We report on the structural evaluation of high fat fish oil-in-water emulsions emulsified with sodium caseinate (CAS) and phosphatidylcholine (PC). The microemulsions contained 70% (w/w) fish oil with 1.05-1.4% (w/w) CAS and 0.4-1.75% (w/w) PC and were studied by the combination of light scattering together with small-angle X-ray and neutron scattering (SAXS/SANS). Aqueous CAS forms aggregates having a denser core of about 100 kDa and less dense shell about 400 kDa with the hard sphere diameter of 20.4 nm. PC appears as multilayers whose coherence length spans from 40 to 100 nm. PC monolayer separates oil and water phases. Moreover, 80% CAS particles are loosely bound to the interface but are not forming continuous coverage. The distance between aggregated CAS particles in microemulsion is increased compared to CAS aggregates in pure CAS-in-water system. PC multilayers become larger in the presence of oil-water interface compared to the pure PC mixtures. Bilayers become larger with increasing PC concentration. This study forms a structural base for the combination of CAS and PC emulsifiers forming a well-defined thin and dense PC layer together with thick but less dense CAS layer, which is assumed to explain its better oxidative stability compared to single emulsifiers.

The present research aims to investigate the chemical and morphological properties of the methylated silica xerogels produced via the co-gelation approach combined with surface silylation. In the sol–gel synthesis, methyltrimethoxysilane (MTMS) and tetraethylorthosilicate (TEOS) were utilized as silica precursors and trimethylchlorosilane (TMCS) served as a silylating agent. Structural changes were observed depending on the MTMS/TEOS molar ratio and on the post-synthesis-performed surface silylation of the xerogels. Post-synthesis silylation plays a critical role in the exchanging of the surface silanols with methyl groups, preserving the monolithic form. The morphological and structural changes were followed by SEM, ²⁹Si-MAS-NMR, FTIR spectroscopy, nitrogen porosimetry, and contact angle measurements. The results have shown significant structural variations depending especially on the MTMS content. With an increasing MTMS content, the morphology of the samples has changed from a micro/mesoporous texture to a meso/macroporous texture. A higher degree of methyl substitution has been achieved for the silylated samples both confirmed by the FTIR and ²⁹Si-NMR results. On the other hand, only the samples with a high MTMS content could preserve their structural integrity after evaporative drying, and all have exhibited a high degree of hydrophobicity with θ > 140°.

This work is focused on a novel class of hybrid materials exhibiting enhanced optical properties and high surface areas that combine the morphology offered by the vinyl substituted silica host, and the excellent absorption and emission properties of 5,10,15,20-tetrakis(N-methyl-4-pyridyl)porphyrin-Zn(II) tetrachloride as a water soluble guest molecule. In order to optimize the synthesis procedure and the performance of the immobilized porphyrin, silica precursor mixtures of different compositions were used. To achieve the requirements regarding the hydrophobicity and the porous structure of the gels for the successful incorporation of porphyrin, the content of vinyltriacetoxysilane was systematically changed and thoroughly investigated. Substitution of the silica gels with organic groups is a viable way to provide new properties to the support. An exhaustive characterization of the synthesized silica samples was realised by complementary physicochemical methods, such as infrared spectroscopy (FT-IR), absorption spectroscopy (UV-Vis) and photoluminescence, nuclear magnetic resonance spectroscopy (29Si-MAS-NMR) transmission and scanning electron microscopy (TEM and SEM), nitrogen absorption (BET), contact angle (CA), small angle X ray and neutron scattering (SAXS and SANS). All hybrids showed an increase in emission intensity in the wide region from 575 to 725 nm (Q bands) in comparison with bare porphyrin. By simply tuning the vinyltriacetoxysilane content, the hydrophilic/hydrophobic profile of the hybrid materials was changed, while maintaining a high surface area. Good control of hydrophobicity is important to enhance properties such as dispersion, stability behaviour, and resistance to water, in order to achieve highly dispersible systems in water for biomedical applications.

In this work, a multi-analytical approach involving nitrogen porosimetry, small angle neutron and X-ray scattering, Fourier transform infrared (FTIR) and nuclear magnetic resonance (NMR) spectroscopies, X-ray diffraction, thermal analysis and electron microscopy was applied to organically modified silica-based xerogels obtained through the sol–gel process. Starting from a tetraethoxysilane (TEOS) precursor, methyltriethoxysilane (MTES) was added to the reaction mixture at two different pH values (2.0 and 4.5) producing hybrid xerogels with different TEOS/MTES molar ratios. Significant differences in the structure were revealed in terms of the chemical composition of the silica network, hydrophilic/hydrophobic profile, particle dimension, pore shape/size and surface characteristics. The combined use of structural characterization methods allowed us to reveal a relation between the cavity dimensions, the synthesis pH value and the grade of methyl substitution. The effect of the structural properties on the controlled Captopril release efficiency has also been tested. This knowledge facilitates tailoring the pore network for specific usage in biological/medical applications. Knowledge on structural aspects, as reported in this work, represents a key starting point for the production of high-performance silica-based hybrid materials showing enhanced efficacy compared to bare silica prepared using only TEOS.

Purpose: Red chili peppers have been highly valued in gastronomy and traditional medicine since ancient times; it seems that it is not just an ingredient for food but also a good remedy for various medical conditions such as increased blood pressure and high levels of serum triglycerides and cholesterol, myocardial infarction, arthritis, and migraines. The objective of this study is the characterization of a new carrier used for encapsulated extract. Methods: Chili pepper extract was obtained and was physically entrapped inside polyurethane microparticles in order to diminish the irritative potential of this extract. The particles were evaluated by Zetasizer measurements, small-angle neutron scattering and thermal analysis, scanning electron microscopy (SEM), and Fourier transform infrared spectroscopy; the encapsulation efficacy and the drug release profile were assessed by UV-Vis spectroscopy. Bioevaluations on mice skin were performed to predict the irritative potential of the samples. Results: Two different types of samples were compared: hollow polyurethane microparticles vs polyurethane particles containing the natural extract. The sizes of the particles were very similar, but the sample containing the extract presents three particle populations (the polydispersity index increases from 0.3 to 0.6 from one sample to another). The zeta-potential measurements and SEM images indicate a medium tendency to form clusters, while the UV-Vis study revealed an almost 70% encapsulation efficacy. Conclusion: The results suggest that encapsulation of a chili pepper extract inside polyurethane microparticles leads to a non-irritative product with a prolonged release: ~30% of encapsulated extract is released within the first 8 days and a maximum 45% is reached in 2 weeks.

Due to their effect of vasodilatation, isosorbide nitrates represent one of the most important and most used solutions for angina pectoris. Unfortunately, these compounds have multiple dose-related adverse drug reactions such as headache, weakness, mild dizziness, and occasionally heart rate changes, nausea, vomiting, and sweating. The main aims of this research were to obtain and to evaluate new polyurethane (PU) structures that can be used as a proper transmembrane carrier with an improved release kinetic. Chitosan-based PU structures were obtained by a polyaddition process between hexamethylene diisocyanate and a mixture of chitosan, butanediol, and polyethylene glycol in the presence of caffeine as a synthesis catalyst. The obtained samples (with and without isosorbide nitrates) were characterized regarding the encapsulation and release rate (UV-Vis spectra), chemical composition (FTIR), thermal stability (thermal analysis), morphology changes (SEM and SANS), and in vivo irritation tests. These methods revealed no significant differences between the two sample structures. Multipopulational structures with sizes between 73 and 310 nm, with an increased tendency to form clusters and a high resistance to heat (up to 280°C), were obtained. This study presents an alternative administration of isosorbide derivatives based on a PU carrier with a high biocompatibility and a prolonged release.