A study is performed of using a transverse electromagnetic wave approximation to measure magnetic permeability in symmetric and asymmetric strip transmissi

Microwave permeability of amorphous Co₆₇Fe₇B₂₆ films deposited on a flexible substrate was studied in a wide range of film thicknesses up to 1.40 μm. Microwave permeability measurements were carried out using the coaxial technique in the frequency range from 0.1 to 10 GHz. It was found that both the static permeability and the ferromagnetic resonance frequency depend weakly on the film thickness. Analysis of the microwave data showed that the studied films possess in-plane magnetic anisotropy. The influence of the skin effect on the frequency dependence of the microwave permeability was modeled using an analytical approach. It was demonstrated that the decrease in the peak of the imaginary part of the microwave permeability with film thickness growth is related to the skin effect. The results obtained may be useful for microwave applications of soft magnetic CoFeB films.

A broadband method for measuring the complex permeability of thin magnetic films using a short-circuited microstrip fixture is presented. The method is based on full one-port offset-short calibration implemented directly in the fixture with a movable shorting wall, reducing sensitivity to coaxial-to-strip transition imperfections and eliminating the need for its precise optimization. Field-dependent normalization to the empty fixture reduces systematic errors from the external magnetic field, and a correction for residual saturated permeability improves retrieval accuracy. The method was validated on Co, supermalloy, and FeCo films on flexible PET substrates. Retrieved spectra agreed well with reference coaxial data and with the spectrum reconstructed from static magnetic measurements. In the present implementation, broadband spectra were obtained from 0.1 to 20 GHz with no significant systematic distortion, indicating that the proposed approach is suitable for accurate broadband characterization of thin magnetic films without reference standards or precise optimization of the coaxial-to-strip transition.