A low cost composite material was synthesized for neodymium recovery from dilute aqueous solutions. The in-situ production of the composite containing chitosan and iron(III) hydroxide (ChiFer(III)) was improved and the results were compared with raw chitosan particles. The sorbent was characterized using Fourier transform infrared spectroscopy (FTIR) and scanning electron microscopy-energy dispersive X-ray analyses (SEM-EDX). The equilibrium studies were performed using firstly a batch system, and secondly a continuous system. The sorption isotherms were fitted with the Langmuir, Freundlich, and Sips models; experimental data was better described with the Langmuir equation and the maximum sorption capacity was 13.8 mg g-1 at pH 4. The introduction of iron into the biopolymer matrix increases by four times the sorption uptake of the chitosan; the individual sorption capacity of iron (into the composite) was calculated as 30.9 mg Nd/g Fe. The experimental results of the columns were fitted adequately using the Thomas model. As an approach to Nd-Fe-B permanent magnets effluents, a synthetic dilute effluent was simulated at pH 4, in order to evaluate the selectivity of the sorbent material; the overshooting of boron in the column system confirmed the higher selectivity toward neodymium ions. The elution step was carried out using MilliQ-water with the pH set to 3.5 (dilute HCl solution).

The present work describes the study of mercury Hg(II) and lead Pb(II) removal in single and binary component systems into easily prepared chitosan-iron(III) bio-composite beads. Scanning electron microscopy and energy-dispersive X-ray (SEM-EDX) analysis, Fourier transform infrared spectroscopy (FTIR), thermogravimetric analysis (TGA) and point of zero charge (pH_pzc) analysis were carried out. The experimental set covered pH study, single and competitive equilibrium, kinetics, chloride and sulfate effects as well as sorption–desorption cycles. In single systems, the Langmuir nonlinear model fitted the experimental data better than the Freundlich and Sips equations. The sorbent material has more affinity to Hg(II) rather than Pb(II) ions, the maximum sorption capacities were 1.8 mmol·g⁻¹ and 0.56 mmol·g⁻¹ for Hg(II) and Pb(II), respectively. The binary systems data were adjusted with competitive Langmuir isotherm model. The presence of sulfate ions in the multicomponent system [Hg(II)-Pb(II)] had a lesser impact on the sorption efficiency than did chloride ions, however, the presence of chloride ions improves the selectivity towards Hg(II) ions. The bio-based material showed good recovery performance of metal ions along three sorption–desorption cycles.

We modified and evaluated the performance of a CuO/Cu electrochemical electrode for chemical oxygen demand (COD) determination by covering it with a Nafion (Nf) film. The resulting modified CuONf/Cu electrode sensor was used for the electrochemical determination of COD in river, slaughterhouse and estuarine water samples in order to evaluate its performance for this particular task. It was compared with the CuO/Cu sensor with no Nafion. The main electrochemical characteristics of interest, resistance, sensitivity, accuracy and reproducibility, were assessed by means of Linear Sweep Voltammetry using glucose as a standard. Results of these essays indicate that the procedure used produced smooth and firmly attached Nf films covering the whole copper surface. This sensor was shown to be resistant to interferences and effective in electro-oxidation of a wide range of organic compounds and therefore very useful for COD determination. Using the newly developed CuONf/Cu electrode an analytical linear range of 50 to 1000 mg·L⁻¹ COD, with a detection limit of 2.11 mg·L⁻¹ (n = 6) COD was achieved. The comparison shows that the CuONf/Cu sensor is more appropriate for COD determination than its counterpart with no Nafion.

The presence of antimony(III) in water represents a worldwide concern, mainly due to its high toxicity and carcinogenicity potential. It can be separated from water by the use of sustainable biopolymers such as chitosan or its derivatives. The present study applied chitosan modified with iron(III) beads to Sb(III) removal from aqueous solutions. The resulting material performed with a high adsorption capacity of 98.68 mg/g. Material characterization consisted of Raman spectroscopy (RS), X-ray diffraction (XRD), scanning electron microscope observations (SEM-EDX), Fourier transform infrared spectroscopy (FTIR) and point of zero charge (pH_pzc). The adsorption study included pH study, effect of initial concentration, kinetics, ion effect, and reusability assessment. The RS, XRD, and FTIR results indicated that the main functional groups in the composite were related to hydroxyl and amino groups, and iron oxyhydroxide species of α-FeO(OH). The pH_pzc was found to be 7.41. The best adsorption efficiency was set at pH 6. The equilibrium isotherms were better fitted with a non-linear Langmuir model, and the kinetics data were fitted with a pseudo-second order rate equation. The incorporation of iron into the chitosan matrix improved the Sb(III) uptake by 47.9%, compared with neat chitosan (CS). The material did not exhibit an impact in its performance in the presence of other ions, and it could be reused for up to three adsorption–desorption cycles.

Neodymium is a key rare-earth element applied to modern devices. The purpose of this study is the development of a hybrid biomaterial based on chitosan (CS) and manganese ferrite (MF) for the recovery of Nd(III) ions from the aqueous phase. The preparation of the beads was performed in two stages; first, MF particles were obtained by the assessment of three temperatures during the co-precipitation synthesis, and the best nano-MF crystallites were incorporated into CS to obtain the hybrid composite material (CS-MF). The materials were characterized by FTIR, XRD, magnetization measurements, and SEM-EDX. The adsorption experiments included pH study, equilibrium study, kinetics study, and sorption–desorption reusability tests. The results showed that for MF synthesis, 60 °C is an appropriate temperature to obtain MF crystals of ~30 nm with suitable magnetic properties. The final magnetic CS-MF beads perform maximum adsorption at pH 4 with a maximum adsorption capacity of 44.29 mg/g. Moreover, the material can be used for up to four adsorption–desorption cycles. The incorporation of MF improves the sorption capacity of the neat chitosan. Additionally, the magnetic properties enable its easy separation from aqueous solutions for further use. The material obtained represents an enhanced magnetic hybrid adsorbent that can be applied to recover Nd(III) from aqueous solutions.