Making the most of twists and turns: The rise of small-scale, portable electronics and wearable devices has boosted the desire for ways to harvest energy from mechanical motion. Such approaches could be used to provide battery-free power with a small footprint. Kim et al. present an energy harvester made from carbon nanotube yarn that converts mechanical energy into electrical energy from both torsional and tensile motion. Their findings reveal how the extent of yarn twisting and the combination of homochiral and heterochiral coiled yarns can maximize energy generation. Science , this issue p. 773

The extraordinary properties of graphene and carbon nanotubes motivate the development of methods for their use in producing continuous, strong, tough fibres. Previous work has shown that the toughness of the carbon nanotube-reinforced polymer fibres exceeds that of previously known materials. Here we show that further increased toughness results from combining carbon nanotubes and reduced graphene oxide flakes in solution-spun polymer fibres. The gravimetric toughness approaches 1,000 J g⁻¹, far exceeding spider dragline silk (165 J g⁻¹) and Kevlar (78 J g⁻¹). This toughness enhancement is consistent with the observed formation of an interconnected network of partially aligned reduced graphene oxide flakes and carbon nanotubes during solution spinning, which act to deflect cracks and allow energy-consuming polymer deformation. Toughness is sensitive to the volume ratio of the reduced graphene oxide flakes to the carbon nanotubes in the spinning solution and the degree of graphene oxidation. The hybrid fibres were sewable and weavable, and could be shaped into high-modulus helical springs.

Getting the most out of muscles: Materials that convert electrical, chemical, or thermal energy into a shape change can be used to form artificial muscles. Such materials include bimetallic strips or host-guest materials or coiled fibers or yarns (see the Perspective by Tawfick and Tang). Kanik et al. developed a polymer bimorph structure from an elastomer and a semicrystalline polymer where the difference in thermal expansion enabled thermally actuated artificial muscles. Iterative cold stretching of clad fibers could be used to tailor the dimensions and mechanical response, making it simple to produce hundreds of meters of coiled fibers. Mu et al. describe carbon nanotube yarns in which the volume-changing material is placed as a sheath outside the twisted or coiled fiber. This configuration can double the work capacity of tensile muscles. Yuan et al. produced polymer fiber torsional actuators with the ability to store energy that could be recovered on heating. Twisting mechanical deformation was applied to the fibers above the glass transition temperature and then stored via rapid quenching. Science , this issue p. 145 , p. 150 , p. 155 ; see also p. 125

Fiber and yarn supercapacitors that are elastomerically deformable without performance loss are sought for such applications as power sources for wearable electronics, micro-devices and implantable medical devices. Previously reported yarn and fiber supercapacitors are expensive to fabricate, difficult to upscale, or non-stretchable, which limits possible use. The elastomeric electrodes of the present solid-state supercapacitors are made by using giant inserted twist to coil a nylon sewing thread that is helically wrapped with a carbon nanotube sheet and then electrochemically depositing pseudocapacitive MnO₂ nanofibers. These solid-state supercapacitors decrease capacitance by less than 15% when reversibly stretched by 150% in the fiber direction and largely retain capacitance while being cyclically stretched during charge and discharge. The maximum linear and areal capacitances (based on active materials) and areal energy storage and power densities (based on overall supercapacitor dimensions) are high (5.4 mF/cm, 40.9 mF/cm², 2.6 μWh/cm² and 66.9 μW/cm², respectively), despite the engineered superelasticity of the fiber supercapacitor. Retention of supercapacitor performance during large strain (50%) elastic deformation is demonstrated for supercapacitors incorporated into the wristband of a glove.