Structural and morphological features of graft polystyrene (PS) and polyethylene (PE) copolymers produced by post-radiation chemical polymerization have been investigated by methods of X-ray microanalysis, electron microscopy, DSC and wetting angles measurement. The studied samples differed in the degree of graft, iron(II) sulphate content, sizes of PE films and distribution of graft polymer over the polyolefin cross section. It is shown that in all cases sample surfaces are enriched with PS. As the content of graft PS increases, its concentration increases both in the volume and on the surface of the samples. The distinctive feature of the post-radiation graft polymerization is the stepped curves of graft polymer distribution along the matrix cross section. A probable reason for such evolution of the distribution profiles is related to both the distribution of peroxide groups throughout the sample thickness and to the change in the monomer and iron(II) salt diffusion coefficients in the graft polyolefin layer. According to the results of electron microscope investigations and copolymer wettability during graft polymerization, a heterogeneous system is formed both in the sample volume and in the surface layer. It is shown that the melting point, glass transition temperature and degree of crystallinity of the copolymer decreases with the increasing proportion of graft PS. It is suggested that during graft polymerization a process of PE crystallite decomposition (melting) and enrichment of the amorphous phase of graft polymer by fragments of PE macromolecules occurs spontaneously. The driving force of this process is the osmotic pressure exerted by the phase network of crystallites on the growing phase of the graft PS.

The adhesion characteristics and surface energies of two series of polyamidoimides (PAI) with different molecular weights, monomer unit structures, hinge groups in the main chain of the macromolecules, and thermal prehistory were determined via delamination at 180° and test fluids contact angles. We found that PAI are high-energy polymers, the surface energy of which varies in the range from 32 to 45 mJ/m². In contrast to flexible-chain polymers, the exponent in the McLeod equation is two, which is due to the flat parallel orientation of the macromolecular chains in the surface layers. The main contribution to the change in surface characteristics of these polymers is the change in the packing density of PAI macromolecules, which is reflected mainly in the change in the polymers’ dispersion component. We found that the adhesion properties of PAI with respect to high- and low-energy substrates are determined mainly by the macromolecules packing density in the surface layers with their conformation state unchanged.

The development of universal finishing compositions for fibers of various natures is an urgent task for polymer composite materials science. The developed finishes can be used for the fiber reinforcement of polymer matrices with a wide range of surface free energy characteristics. Epoxy systems modified with diaminesilane in a wide concentration range were examined by optical interferometry, FTIR spectroscopy, DSC and the sessile drop technique. It was shown that the partial curing of epoxy resin by diaminesilane at room temperature under an inert atmosphere, followed by contact with air, leads to a significant increase of the surface free energy of the system. Varying the concentration of diaminesilane allows us to effectively regulate the surface free energy of the composition. This makes it possible to use fibers finished with epoxyaminosilane compositions in composite materials based on a various thermosetting and thermoplastic binders with a surface tension of up to 75 mJ/m².

The results of systematic studies on the surface energy γ and its polar γ^P and dispersion γ^D components of statistical copolymers of styrene and butadiene, acrylonitrile and butadiene, and butyl acrylate and vinyl acetate, with regard to their thermal prehistory, are generalized. Along with copolymers, the surfaces of their composing homopolymers were examined. We obtained the energy characteristics of the adhesive surfaces of copolymers that contacted with air, high-energy aluminium Al (γ = 160 mJ/m²), and the low-energy substrate surface of polytetrafluoroethylene F4 (PTFE) (γ = 18 mJ/m²). The surfaces of copolymers in contact with air, aluminium, and PTFE were investigated for the first time. It was found that the surface energy of these copolymers tended to occupy an intermediate value between the surface energy of the homopolymers. The additive nature of the change in the surface energy of the copolymers with their composition, as previously established in the works of Wu, extends to the dispersive component of the free surface energy γ^D and the critical surface energy γ_cr, according to Zisman. It was shown that a significant influence on the adhesive activity of copolymers was exerted by the substrate surface upon which the adhesive was formed. Thus, for the butadiene–nitrile copolymer (BNC) samples formed in contact with a high-energy substrate, their surface energy growth was associated with a significant increase in the polar component of the surface energy γ^P from 2 mJ/m² for the samples formed in contact with air, to an increase from 10 to 11 mJ/m² for the samples formed in contact with Al. The reason why the interface influenced the change in the energy characteristics of the adhesives was the selective interaction of each macromolecule fragment with the active centres of the substrate surface. As a result, the composition of the boundary layer changed and it became enriched with one of the components. The structure of such layers is nonequilibrium. The thermal annealing of copolymers in the mode of a stepwise temperature increase led to a convergence in the values of γ, asymptotically tending to the value characteristic of the surface of the copolymers formed in air. The activation energies for the processes of the conformational rearrangements of the macromolecules in the surface layers of the copolymers were calculated. It was found that the conformational rearrangements of the macromolecules in the surface layers occurred as a result of the internal rotation of the functional groups that determined the polar component of the surface energy.

Electroadhesive systems are promising for creating delicate robotic manipulators operating both in the natural environment and in space conditions. Using thermosetting epoxy resin, polyurethane and polyester resin as examples, the influence of the polymers’ natures, potential differences and current strengths on electroadhesive interactions in polymer–polymer systems was studied. The investigations were carried out by recording the force of normal separation of substrates from electroadhesives using contact and contactless methods at various electrical parameters of the systems and their components. A correlation was established between the relative permittivity and the electroadhesive force. The relaxation nature of the electroadhesion phenomenon after removing the electrical voltage was revealed. The influence of the potential difference and current strength on the effect of electroadhesion for polymer substrates of various natures was established. The obtained dependencies describe the main regularities of electroadhesive interactions necessary for creating promising electroadhesive materials.

A comparative study of anticorrosive inhibited polymer films on the tungsten surface formed from an aqueous solution of inhibited formulations (INFOR) containing organosilane and corrosion inhibitors was carried out by means of the prolonged exposure of a tungsten product in a modifying solution and by the method of cataphoretic deposition (CPD). Depending on the method of forming films on tungsten, the molecular organization of the near-surface layers was studied (ATR-FTIR), and the subprimary structure of the films was explored (TEM). The optimal modes of cataphoresis deposition (CPD duration and current density applied to the sample) for the formation of a protective inhibited polymer film on the tungsten surface were established by means of SEM. The energy and thermochemical characteristics (sessile drop and DSC methods), as well as operational (adhesive behavior) and protective filming ability (EIS and corrosion behavior), according to the method of formation of inhibited polymer film, were determined. Based on the combined characteristics of the films obtained by the two methods and the deposition modes, the CPD method showed better performance than the electroless dipping method.