In this paper, the resistance to the freeze/thaw cycles for four groups of mortars (lime—LM, lime based—LBM, cement—CM, and aerated cement—ACM mortars) with different amount of mortar components within each group is quantified via a ratio of flexural/compressive strength after and before exposure to freeze/thaw cycles. Using a pore system obtained by three different methods (mercury intrusion porosimetry, X-ray micro-computed tomography analysis, and SEM (Scanning Electron Microscopy) analysis), an attempt was made to explain why some mortars achieved better resistance to freeze/thaw cycles than others. The mortars with lime as a binder in the composition (LM and LBM groups) did not survive the freezing and thawing regime, while no visible damage was recorded in samples of the CM and ACM group. It is concluded that the low initial value of the mechanical properties of the LM and LBM mortars, as well as the higher proportion of harmful pores (pores greater than 0.064 μm) compared to CM and ACM mortars are responsible for their poor durability. According the results of nanotomography, it is concluded that the most important factor influencing freeze/thaw resistance is pore connectivity—the higher the connectivity of the macropores, the higher the freeze/thaw resistance of the mortar. SEM analysis proved to be a very useful method for aerated cement mortars as it revealed the pore sizes that were not covered by mercury porosimetry and nanotomography.

This paper estimates the frost resistance of bricks using the ratio of compressive strength before freezing to compressive strength after freezing to describe the damage degree of bricks being exposed to freeze-thaw cycles. In an effort to find the ratio that clearly distinguishes resistant bricks from non-resistant bricks, the authors attempted to establish the correlation between the ratio and Maage factor as a recognized model for assessing brick resistance. To clarify the degree of damage of individual bricks, the pore size distribution has been investigated by means of mercury porosimetry. Additionally, micro computed X-ray tomography (micro-CT) has been employed to define the influence of the type of pores (open or closed) and their connectivity on the frost resistance of bricks. According to the results, it can be concluded that there is a good correlation between the Maage factor and the ratio of pre- to post-freeze-thaw cycle compressive strengths, and that the latter ratio strongly correlates with the percentage of large pores (≥3 mm) in the brick. If such a correlation could be confirmed in a larger sample, then the ratio of pre- to post-freeze-thaw cycle compressive strengths could be used as a new method for assessing brick resistance to freeze-thaw cycles and it would be possible to determine the minimum percentage of large pores required to ensure the overall resistance of brick to freeze-thaw conditions. The complexity of the problem is, however, evidenced by the fact that no clear connection between the type (open versus closed) or connectivity of pores and the frost resistance of bricks could be revealed by micro-CT.

This article describes the quantitative analysis of the 3D orientation of objects (i.e. particles and voids) within pottery fabrics to differentiate two categories of pottery hand-building primary forming techniques, specifically percussion-building and coil-building, comparing the use of two independent non-destructive imaging modalities, X-ray microtomography (µ-CT) and neutron tomography (NT). For this purpose, series of experimental organic-tempered vessels and coil sections were analysed. For both imaging modalities, two separate systems were employed for quantitatively describing both the orientation of individual objects, as well as the collective preferential alignment of objects within samples, utilising respectively polar and azimuth angles within a spherical coordinate system, and projected sizes within a positive Cartesian coordinate system. While the former provided full descriptions of the orientations of objects within 3D space, the latter, through a ratio dubbed here the ‘Orientation Index’ (OI), gave a simple numerical value with which the investigated samples were differentiated according to forming technique. Both imaging modalities were able to differentiate between coil-built and percussion-built vessels with a high degree of confidence, with the strength of these findings additionally demonstrated through extensive statistical modelling using Monte Carlo simulations. Despite differences in resolution and differences in the attenuation of X-rays and neutrons, µ-CT and NT were shown to provide comparable results. The findings presented here broadly agree with earlier studies; however, the quantitative and three-dimensional nature of the results enables more subtle features to be identified, while additionally, in principle, the non-destructive nature of both imaging techniques facilitates such structural analysis without recourse to invasive sampling.

Efficient Lewis-acid-catalyzed direct conversion of aldehydes to 1,2-diketones in the liquid phase was enabled by using newly designed and developed ceria–zirconia-based high-entropy oxides (HEOs) as the actual catalysts. The synergistic effect of various cations incorporated in the same oxide structure (framework) was partially responsible for the efficiency of multicationic materials compared to the corresponding single-cation oxide forms. Furthermore, a clear, linear relationship between the Lewis acidity and the catalytic activity of the HEOs was observed. Due to the developed strategy, exclusively diketone-selective, recyclable, versatile heterogeneous catalytic transformation of aldehydes can be realized under mild reaction conditions.