The paper presents the process of cellulose extraction from rice straw using water–alkaline solution treatment and the subsequent process of carboxymethylation of the obtained product when activated by microwave radiation. After mercerization of rice straw, the obtained product contained 89.2% cellulose and 6.7% lignin. The X-ray diffraction pattern of the obtained lignocellulose shows three diffraction peaks in the region typical for the polymorphic modification of cellulose Iβ (2θ = 15.50(78), 21.70(145), 34.70(52)). The degree of crystallinity was 65%. The product was heat-stable up to 247 °C. The synthesis of carboxymethylcellulose (CMC) based on the obtained product included successive processes of thermostating in alcohol–alkali solution and cellulose esterification reaction using monochloroacetic acid. To activate the carboxymethylation process, microwave radiation was used (350 W for 90 s), which made it possible to reduce the reaction time by more than 100 times. Functional group analysis of the carboxylated lignocellulose from rice straw was carried out using an FTIR spectrometer. In the IR spectra, a band with a maximum of 1742 cm⁻¹ was recorded, corresponding to stretching vibrations of >C(O)OH groups. The degree of polymerization was recorded by mass spectrometry.

The work is aimed at the development of an energy-saving technique involving the partial carboxylation of powdered lignocellulose products from the straw of annual agricultural plants and the use of the obtained products in rubber compositions as a water-swelling filler. Lignocellulose powder from oat straw (composition: α-cellulose—77.0%, lignin—3.8%, resins and fats—1.8%) was used for carboxylation without preliminary separation into components. Microwave radiation was used to activate the carboxylation process. This reduced the reaction time by 2–3 times. The synthesized products were analyzed by IR spectroscopy, thermogravimetry and scanning electron microscopy. Industrial product sodium carboxymethylcellulose (Na-CMC) was used as a swelling filler for comparison. The swelling fillers were fractionated by the sieve method; particles with the size of 0–1 mm were used for filling rubber compounds. The amount of swelling filler was 150 parts per 100 parts of rubber (phr). Due to the high filling of rubber compounds, plasticizer Oxal T-92 was added to the composition of a number of samples to facilitate the processing and uniform distribution of ingredients. The rubber composition was prepared in two stages. In the first stage, ingredients without swelling filler were mixed with rubber on a laboratory two-roll mill to create a base rubber compound (BRC). In the second stage, the BRC was mixed with the swelling filler in a closed laboratory plasti-corder rubber mixer, the Brabender Plasti-Corder^® Lab-Station. Vulcanization was carried out at 160 °C. For the obtained samples, the physical-mechanical and sorption properties were determined. It has been shown that the carboxylated powdered lignocellulose from oat straw increases the strength properties of rubber in comparison with Na-CMC. It has been shown that when the carboxylated powdered lignocellulose from oat straw is introduced into the rubber composition, the degree of rubber swelling in aqueous solutions of various mineralizations increases by 50 and 100% in comparison with a noncarboxylated lignocellulose.

This study presents data on the use of shungite ore (the Bakyrchik deposit, Kazakhstan) and its concentrate as fillers in elastomer composites based on nitrile butadiene rubber. In addition to carbon, these shungite materials contain oxides of Si, Fe, K, Ca, Ti, Mn, and Al. The shungite concentrate was obtained through a flotation process involving five stages. The chemical composition analysis of these natural fillers revealed that during flotation, the carbon content increased 3.5 times (from 11.0 wt% to 39.0 wt%), while the silicon oxide content decreased threefold (from 49.4 wt% to 13.6 wt%). The contents of oxides of K, Ca, Ti, Mn, and Al decreased by less than 1%, and iron oxide content increased by 40% (from 6.7 wt% to 9.4 wt%). The study explored the impact of partial or full replacement of carbon black (CB) of P 324 grade with the shungite ore (ShO) and the shungite concentrate (ShC) on the vulcanization process and the physical–mechanical properties of the rubber. It was found that replacing CB with ShO and ShC reduces Mooney viscosity ML (1 + 4) 100 °C of the rubber compounds by up to 29% compared to the standard CB-filled sample. The use of the shungite fillers also increased scorch time (t_s) by up to 36% and cure time (t₉₀) by up to 35%. The carbon content in the shungite fillers had little influence on these parameters. Furthermore, it was demonstrated that replacing 5–10 wt% of CB with ShO or ShC improves the tensile strength of the rubber. The results of the flotation enrichment process enable the assessment of how these shungite fillers affect the properties of the composites for producing rubbers with specific characteristics. It was also found that substituting CB with ShO or ShC does not significantly affect the rubber’s resistance to standard oil-based media. The findings indicate that Kazakhstan’s shungite materials can be used as fillers in rubber to partially replace CB.

In the course of this study, the possibility of using powdered cotton cellulose as a water-swelling filler (WSF), which made it possible to improve the strength characteristics of rubbers in comparison with Na-carboxymethyl cellulose (Na-CMC), was studied. Compound scorch time and optimum time of vulcanization of the samples with WSF remained at the level of the sample without WSF. Minimum and maximum torques of the samples with WSF increased. That indicates an increase in the viscosity of the compounds. The introduction of powdered cotton cellulose led to an increase in Shore A hardness of the rubbers up to 40% and a slight decrease in reflection elasticity of the rubbers compared to the control. It was found that tensile strength of the samples filled with powdered cotton cellulose was 3 times higher compared to the rubbers filled with Na-CMC. Reducing viscosity of the rubbers with WSF was achieved using plasticizers PN-6 (a mixture of aromatic hydrocarbons) and T-92 (a mixture of dioxane ethers and alcohols) in an amount of 30 parts per 100 parts of rubber by weight. The introduction of the plasticizers made it possible to reduce Shore A hardness in comparison with the samples without the plasticizers by 7-12%. The introduction of PN-6 and T-92 plasticizers into rubber compounds, both containing mixed swelling polymers from Na-CMC and powdered cellulose, or individually, reduced tensile strength of the rubbers in comparison with the samples without the plasticizers. At the same time, with the introduction of T-92, tensile strength of the samples decreased to a lesser extent than with the introduction of PN-6 plasticizer. It was found that when replacing the water-swellable Na-CMC filler with powdered cotton cellulose, the degree of rubbers swelling decreases both in alkaline and acidic environments.

The present work investigates the effect of powdered lignocellulose from alfalfa straw obtained by a chemo-extrusion method, as well as its carboxymethylated derivative, on the physicomechanical properties and swelling behavior of vulcanizates based on nitrile butadiene rubber (NBR, BNKS-28 AMN grade). Carboxymethylation of lignocellulose was performed using microwave activation. The functional group composition of the modified lignocellulose was characterized by Fourier-transform infrared (FTIR) spectroscopy, which confirmed successful carboxymethylation and revealed a reduction in crystallinity. Thermogravimetric analysis (TGA) was used to determine the thermal stability of the swelling carboxymethylated fillers. The degree of crystallinity of the carboxymethylated swelling fillers was evaluated by X-ray diffraction (XRD). It was shown that the introduction of powdered lignocellulose and its carboxymethylated derivative into the rubber compounds lead to an increase in compound viscosity and prolong the optimum cure time, while having no effect on the scorch time, in a manner similar to that observed for the commercial product sodium carboxymethylcellulose (NaCMC). It has been shown that the introduction of powdered lignocellulose and its carboxymethylated derivative increases the tensile strength of the rubber and improves its resistance to the action of mineralized water compared with the samples containing NaCMC. It was also demonstrated that carboxymethylated lignocellulose exhibits enhanced sorption capacity comparable to that of NaCMC. Overall, carboxymethylation of lignocellulose derived from alfalfa straw significantly improves the stability and sorption characteristics of nitrile butadiene rubber composites. These findings indicate that carboxymethylated lignocellulose is a sustainable and effective alternative to industrial NaCMC for use as a functional filler in elastomeric materials.

It has been established that the introduction of powdered cellulose, obtained by chemo-mechanical destruction from oat straw, into the composition of rubbers as a hydrosorption filler increases the conditional tensile strength of vulcanizates in comparison with samples without this filler. It was revealed that the degree of swelling of rubbers containing powdered cellulose from oat straw, the pH of the aqueous medium and the degree of mineralization have little effect.