Titanium (Ti) is widely recognized for its exceptional properties and compatibility with medical applications. In our study, we successfully formed laser-induced periodic surface structures (LIPSS) on Ti plates with a periodicity of 520–740 nm and a height range of 150–250 nm. To investigate the morphology and chemical composition of these surfaces, we employed various techniques, including field emission scanning electron microscopy, energy dispersive X-ray spectroscopy, atomic force microscopy, X-ray photoelectron spectroscopy, and Raman spectroscopy. Additionally, we utilized a drop-shape analyzer to determine the wetting properties of the surfaces. To evaluate the antibacterial activity, we followed the ISO 22196:2011 standard, utilizing reference bacterial cultures of Gram-positive Staphylococcus aureus (ATCC 25923) and Gram-negative Escherichia coli (ATCC 25922). The results revealed enhanced antibacterial properties against Staphylococcus aureus by more than 99% and Escherichia coli by more than 80% in comparison with non-irradiated Ti. Furthermore, we conducted experiments using the Escherichia coli bacteriophage T4 (ATCC 11303-B4) and the bacterial host Escherichia coli (ATCC 11303) to investigate the impact of Ti plates on the stability of the bacteriophage. Overall, our findings highlight the potential of LIPSS on Ti plates for achieving enhanced antibacterial activity against common bacterial strains while maintaining the stability of bacteriophages.

CeO₂/CuO primary antimicrobial mechanism was high ROS production, resulting in faster and stronger activity than CuO. It showed low cytotoxicity to human keratinocytes in vitro and no acute toxicity to the bacterium Vibrio fischeri.

Mullite and mullite–alumina ceramics materials with dominance of the mullite phase are used in different areas of technology and materials science. Porous mullite ceramics materials can be used simultaneously as refractory heat insulators and also as materials for constructional elements. The purpose of this work was to investigate the WO₃ nanoparticle influence on the evolution of the aluminum tungstate and zircon crystalline phases in mullite ceramics due to stabilization effects caused by different microsize ZrO₂ and WO₃. The use of nano-WO₃ prevented the dissociation of zircon in the ceramic samples with magnesia-stabilized zirconia (MSZ), increased porosity by approximately 60 ± 1%, increased the intensity of the aluminum tungstate phase, decreased bulk density by approximately 1.32 ± 0.01 g/cm³, and increased thermal shock resistance by ensuring a loss of less than 5% of the elastic modulus after 10 cycles of thermal shock.

We elaborate a method for determining the 0D–1D nanostructure size by photoluminescence (PL) emission spectrum dependence on the nanostructure dimensions. As observed, the high number of diamond-like carbon nanocones shows a strongly blue-shifted PL spectrum compared to the bulk material, allowing for the calculation of their top dimensions of 2.0 nm. For the second structure model, we used a sharp atomic force microscope (AFM) tip, which showed green emission localized on its top, as determined by confocal microscopy. Using the PL spectrum, the calculation allowed us to determine the tip size of 1.5 nm, which correlated well with the SEM measurements. The time-resolved PL measurements shed light on the recombination process, providing stretched-exponent decay with a τ₀ = 1 ns lifetime, indicating a gradual decrease in exciton lifetime along the height of the cone from the base to the top due to surface and radiative recombination. Therefore, the proposed method provides a simple optical procedure for determining an AFM tip or other nanocone structure sharpness without the need for sample preparation and special expensive equipment.