There are many studies related to using alkali activated binders for the improvement of clayey soil mechanical properties. In this study, alkali activated slag (AAS) for the improvement of clayey soil strength was used and it reinforced the clay. This paper presents results of an investigation on the utilization of ground-granulated blast-furnace slag in the reinforcement of clay soils. Therefore, significant cost savings could be achieved by using alkali activated slag as binding material. These samples were analyzed by X-Ray fluorescence analysis (XRF), X-Ray diffraction (XRD), scanning electron microscopy (SEM) and strength tests after the curing. The clay samples reinforced with AAS showed higher shear stress, cohesion and internal friction angle compared with the samples without reinforcement. The highest shear strength was achieved by using the highest amount of AAS (30%). This shear stress of the unreinforced clay samples could be increased from 63.2 to 137.4 kPa (117.4%) and from 123.2 to 257.4 kPa (108.9%) when the normal stress value of 100 and 500 kPa was used, respectively. The increase in shear strength is closely related to the compact contact zone between AAS and clay. Moreover, the new formed cementitious compounds of AAS had a positive influence on the shear strength of samples as well.

A study of immobilization of hexavalent chromium in the form of Na₂CrO₄ salt by self-compacting soils (SCS) is presented. Carbofill E additive was used as SCS binder. The efficiency of immobilization of Cr (VI) was evaluated by washing out chromium compounds from SCS samples. The influence of the nature of the soil and the content of Carbofill E and Na₂CrO₄ in the SCS samples on the efficiency of Cr (VI) immobilization was studied. It was found that the nature of the soil and the content of Carbofill E in the SCS samples affect the immobilization of Cr (VI). Moreover, increasing the Carbofill E content in SCS samples further increases Cr (VI) immobilization. X-ray diffraction studies of the samples with immobilized hexavalent chromium showed that part of the sample transforms from a readily soluble form of salt into oxide forms of chromium and calcium-chromium, which are practically insoluble in water.

This paper presents new ideas about the possibilities to increase the reliability of clay slope stability computation method. Many known methods are proved to give controversial results. The reason for this discrepancy is explained to be the result of assumptions and simplifications introduced into the methods, insufficiently precise estimation of porous water pressure, and the dependency of clay cohesion on a sudden change of compression as well. The method of a modified Boussinesq equation and slices is suggested to compute slope stability in terms of clay cohesion and internal friction determined under unconsolidated‐undrained conditions.

A whole series of factors influence the temperature of the soil surface and surface layers. The soil surface is heated by solar radiation during the day. It radiates some of the obtained heat at night. The heat exchange between the soil and the atmosphere depends on the air and soil temperatures and the speed of air movement. Precipitation may also affect surface soil layers, but this was not considered in this study. In the mentioned interaction, a specific temperature field of the surface layers of the soil is established. To increase the building’s energy efficiency, the aim is to optimize the operation of its heating and cooling systems and to reduce heat loss to the environment as much as possible. Heat loss through the floor of the building or the walls of the recessed part into the ground changes the established temperature field of the ground. The heat spreads in the soil and is given to the atmospheric air. During the research, to validate the numerical model, the heat flow density was analysed to determine how it changes while maintaining a constant temperature of the heating surface at a certain depth of the soil. It was found that the new thermodynamic equilibrium, depending on the seasonality, can be reached in a time interval of up to a week. The temperature change in the artificially limited volume of the ground under the building or next to it can be treated as the work of the ground thermo-accumulator: its charge or discharge by heat. This makes it possible to reduce the annual energy costs of the building by more than ten percent.

The purpose of this study was to evaluate how an alkali activator, specifically soluble glass, influences the geotechnical performance of sandy-pebble soil when combined with biomass bottom ash (BMA) as a sustainable stabilizing material. This work focused on understanding whether alkali activation could increase the strength, compactness, and overall engineering suitability of these mixtures while also examining how the activator affects permeability. To accomplish this, mixtures containing different proportions of BMA were prepared and treated with soluble glass at controlled water-to-activator ratios, followed by standard geotechnical procedures including Proctor compaction and California Bearing Ratio testing to assess density and load-bearing capacity. The results showed that soluble glass substantially improved the mechanical behavior of the mixtures, with both Proctor density values varying from 1.48 to 2.04 Mg/m³, depending on BMA content and activator dosage, while CBR values more than doubled for mixtures containing 20% BMA at a water-to-soluble-glass ratio of 1:3. Water permeability decreased with increasing BMA and activator content, from 8.11 × 10⁻⁵ to 5.91 × 10⁻⁵ m/s, although the permeability threshold of ≤2 × 10⁻⁵ m/s was not reached. These enhancements were linked to better packing of soil particles due to the void-filling effect of BMA and the formation of new binding compounds produced through alkali-activation reactions, including N-A-S-H and C-S-H gels. However, this study also found that higher amounts of soluble glass reduced water permeability, an effect associated with the denser microstructure created during geopolymerization. Overall, the findings demonstrate that stabilizing sandy-pebble soil with alkali-activated BMA is an effective approach to improving essential geotechnical properties while simultaneously offering environmental benefits by repurposing biomass waste in ground-improvement applications.