Protection against microbiologically influenced corrosion (MIC) is critical for materials used in aquatic environments, as MIC accelerates material degradation and leads to faster structural failure. Copper (Cu) has the potential to substantially improve the MIC resistance in alloys. In this study, high-entropy alloy (HEA) coatings containing Cu were deposited using DC (Direct Current) magnetron sputtering to enhance the corrosion resistance and mechanical properties of various substrates. Two CuCrFeMnNi HEA compositions in the form of bulk alloys and PVD (Physical Vapor Deposition) coatings, with 5% and 10% Cu, were analyzed for their microstructural, mechanical, and anticorrosive characteristics. Deposition parameters were varied to select the optimal values. Microstructural evaluations using SEM-EDS (scanning electron microscopy and energy dispersive X-ray spectroscopy), XRD (X-ray diffraction), and AFM (atomic force microscopy) revealed uniform, dense coatings with good adhesion composed of dendritic and interdendritic BCC (body-centered cubic) and FCC (face centered cubic) structures, respectively. Microhardness tests indicated improved mechanical properties for the samples coated with developed HEAs. The coatings exhibited improved corrosion resistance in NaCl solution, the 10% Cu composition displaying the highest polarization resistance and lowest corrosion rate. These findings suggest that Cu-containing HEA coatings are promising candidates for applications requiring enhanced corrosion protection.

Chromium nitride thin films are known for their good mechanical properties. We present the characteristics of ultrathin chromium nitride films under 400 nm thickness deposited on silicon substrates by direct current and high-power impulse magnetron sputtering techniques. The methods of investigation of the CrN films were scanning electron microscopy, atomic force microscopy, and nanoindentation. Qualitative and quantitative analyses were performed using AFM and SEM images by fractal dimension, surface roughness and gray-level co-occurrence matrix methods. Our results show that using magnetron techniques, ultrathin CrN films with excellent mechanical properties were obtained, characterized by values of Young’s modulus between 140 GPa and 250 GPa for the samples obtained using high-power impulse magneton sputtering (HiPIMS) and between 240 GPa and 370 GPa for the samples obtained using direct current sputtering (DC). Stiffness measurements also reveal the excellent mechanical properties of the investigated samples, where the samples obtained using HiPIMS sputtering had stiffness values between 125 N/m and 132 N/m and the samples obtained using DC sputtering had stiffness values between 110 N/m and 119 N/m.