Additive manufacturing procedures are being increasingly developed, from prototyping to finished functional products. However, their rapid development also brings along the testing of properties with different manufacturing parameters. In selective laser sintering, the most influential manufacturing parameter is the energy density, which also consists, among other things, of the hatch distance. For better usage of the entire chamber and a reduction in the overall price of the finished product, in practice, the manufacturing of products at different heights (levels) of the working chamber with different orientations is inevitable. The study examines how hatch distance and product orientation impact the tensile strength and dimensional stability of polyamide products across two levels within the chamber. Upon analysis, it was observed that manufacturing products at different levels within the working chamber does not influence their dimensions. Achieving precise product dimensions comparable to those in the CAD model is possible. Furthermore, the same factors (orientation and hatch distance) and their combinations affect the length, thickness, and width of the product. Although all test specimens were tested, a tensile strength analysis of variance (ANOVA) of test specimens produced at the lower level of the chamber with a combination of hatch distance (ranging from 0.23 to 0.6 mm) and orientation (ranging from 0° to 60°) was not feasible in the design of the experiment. Despite this limitation, it was noted that both chamber levels had the potential to reach a maximum tensile strength of 47 N/mm². Nevertheless, the average tensile strength of PA12, obtained through combinations of input factors, stood at only 30 N/mm², which is quite a low value for polyamide made by selective laser sintering.

Polymer composites have been utilized across various industries, especially in transportation, for many years. With a growing emphasis on sustainable production resources, the industry increasingly favours composite materials reinforced with natural fibres or particles. Unlike conventional fibres such as glass, carbon, or aramid, natural fibres typically have low compatibility with polymer matrices, often necessitating pretreatment to enhance bonding. In this study, coir fibres were physically and chemically treated with sodium bicarbonate solutions at varying concentrations (5–15%) and immersion durations (0–5 days). The treated fibres were then mixed into epoxy resin and poured into moulds to produce test specimens for evaluating mechanical properties. The fibre content in the composites ranged from 10 to 20%. Statistical analysis revealed that immersion time significantly affects all mechanical properties tested (tensile modulus, tensile strength, strain, and impact strength). Solution concentration significantly influences tensile modulus and strain, while fibre content significantly affects tensile modulus and strength. The conducted optimization shows that the best mechanical properties are achieved with the minimum tested coir fibre content of 10%. Maximum stiffness and strength can be expected with the longest immersion time of 5 days in the highest solution concentration of 15%. The best strain and impact strength properties, however, are observed at the lowest solution concentration of 5%.