Protective SiO₂ coating deposited to iron microparticles is highly demanded both for the chemical and magnetic performance of the latter. Hydrolysis of tetraethoxysilane is the crucial method for SiO₂ deposition from a solution. The capabilities of this technique have not been thoroughly studied yet. Here, two factors were tested to affect the chemical composition and the thickness of the SiO₂ shell. It was found that an increase in the hydrolysis reaction time thickened the SiO₂ shell from 100 to 200 nm. Moreover, a decrease in the acidity of the reaction mixture not only thickened the shell but also varied the chemical composition from SiO_3.0 to SiO_8.6. The thickness and composition of the dielectric layer were studied by scanning electron microscopy and energy-dispersive X-ray analysis. Microwave permeability and permittivity of the SiO₂-coated iron particles mixed with a paraffin wax matrix were measured by the coaxial line technique. An increase in thickness of the silica layer decreased the real quasi-static permittivity. The changes observed were shown to agree with the Maxwell Garnett effective medium theory. The new method developed to fine-tune the chemical properties of the protective SiO₂ shell may be helpful for new magnetic biosensor designs as it allows for biocompatibility adjustment.

Changes in the microwave permeability of permalloy films with an increase in the film thickness are studied. Measurement data on the evolution of microwave permeability with film thickness are analyzed in the framework of a model for the film with a regular stripe domain structure and out-of-plane magnetic anisotropy. A correlation between the microwave magnetic properties and magnetic structure of permalloy films is established. It is demonstrated that the observed decrease in the ferromagnetic resonance frequency and the static permeability with a growth in the film thickness can ascribed to the appearance of perpendicular anisotropy and the formation of a stripe domain structure. The calculated dependences of the ferromagnetic resonance frequency and static permeability on the film thickness are in reasonable agreement with the measurement results. Based on the analysis of these dependences, the domain width in the permalloy films is estimated. It is found that for thick permalloy films, the domain width is of the order of the film thickness. The results obtained may be useful for high-frequency applications of soft magnetic films.

Hollow ferromagnetic powders of iron were obtained by means of ultrasonic spray pyrolysis. A variation in the conditions of the synthesis allows for the adjustment of the mean size of the hollow iron particles. Iron powders were obtained by this technique, starting from the aqueous solution of iron nitrate of two different concentrations: 10 and 20 wt.%. This was followed by a reduction in hydrogen. An increase in the concentration of the solution increased the mean particle size from 0.6 to 1.0 microns and widened particle size distribution, but still produced hollow particles. Larger particles appeared problematic for the reduction, although admixture of iron oxides did not decrease the microwave permeability of the material. The paraffin wax-based composites filled with obtained powders demonstrated broadband magnetic loss with a complex structure for lesser particles, and single-peak absorption for particles of 1 micron. Potential applications are 5G technology, electromagnetic compatibility designs, and magnetic field sensing.

A resonant RLC circuit with a magnetic core has been investigated experimentally and theoretically as a promising metamaterial cell design. Laminates of multilayer ferromagnetic films serve as a magnetic core. The ferromagnetic resonance frequency of the bare laminate core is above 1 GHz. An intensive magnetic absorption peak is obtainable at lower frequencies due to a resonant wire coiled around the core. Such magnetic metamaterials seem promising for applications that require high magnetic loss at frequencies of hundreds of megahertz. This paper focuses on efficient approaches to adjusting the location of magnetic loss peak in magnetic metamaterials. High-frequency permeability of the metamaterial samples has been measured in a rectangular waveguide. It is shown that by varying the geometry, structure, and composition of the measured metamaterial samples, the magnetic spectra can be radically changed. Excitation of electromagnetic resonance in the ferromagnetic core with the resonant wire is discussed within the frame of the quasi-static approximation.

The relationship between the chemical purity of one-size particles and microwave properties in ferromagnetic materials is not clearly studied. Ferromagnetic nanostructured iron powders were synthesized from iron nitrate solution using ultrasonic spray-pyrolysis and then reduced in H₂ flow at 350, 400, 450, and 500 °C. A rise in the concentration of solutions of a precursor from 10 to 20 wt. % led to an increase in mean particle size. The interrelationship was studied between chemical composition and the microwave dispersion of the powders obtained. An increase in the temperature of reduction changes the chemical composition and increases the amplitude of complex microwave permeability, which was studied using solid-state physics methods (XRD, STA, SEM, and VNA). It was found that annealing at 400 °C is the optimal treatment that allows the production of iron powders, consisting of about 90% of α-Fe phase, possessing a particle surface with low roughness and porosity, and demonstrating intense microwave absorption. Annealing at a higher temperature (500 °C) causes an even higher increase in permeability but leads to the destruction of nanostructured spheres into smaller particles due to grain growth. This destruction causes an abrupt increase in permittivity and therefore significantly reduces potential applications of the product. The insight into chemical–magnetic relationships of these materials enhances the data for design applications in magnetic field sensing.

Microwave permeability of amorphous Co₆₇Fe₇B₂₆ films deposited on a flexible substrate was studied in a wide range of film thicknesses up to 1.40 μm. Microwave permeability measurements were carried out using the coaxial technique in the frequency range from 0.1 to 10 GHz. It was found that both the static permeability and the ferromagnetic resonance frequency depend weakly on the film thickness. Analysis of the microwave data showed that the studied films possess in-plane magnetic anisotropy. The influence of the skin effect on the frequency dependence of the microwave permeability was modeled using an analytical approach. It was demonstrated that the decrease in the peak of the imaginary part of the microwave permeability with film thickness growth is related to the skin effect. The results obtained may be useful for microwave applications of soft magnetic CoFeB films.