Building construction and building operations have a massive direct and indirect effect on the environment. Cement-based materials will remain essential to supply the growth of our built environment. Without preventive measures, this necessary demand in cement production will imply a substantial increase in CO₂ generation. Reductions in global CO₂ emissions due to cement consumption may be achieved by improvements on two main areas: increased use of low CO₂ supplementary cementitious materials and a more efficient use of Portland cement clinker in mortars and concretes. The use of ground granulated blast furnace slag in concrete, as cement constituent or as latent hydraulic binder, is a current practice, but information of concrete with ladle furnace slag is more limited. Specific knowledge of the behavior of mixtures with steel slag in relation to certain properties needs to be improved. This paper presents the results of the shrinkage (total and autogenous) of five concrete mixtures, produced with different percentages of two different slags in substitution of cement. The results show that shrinkage of concrete with the two different slags diverges. These different characteristics of the two materials suggest that their use in combination can be useful in optimizing the performance of concrete.

This paper presents a study of the effect of a superabsorbent polymer (SAP) for autogenous shrinkage control on the uniaxial tensile behavior of steel fiber reinforced concrete (SFRC). The use of fibers and SAP potentially increases the durability of the concrete, preventing cracking by autogenous shrinkage and enhancing post-cracking behavior. Furthermore, SAP can provide further hydration for self-healing purposes and improve the ductility of the SFRC. In order to evaluate the effect of the addition of SAP in SFRC, dog-bone SFRC specimens with different dosages of superabsorbent polymers were cast and tested under uniaxial tension. The digital image correlation (DIC) technique was used to understand the effect of SAP on the steel fibers’ crack-bridging mechanisms. Surface strains and crack openings were inferred using the DIC technique. The effect of SAP and fibers on fresh and hardened concrete was individually investigated by flow tests and compressive strength tests. Autogenous shrinkage was measured in plain concrete to investigate the minimum SAP content required to mitigate autogenous shrinkage of 0.3%. The use of 0.3% SAP was also sufficient to reach multiple cracking behavior. This content of SAP completely suppressed the autogenous shrinkage with minimal side effects on compressive strength. An analytical formulation for the tensile behavior of SFRC was developed using the variable engagement model, presenting a mean correlation of R² of 0.97 with the experimental results.

Over the past few decades, a significant number of large concrete structures with deterioration problems related to the alkali–silica reaction (ASR) have been identified in Portugal and worldwide. Assessing the condition of ASR-affected concrete dams involves both diagnosis and prognosis. Diagnosis evaluates the structure’s current state, while prognosis predicts deterioration and safety implications. This is key to estimate the period during which the structure will effectively perform its function, and essential for the timely and cost-effective planning of the necessary mitigation, rehabilitation, and/or reconstruction works. This article aims to contribute to the ongoing discussion of this topic by the scientific and technical community and, therefore, presents the methodology adopted to assess the condition of a severely ASR-affected concrete dam in Portugal, the Alto Ceira dam, in which the concrete was produced with susceptible to ASR quartzitic aggregates and that was decommissioned and replaced by a new one in 2014. The article provides a brief review of the diagnosis and prognosis of the ASR in concrete dams, presents and analyses the results from laboratory testing (including chemical, microstructural, physical, mechanical, and expansion tests), in-situ testing, structural monitoring systems, visual inspections, and numerical modelling, aiming at assessing ASR impacts and evidencing the utility of the reported methodology on the appraisal of ASR-affected structures.