the feasibility of the various mandrels. Electroforming experiments were implemented to verify the achievement of the seamless perforated thin-walled hollow cylinder. It was found that five different types of polymer extrusion pattern were able to be obtained on the same extruding pipe just by adjusting some extruding conditions and parameters, and correspondingly four types of perforated hollow cylinder with different tapered orifices are produced after the electroforming process. The obtainable perforations are: perforation with double conic-orifices, perforation with hemispheric orifice and conic orifice, unidirectionally tapered perforation, and straight-walled perforation. The geometric profile of the extrusion patterns is highly dependent on the processing conditions and parameters. The proposed hybrid process represents a promising alternative process to fabricate seamless thin-walled perforated hollow metallic cylinder efficiently, flexibly, and with low cost.