The fashion industry contributes to a significant environmental issue due to the increasing production and needs of the industry. The proactive efforts toward developing a more sustainable process via textile recycling has become the preferable solution. This urgent and important need to develop cheap and efficient recycling methods for textile waste has led to the research community’s development of various recycling methods. The textile waste recycling process can be categorized into chemical and mechanical recycling methods. This paper provides an overview of the state of the art regarding different types of textile recycling technologies along with their current challenges and limitations. The critical parameters determining recycling performance are summarized and discussed and focus on the current challenges in mechanical and chemical recycling (pyrolysis, enzymatic hydrolysis, hydrothermal, ammonolysis, and glycolysis). Textile waste has been demonstrated to be re-spun into yarn (re-woven or knitted) by spinning carded yarn and mixed shoddy through mechanical recycling. On the other hand, it is difficult to recycle some textiles by means of enzymatic hydrolysis; high product yield has been shown under mild temperatures. Furthermore, the emergence of existing technology such as the internet of things (IoT) being implemented to enable efficient textile waste sorting and identification is also discussed. Moreover, we provide an outlook as to upcoming technological developments that will contribute to facilitating the circular economy, allowing for a more sustainable textile recycling process.

Electrospun nanofibers of polyvinyl alcohol (PVA) have poor mechanical strength. As such their use has often been avoided, particularly in applications that require high mechanical properties. The objective of this study is to increase the mechanical properties of PVA nanofiber mats via physical crosslinking with solvent vapor treatment using organic solvents, dimethyl sulfoxide (DMSO), N, N-dimethyl formamide (DMF), and methanol. The effect of solvent vapor treatment on PVA nanofibers is clearly observed by scanning electron microscope (SEM). The tensile strength increased by over 60%, 90%, and 115% after solvent vapor treatment with DMF at a temperature of 40 °C for 2 h, 4 h, and 8 h, respectively, compared to untreated PVA nanofibers. In addition, Young's modulus of PVA nanofiber mats also increased after DMF treatment. As a comparison, DMSO and methanol were also used in solvent vapor treatment because of differences in their polymer-solvent affinity. Results showed that the highest improvement (100%) in mechanical strength was obtained using DMF. This study shows that solvent vapor treatment offers a simple and inexpensive method that provides excellent results and is a promising alternative treatment for use in increasing the mechanical properties of electrospun nanofibers.