Temperature-responsive photonic coatings are appealing for a variety of applications, including smart windows. However, the fabrication of such reflective polymer coatings remains a challenge. In this work, we report the development of a temperature-responsive, infrared-reflective coating consisting of a polymer-stabilized cholesteric liquid crystal siloxane, applied by a simple bar coating method. First, a side-chain liquid crystal oligosiloxane containing acrylate, chiral and mesogenic moieties was successfully synthesized via multiple steps, including preparing precursors, hydrosilylation, deprotection, and esterification reactions. Products of all the steps were fully characterized revealing a chain extension during the deprotection step. Subsequently, the photonic coating was fabricated by bar-coating the cholesteric liquid crystal oligomer on glass, using a mediator liquid crystalline molecule. After the UV-curing and removal of the mediator, a transparent IR reflective polymer-stabilized cholesteric liquid crystal coating was obtained. Notably, this fully cured, partially crosslinked transparent polymer coating retained temperature responsiveness due to the presence of non-reactive liquid-crystal oligosiloxanes. Upon increasing the temperature from room temperature, the polymer-stabilized cholesteric liquid crystal coating showed a continuous blue-shift of the reflection band from 1400 nm to 800 nm, and the shift was fully reversible.

1,4,7,10‐Tetrakis{[N‐(1H‐imidazol‐2‐yl)carbamoyl]methyl}‐1,4,7,10‐tetraazacyclododecane (dotami), a tetra(1H‐imidazol‐2‐yl) derivative of the well‐studied octadentate 1,4,7,10‐tetrakis[(carbamoyl)methyl]‐1,4,7,10‐tetraazacyclododecane (dotam) ligand, was synthesized by reaction of 1,4,7,10‐tetraazacyclododecane with N‐(1H‐imidazol‐2‐yl)chloroacetamide in high yield. Its tricationic thulium complex was isolated as a water‐soluble chloride salt. The detection of the mildly acidic amide and amine protons by direct proton NMR in aqueous solution was unsuccessful, but such exchangeable protons could be detected via their chemical exchange‐dependent saturation transfer (CEST) effect. The observed CEST effect was distinctly different from that found for respective dotam complexes and is, therefore, ascribed to exchangeable protons associated with the imidazole substituent.

Despite progress in the field of electrochromic devices, developing structural color-tunable photonic systems having both high transparency and flexibility remains challenging. Here, an ink-deposited transparent electrochromic structural colored foil displaying reflective colors, tuned by an integrated heater, is prepared in a single-substrate method. Efficient and homogeneous heating is induced by a gravure printed silver nanowire-based substrate, delivering an electrothermal response upon applying an electrical potential. On top of this flexible, transparent heater, a cholesteric liquid crystal ink is bar-coated and subsequently photopolymerized, yielding a structural colored film that exhibits temperature-responsive color changes. The transparent electrochromic foils appear colorless at room temperature but demonstrate structural color tuning with high optical quality when modifying the electrical potential. Both optical and electrothermal performances were preserved when deforming the foils. Applying the conductive and structural colored inks via the easy processable, continuous methods of gravure printing and barcoating highlights the potential for scaling up to large-scale stimuli-responsive, transparent optical foils. These transparent structural colored foils can be potentially used for a wide range of photonic devices including smart windows, displays, and sensors and can be directly installed on top of curved, flexible surfaces.

Cholesteric liquid crystal oligomers are widely researched for their interesting thermochromic properties. However, structure-property relationships to program the thermochromic properties of these oligomers have been rarely reported. In this work, we use the versatile thiol-ene click reaction to synthesize a series of hetero-oligomers and study the impact of different compositions on the thermochromic behavior of the resulting material. Characterization of the oligomers shows significantly different rates of reaction for the monomers despite their very similar structures, which leads to oligomer compositions that do not match the original reaction feed. The oligomers are then used to produce thin near-infrared reflecting coatings. The best-performing thermochromic reflector has a room-temperature reflection band that shifts a total of 510 nanometers upon heating to 120 °C. The shift is repeatable for up to 10 times with no appreciable degradation. The room temperature reflection of the coatings is shown to be tunable not only by adjusting the chiral dopant concentration but also by the ratio of the monomers. Finally, we show that the oligomers can be chemically modified by making their reactive end groups undergo a reaction with monothiol compounds. These modifications allow for further fine-tuning of liquid crystal oligomers for heat-regulating window films, for example.

The fabrication of a foldable, compact liquid crystal actuator based on oxetane reactive monomers is reported. The free-standing liquid crystal network films are optically clear, flexible, and have easily tunable anisotropic thermal and mechanical properties. The oxetane liquid crystal networks demonstrate excellent one-way shape memory properties, with good temporary shape fixation and complete shape recovery. In addition, the flexible polyether backbone of the oxetane liquid crystal networks results in large two-way bending actuation, with the actuators showing rotation inversion and making multiple rotations. Both actuation mechanisms could be combined to form actuators that can be temporarily folded before fully recovering to their original shape prior to use. As a result, the oxetane liquid crystal networks have great potential as foldable, compact actuators.

The effect of layer spacing and halogenation on the gas separation performances of free-standing smectic LC polymer membranes is being investigated by molecular engineering. LC membranes with various layer spacings and halogenated LCs were fabricated while having a planar aligned smectic morphology. Single permeation and sorption data show a correlation between gas diffusion and layer spacing, which results in increasing gas permeabilities with increasing layer spacing while the ideal gas selectivity of He over CO₂ or He over N₂ decreases. The calculated diffusion coefficients show a 6-fold increase when going from membranes with a layer spacing of 31.9 Å to membranes with a layer spacing of 45.2 Å, demonstrating that the layer spacing in smectic LC membranes mainly affects the diffusion of gasses rather than their solubility. A comparison of gas sorption and permeation performances of smectic LC membranes with and without halogenated LCs shows only a limited effect of LC halogenation by a slight increase in both solubility and diffusion coefficients for the membranes with halogenated LCs, resulting in a slightly higher gas permeation and increased ideal gas selectivities towards CO₂. These results show that layer spacing plays an important role in the gas separation performances of smectic LC polymer membranes.