This study addresses the challenges associated with conventional plywood shear testing by introducing a novel miniaturized shear test method. This approach utilizes a controlled router toolpath for precise sample fabrication, enabling efficient material use and data acquisition. Miniaturized samples, designed with double shear zones, were tested for τ_xy, τ_xz, and τ_yz configurations using a universal testing machine. Results revealed a mean ultimate shear strength ranging from 5.6 MPa to 7.3 MPa and a mean shear modulus ranging from 0.039 GPa to 0.095 GPa, confirming the orthotropic nature of plywood. The resulting shear behavior was determined with stress–strain curves correlated with failure patterns. The miniaturized tests effectively captured the material’s heterogeneous behavior, particularly at smaller scales, and demonstrated consistent load-bearing capacity even after substantial stress reduction, suggesting suitability for bracing applications. This method allows for increased sample sizes, facilitating robust data collection for developing and validating finite element models. Future work will focus on evaluating the scalability of the observed orthotropic behavior and data scatter at larger scales and assessing the potential for this method to replace conventional full-scale plywood shear testing.

The construction sector’s environmental footprint is driving the adoption of sustainable modular timber systems. The WikiHouse Skylark is a promising open-source model whose structural reliability depends on the performance of its critical plywood TIE joints. This study presents an experimental investigation of full-scale TIE joints fabricated from 18 mm Pinus radiata plywood in three variants: Standard (STD), Weather-Resistant (HR), and Fire-Resistant (FR). Monotonic tensile and shear tests were conducted to evaluate load–displacement behavior and failure modes. While the mean ultimate strengths varied between panel types, with HR highest in tension (7.7 kN) and FR highest in shear (8.2 kN), the most critical finding was the effect of the treatments on failure mode. The FR treatment induced a brittle fracture with significantly reduced ductility, in contrast to the more ductile tearing observed in STD and HR panels. This highlights a clear strength–ductility trade-off introduced by the fire-retardant treatment, a key consideration for structural design in modular timber construction. This dataset provides an essential empirical foundation for the numerical modeling and design guidelines of WikiHouse TIE joints, advancing the development of resilient and sustainable prefabricated housing.

This study introduces and validates a miniaturized testing methodology for the complete orthotropic characterization of structural plywood, including out-of-plane directions that are typically difficult to access. Novel small-scale geometries were developed for tension and shear configurations, with compliance corrections applied to ensure accurate stress–strain responses. The method proved reliable and sensitive to mechanical differences arising from veneer architecture, adhesive type, and interfacial bonding. Two sets of 18 mm structural plywood panels—manufactured with distinct adhesive systems, one bio-based (F1) and one phenol-formaldehyde (F2)—were systematically tested under tensile, compressive, and shear loading in ten orthogonal configurations (T_x, T_y, T_z, C_x, C_y, C_z, τ_xy, τ_yx, τ_xz, τ_yz), following standards NCh 3617, EN 789, and ASTM B831. Tensile moduli were approximately twice the corresponding compressive values, while out-of-plane moduli reached only 6–11% of in-plane values. F1 exhibited higher stiffness in both tension and compression, particularly in transverse directions, due to thicker perpendicular veneers enhancing bending restraint and shear coupling. In contrast, F2 achieved greater peak shear strength owing to its more uniform veneer structure, which improved stress distribution and delayed interlaminar failure. Observed asymmetry between tension and compression reflected microstructural mechanisms such as fiber alignment and cell-wall buckling. The miniature-specimen data provide reliable input for constitutive calibration and finite-element modeling, while revealing clear links between veneer-thickness distribution, shear-transfer efficiency, and macroscopic performance. The proposed framework enables efficient, reproducible orthotropic characterization for optimized, lightweight, and carbon-efficient timber systems.