Transparent conductive oxides are essential materials for many optoelectronic applications. For new devices for aerospace and space applications, it is crucial to know how they respond to the space environment. The most important issue in commonly used low-Earth orbits is proton radiation. This study examines the effects of high-energy proton irradiation (226.5 MeV) on thin films of aluminium-doped zinc oxide (AZO) and indium tin oxide (ITO). We use X-ray diffraction and electron microscopy observations to see the changes in the structure and microstructure of the films. The optical properties and homogeneity of the materials are determined by spectrophotometry and spectroscopic ellipsometry (SE). Analysis of the chemical states of the elements with X-ray photoelectron spectroscopy (XPS) gives insight into what proton irradiation changes at the surface of the oxides. All measurements show that ITO is less influenced than AZO. The proton energy and fluence used in this study simulate about a hundred years in low Earth orbit. This research demonstrates that both transparent conductive oxide thin films can function under simulated space conditions, with ITO showing superior resilience. The ITO film was more homogenous in terms of the total thickness measured with SE, had fewer defects and adsorbates present on the surface, as XPS analysis proved, and did not show a difference after irradiation regarding its optical properties, transmission, refractive index, or extinction coefficient.

Titanium-based bulk metallic glasses (BMGs) offer high strength, lower stiffness than Ti-6Al-4V, and superior corrosion resistance, but conventional Ti glass-forming systems often contain toxic Ni, Be, or Cu. This work investigates five novel Ti-based alloys free of these elements—Ti₄₂Zr₃₅Si₅Co_12.5Sn_2.5Ta₃, Ti₄₂Zr₄₀Ta₃Si₁₅, Ti₆₀Nb₁₅Zr₁₀Si₁₅, Ti₃₉Zr₃₂Si₂₉, and Ti_65.5Fe_22.5Si₁₂—synthesized by arc melting and suction casting. Single-track laser remelting using a selective laser melting (SLM) system was performed to simulate additive manufacturing and examine microstructural evolution, cracking behavior, mechanical properties, and cytocompatibility. All alloys solidified into fully crystalline α/β-Ti matrices with Ti/Zr silicides; no amorphous structures were obtained. Laser remelting refined the microstructure but did not induce glass formation, consistent with the known limited glass-forming ability of Cu/Ni/Be-free Ti systems. Cracking was observed at low laser energies but crack density decreased as laser energy increased. Cracks were eliminated above ~0.4 J/mm for most alloys. Ti₄₂Zr₃₅Si₅Co_12.5Sn_2.5Ta₃ exhibited the lowest stiffness (~125 GPa), while Ti₆₀Nb₁₅Zr₁₀Si₁₅ showed the highest due to silicide precipitation. Cytotoxicity tests (ISO 10993-5) confirmed all alloys to be non-toxic, with some extracts even enhancing fibroblast proliferation. This rapid laser-remelting approach enables cost-effective screening of Ti-based glass-forming alloys for additive manufacturing. Ti–Zr–Ta–Si systems demonstrated the most promising properties for further testing using the powder bed method.