With the increasing volume of synthetic fiber waste, interest in plastic reuse technologies has grown. To address this issue, physical and chemical recycling techniques for polyamide, a major component of textile waste, have been developed. This study investigates the remelting and reforming properties of four types of pristine and recycled polyamide 6, focusing on how the microstructural arrangement of recycled polyamides affects polymer fiber formation. DSC and FT-IR were used to determine the thermal properties and chemical composition of the reformed thin films. Differences in the elongation behavior of molten fibers during the spinning process were also observed, and the morphology of the resulting fibers was examined via SEM. Birefringence analysis revealed that the uniformity of the molecular structure greatly influenced differences in the re-fiberization process, suggesting that chemically recycled polyamide is the most suitable material for re-fiberization with its high structural similarity to pristine polyamide.

In this study, a transient viscosity adjustment method using a coaxial nozzle was explored to fabricate nanofibers from non-spinnable m-poly(hydroxyamide) (m-PHA). Unlike conventional electrospinning methods that often require additives to induce fiber formation, this approach relies on a sheath-core configuration, introducing tetrahydrofuran (THF) to the sheath to temporarily adjust solution viscosity. The diffusion of THF into the core m-PHA solution resulted in momentary solidification at the interface, promoting nanofiber formation without compromising polymer solubility. SEM and rheological analyses confirmed that optimized sheath-to-core flow ratios yielded nanofibers with significantly reduced particle formation. Notably, increasing the THF flow rate facilitated a faster solidification rate, enhancing jet elongation and resulting in uniform nanofibers with diameters of approximately 180–190 nm. Although complete nanofibers without beads were not achieved in this study, this coaxial electrospinning approach presents a possible pathway for fabricating nanofibers from polymers with limited spinnability, potentially expanding the application scope of electro-spun materials in high-performance fields.