A Co-doped porous carbon was successfully fabricated by a facile carbonizing procedure using coal hydrogasification semi-coke (SC) as the carbon and cobalt nitrate as the magnetic precursors, respectively. The mass ratio of the precursors was changed to regulate the microwave absorption (MA) capabilities. The favorable MA capabilities are a result of a synergistic interaction be-tween the dielectric loss from the carbon framework, the magnetic loss from nano-sized Co particles, and multiple scattering from the residual pores. At a thickness of 4.0 mm, the Co/C composite showed the lowest reflection loss of −33.45 dB when the initial mass ratio of cobalt nitrate and SC was 1:1. The effective absorbing bandwidth (EAB) could achieve 3.5 GHz at 2 mm thickness. This work not only opens up a new avenue for the facile fabrication of dielectric and magnetic loss combinations and their structural design, but it also creates a new route for the high value-added exploitation of SC.

We studied the boron-based composite cluster B₈Al₃⁺ doped with Al atoms. The global minimum structure of the B₈Al₃⁺ cluster is a three-layer structure, consisting of three parts: an Al₂ unit, a B₈ ring and an isolated Al atom. Charge calculations analysis shows that the cluster can be expressed as [Al]⁺[B₈]²⁻[Al₂]²⁺, has 6π/6σ double aromaticity and follows the (4n+2) Hückel rule. Born–Oppenheimer molecular dynamics (BOMD) simulation shows that the B₈Al₃⁺ cluster has dynamic fluxionality properties. Remarkably, at the single-point coupled cluster singles, doubles and triples (CCSD(T)) level, the energy barrier for intramolecular rotation is merely 0.19 kcal mol⁻¹. [B₈]²⁻ molecular wheels have magical 6π/6σ double aromaticity properties, providing a continuous cloud of delocalized electrons, which is a key factor in the dynamic fluxionality of the cluster. The B₈Al₃⁺ cluster provides a new example of dynamic structural fluxionality in molecular systems.

A Co–doped porous carbon was successfully fabricated by a facile carbonizing procedure using coal hydrogasification semi-coke (SC) as the carbon and cobalt nitrate as the magnetic precursors, respectively. The microwave absorption (MA) performances were regulated by adjusting the mass ratio of the precursors. The dielectric loss from the carbon framework, the magnetic loss from nano–sized Co particles coupled with multiple scattering from the residual pores synergistically contribute to the favorable MA capabilities. When the initial mass ratio of cobalt nitrate and SC was 1:1, the Co/C composite showed the lowest reflection loss of -33.45 dB at the thickness of 4.0 mm. The effective absorbing bandwidth (EAB) could achieve 3.5 GHz at 2 mm in thickness. This work not only exploits a new avenue for the structural design and facile fabrication of dielectric and magnetic loss combinations, but also opens up another way for the high value–added utilization of SC.

As a member of smart materials, electrorheological elastomers (EREs) formed by pre-treating active electrorheological particles are attracting more and more attention. In this work, four Mg-doped strontium titanate particles with spherical, dendritic, flake-like and pinecone-like morphorlogies were obtained by hydrothermal and low-temperature co-precipitation. XRD, SEM, Raman and FT-IR were used to characterize the obtained products. The results showed that the sizes of Mg-doped strontium titanates are about 1.5‒2.0 μm, and the phase structure are dominated by cubic crystal. These Mg-doped strontium titanates were dispersed in a hydrogel composite elastic medium. Then, Mg-doped strontium titanate/glycerol/gelatin electrorheological composite hydrophilic elastomers were obtained with or without electric field. The electric field response properties of Mg-doped strontium titanate composite elastomers were investigated. It concluded that dendritic Mg-doped strontium titanate composite elastomers is high-performance EREs. And the maximum value of energy storage modulus of Mg-doped strontium titanate composite elastomers has achieved 8.70 MPa. This high electrorheological performance of the products is helpful for their applications in vibration control, force transducers, smart structures, dampers, and other fields.

As smart materials, electrorheological elastomers (EREs) formed by pre-treating active electrorheological particles are attracting more and more attention. In this work, four Mg-doped strontium titanate (Mg-STO) particles with spherical, dendritic, flake-like, and pinecone-like morphologies were obtained via hydrothermal and low-temperature co-precipitation. XRD, SEM, Raman, and FT-IR were used to characterize these products. The results showed that Mg-STOs are about 1.5–2.0 μm in size, and their phase structures are dominated by cubic crystals. These Mg-STOs were dispersed in a hydrogel composite elastic medium. Then, Mg-STO/glycerol/gelatin electrorheological composite hydrophilic elastomers were obtained with or without an electric field. The electric field response properties of Mg-doped strontium titanate composite elastomers were investigated. We concluded that dendritic Mg-STO composite elastomers are high-performance EREs, and the maximum value of their energy storage was 8.70 MPa. The significant electrorheological performance of these products is helpful for their applications in vibration control, force transducers, smart structures, dampers, and other fields.

We studied the boron-based composite cluster B8Al3+ doped with Al atoms. The global minimum structure of the B8Al3+ cluster is a three-layer structure, consisting of three parts: Al2 unit, B8 ring and isolated Al atom. Charge calculations analysis shows that the cluster can be expressed as [Al]+[B8]2−[Al2]2+, has 6/6 double aromaticity, and follows the (4n+2) Hückel rule. Born–Oppenheimer molecular dynamics (BOMD) simulation shows that, B8Al3+ cluster has dynamic fluxionality properties. Remarkably, at the single-point CCSD(T) level, the energy barrier for intramolecular rotation is merely 0.19 kcal mol−1. [B8]2− molecular wheels has magical 6/6 double aromaticity properties, providing a continuous cloud of delocalized electrons, which is a key factor in the dynamic fluxionality of the cluster. The B8Al3+ cluster provides a new example of dynamic structural fluxionality in molecular systems.